• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2005.11a
• /
• pp.81-85
• /
• 2005

Recently, fire resistance of high performance concrete for explosive spalling was issued as high performance concrete was vulnerable to the explosive spalling in initial fire. Therefore, in this study, an experiment about reduction effect to explosive spalling of high performance concrete is performed by adding several polymer fiber with various volume fraction, an then final fiber and volume fraction of that which reduce the explosive spalling of high performance concrete is presented. As the result of this study, the most fitted fiber volume fraction of reducing effect for explosive spalling at high performance concrete is under the 0.1%, as consider the flowability and efficiency.

• Fire Science and Engineering
• /
• v.25 no.1
• /
• pp.42-49
• /
• 2011

In the high temperature situation like in a fire, the high strength of concrete (HSC) has extreme danger named explosive spalling. It is assumed that the major cause of explosive spalling is water vapour pressure inside concrete. This paper examines the effect of the compressive strength and the moisture content on the initial occurrence of explosive spalling. For the effective experiment of the initial explosive spalling, the curve of ISO834 temperature profile is applied on the basis of 15 minute and 30 minute. As a result, the more increase the compressive strength and the moisture content, the more increase the occurrence and phenomenon of explosive spalling. This paper analyzes the territory of explosive spalling depending the compressive strength and the moisture content. The explosive spalling is not examined in the case of the compressive strength 50~100 MPa and the moisture content below 3% and the compressive strength over 100 MPa and the moisture content below 1%. Also, due to the HSC, which makes it more difficult to transport vapour and moisture, very high vapour-pressure may occur close to the surface, there is a greater risk that HSC spalls compared with normal strength concrete (NSC).

• Journal of the Korea Concrete Institute
• /
• v.24 no.2
• /
• pp.173-183
• /
• 2012

Recently, experimental studies to prevent explosive spalling based on spalling mechanism and addition of Polypropylene fiber in high strength concrete (HSC) are performed actively. However, with respect to ultra high strength concrete (UHSC), its compact internal structure is more difficult release vapor pressure at rapid rising temperature compared to HSC. Therefore, in this study, an experiment was conducted to evaluate spalling properties of UHSC using ${\Box}$ $100mm{\times}100{\times}H200mm$ rectangular specimen according to ISO-834 standard fire curve. With respect melting point of fiber, three fiber types of Polyethylene, Polypropylene, and Nylon fibers with melting temperature of $110^{\circ}C$, $165^{\circ}C$, and $225^{\circ}C$, respectively, were considered. Mixed fiber of 0.15% and 0.25% of concrete volume was used to consider spalling properties based on water vapor pressure release. Then, TGDTA test on fiber and FEM analysis were performed. The results showed that it is difficult to prevent initial spalling without loss of fiber mass even if fiber melting temperature is low. Also, in preventing thermal spalling, fiber that melts to rapidly create porosity within 10 minutes of fire is more effective than that of low melting temperature property of fiber.

• Steel and Composite Structures
• /
• v.36 no.6
• /
• pp.657-669
• /
• 2020

This study investigates the fire resistance characteristics of reactive powder concrete according to changes in the cement content per unit area, mixing ratio of metakaolin (MK), and content of polypropylene fiber. A fire test was conducted, and the resulting residual strength characteristics were investigated through flexural and compressive strength measurements, as well as condition rating classification based on visual evaluation. MK effectively reduced the initial high content of calcium hydroxide, thereby reducing the water vapor pressure generated during pyrolysis and slowing spalling. Furthermore, the pore structure and loose tissue were effective for relieving the water vapor pressure in the event of a fire.

• Journal of the Earthquake Engineering Society of Korea
• /
• v.27 no.2
• /
• pp.119-127
• /
• 2023

In this paper, seismic performance evaluation was carried out for eight circular reinforced concrete columns designed seismically by KRTA[1]and KCI[8]. Primary design parameters for such columns included many longitudinal reinforcements, yield strength of reinforcements, the vertical spacing of spirals, aspect ratio, and axial force ratio. The test results showed that all the columns exhibited stable hysteretic and inelastic responses. Based on the test results, drift ratios corresponding to each damage state, such as initial yielding, initial cover spalling, initial core concrete crushing, buckling, and fracture of longitudinal reinforcement and final spalled region, were evaluated. Then, those ratios were compared with widely accepted damage limit states. The comparison revealed that the existing damage states were considerably conservative. This implies that additional research is required for the damage limit states of such columns designed seismically by current Korean design codes.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.705-708
• /
• 2008

To obtain tunnel concrete safety in case of fire, this study analyzed fire proof characteristics by fire proof method change, and the results are as follows. As a fire proof characteristics by RABT temperature heating curve, plain concrete experienced severe spalling by initial extremely high temperature. In view of fire proof method, in the cases of organic fiber mixing method and board method, spalling was prevented, and in the case of spray method, severe spalling of over 100mm depth occurred along with exposure of structural concrete including spray coat by heat stress, etc while metal lath, the stiffener, falls off. As for fire proof characteristics by RWS temperature heating curve, in case of organic fiber inclusion, concrete surface experienced fusion of within 5mm, while in the case of spray method, spray coat was severely spalled to a depth of over 100mm causing structural body concrete to expose its reinforcement, and also in the case of board method, board was fused by high temperature, causing structural body concrete be directly exposed to high temperature, which triggered overall fall-off phenomenon, so in such extraordinary high temperature heating condition, establishment of special fire proof measures is needed.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.26 no.3C
• /
• pp.219-228
• /
• 2006

In this study, a series of fire tests was carried out to evaluate fire-induced damage to structural members in tunnels. From the tests, the loss amount of concrete materials under the RWS scenario was slightly bigger than under the RABT fire scenario. Especially under the RWS fire scenario where the maximum temperature is over $1,200^{\circ}C$, the loss of concrete materials was mainly induced by melting. Generally, the loss of materials in reinforced concrete was slightly smaller than that in unreinforced concrete. Depending upon an applied fire scenario, fire-induced damage to shotcrete was quite different. From the realtime investigation of a specimen surface by a digital camcorder, it was proved that the material loss under the RABT fire scenario was mainly induced by spalling. However, it was also revealed that although fire-induced damage in the initial heating stage under the RWS was so close to that under the RABT, the material loss under the RWS at the later stage after 50 minutes elapsed since fire initiation was induced not by spalling but by melting.

• Proceedings of the Korean Geotechical Society Conference
• /
• 2006.03a
• /
• pp.960-969
• /
• 2006

In this study, a series of fire tests was carried out to evaluate fire-induced damage to structural members in tunnels. From the tests, the loss amount of concrete materials by the RWS fire scenario was slightly bigger than by the RABT fire scenario. Especially under the RWS fire scenario where the maximum temperature is over 1,200, the loss of concrete materials was mainly induced by melting. Generally, the loss of materials in reinforced concrete was slightly smaller than that in unreinforced concrete. Depending upon an applied fire scenario, fire-induced damage to shotcrete was quite different. From the real-time investigation of a specimen surface by a digital camcorder, it was proved that the material loss under the RABT fire scenario was mainly induced by spalling. However, it was also revealed that although fire-induced damage in the initial heating stage under the RWS was so close to that under the RABT, the material loss under the RWS at the later stage after 50 minutes elapsed since fire initiation was induced not by spalling but by melting.

• Journal of the Korea Concrete Institute
• /
• v.17 no.4 s.88
• /
• pp.655-662
• /
• 2005

Evaporation of concrete influences the development of both initial transverse cracking and delamination in the concrete slab. It was suggested that spatting distress might develop in the slab where the initial transverse cracking occurred by theoretical equations and a field investigation. Thus, efforts to prevent the evaporation of concrete using proper curing methods are required to minimize the distresses of the slabs. Effective curing thickness (ECT) concept was used in this paper to evaluate various curing methods used to prevent the evaporation from concrete. Curing effectiveness quantified by the ECT of different types and amounts of curing compound under various curing conditions was investigated based on the results of laboratory tests. According to the test results, the wind speed is inferred to be a significant factor of the magnitude and continuance duration of the curing effectiveness.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.12 no.3
• /
• pp.223-237
• /
• 2010

The initial heating rate is well known as one of the most influencing factors on the occurrence of spalling and the loss of strength in concrete after fire initiation. In this study, a series of fire tests were carried out at different initial heating rates to find out its effects on the deterioration of tunnel structural members. Heat transfer analyses combined with an element elimination model were also carried out to verify its applicability in the same conditions as the fire tests. Moreover, the convection heat transfer coefficients compatible with fire test results were derived from parametric studies. In this course, their time-dependent variations were also analyzed at different initial heating rates. Finally, a numerical formula to estimate the heat transfer coefficients at the various initial heating rates was proposed by the interpolation of the results of numerical analyses.