• Carbon letters
• /
• v.17 no.1
• /
• pp.33-38
• /
• 2016

In the present study, exfoliated graphite nanoplatelets (xGnP) with different particle sizes were coated onto polyacrylonitrile-based carbon fibers by a direct coating method. The flexural properties, interlaminar shear strength, and the morphology of the xGnP-coated carbon fiber/phenolic matrix composites were investigated in terms of their longitudinal flexural strength and modulus, interlaminar shear strength, and by optical and scanning electron microscopic observations. The results were compared with a phenolic matrix composite counterpart prepared without xGnP. The flexural properties and interlaminar shear strength of the xGnP-coated carbon fiber/phenolic matrix composites were found to be higher than those of the uncoated composite. The flexural and interlaminar shear strengths were affected by the particle size of the xGnP, while the particle size had no significant effect on the flexural modulus. It seems that the interfacial contacts between the xGnP-coated carbon fibers and the phenolic matrix play a role in enhancing the flexural strength as well as the interlaminar shear strength of the composites.

• Composites Research
• /
• v.30 no.1
• /
• pp.71-76
• /
• 2017

The purpose of this study was to predict the long-term performance using the interlaminar shear strength of carbon fiber/epoxy composites exposed to environmental factors. Interlaminar shear specimens, manufactured by the filament winding method, were exposed to the conditions of drying at $50^{\circ}C$, $70^{\circ}C$, and $100^{\circ}C$ and of immersion at $25^{\circ}C$, $50^{\circ}C$, and $70^{\circ}C$ for up to 3000 hours, respectively. According to the results, the interlaminar shear strength did not vary significantly with the exposure time for the drying at $50^{\circ}C$ and $70^{\circ}C$, but it increased somewhat for the drying at $100^{\circ}C$ due to the post curing as the exposure time increased. The interlaminar shear strength of the specimens exposed to the immersion at $25^{\circ}C$ did not change significantly at the beginning of exposure, but it decreased with the exposure time and the degree of decrease increased as the environmental temperature increased. The linear regression equations for the environmental temperatures were obtained from the interlaminar shear strength of the specimens exposed to the immersion for up to 3000 hours. Using these linear regression equations, the interlaminar shear strength was estimated to be within 5.5% of the measured value at $25^{\circ}C$ and $50^{\circ}C$, and 2.3% of the measured value at $70^{\circ}C$. Therefore, the proposed performance prediction procedures can predict well the long-term interlaminar shear strength of carbon fiber/epoxy composites exposed to environmental factors.

• Composites Research
• /
• v.21 no.2
• /
• pp.1-7
• /
• 2008

Composite materials are currently used in aero-space industry, sport and leisure industry but it has many problems such as mechanical properties deterioration by moisture absorption. In this study, we appraised interlaminar shear strength with specimen that immersed/ immersed-dried in water environment(distilled/sea) during $100{\sim}200$days. In the result, properties degradation of resin part and silan part by moisture absorption is judged early on main cause of interlaminar shear strength, and later destruction of mechanical bonding between silan part and fiber by moisture absorption is Judged later main cause of interlaminar shear strength. In conclusion, the recovery of interlaminar shear strength is judged to difficult due to interfacial destruction by moisture when pass over irreversible by moisture in composite material.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.4
• /
• pp.31-39
• /
• 1997

This research is to evaluate the effect of sunshine treatment on the strength in the Al 6061/AFRP hybrid composite(APAL). APAL specimens were processed by autoclave curing system under the constant condition of curing temperature, time and aluminum surface pertreatment. Aramid patched aluminum alloy can be widely used for the repair of the damage part of the aircraft. The tensile strength of the sunshine treated APAL 2P and 6P composite is 14%, 22% smaller than that of the non-treated material. The interlaminar shear strength of the APAL specimens for the adhesive length of 5mm is 24% higher than that of the APAL for the adhesive length of 10mm. In the case of APAL DS 1P material, interlaminar shear strength of the specimen which was sunshine treated for 200 hours is 21% smaller than that of the non-treated material while interlaminar shear strength of the specimen which was immersed in a 70.deg. C fresh water for 1200 hours decreases by 75.7%.

• Composites Research
• /
• v.24 no.5
• /
• pp.34-38
• /
• 2011

Carbon nanotubes (CNTs) have been widely investigated as reinforcements of CNT/polymer nanocomposites to enhance mechanical and electrical properties of polymer matrices since their discovery in the early 90's. Furthermore, the number of studies about incorporating CNTs into carbon fiber reinforced plastics (CFRP) to reinforce their polymer matrices is increasing recently. In this study, single-walled carbon nanotubes (SWNT) were dispersed in epoxy with 0.2 wt.% and 0.5 wt.%. Then, the SWNT/epoxy mixtures were processed to carbon fiber composites by a vacuum assisted resin transfer molding (VARTM) and a wet lay up method. The processed composite samples were tested for the interlaminar shear strength (ILSS). The relationship between the interlaminar shear strengths and processing, and the reinforcement mechanism of carbon nanotubes were investigated. CNT/epoxy nanocomposite specimens showed the increased tensile properties. However, the ILSS of carbon fiber composites was not enhanced by reinforcing the matrix with CNTs because of processing issues caused by increased viscosity of the matrix due to addition of CNTs particularly for a VARTM method.

• Carbon letters
• /
• v.1 no.2
• /
• pp.60-63
• /
• 2000

In this work, the carbon fibers-reinforced carbon matrix composites made with different carbon char yields of phenolic resin matrix have been characterized by mechanical flexural tests for acoustic emission properties. The composites had been fabricated in the form of two-dimensional polyacrylonitrile based carbon fibers during the carbonization process. It was found that the composites made with the carbon char yield-rich of resin matrix result in better mechanical interfacial properties, i.e., the interlaminar shear strength (ILSS) of the composites. The data obtained from the acoustic emission monitored appeared to show that the composites made with carbon char yield-rich were also more ductile. From the acoustic emission results, the primary composite failure was largely depended on the debonding at interfaces between fibers and matrix. The interlaminar shear strengths of the composites were correlated with the acoustic emission results.

• Composites Research
• /
• v.28 no.3
• /
• pp.94-98
• /
• 2015

This paper reports the effects of nickel film interleaves on the interlaminar shear strength(ILSS) of carbon fiber reinforced epoxy composites(CFRPs). A nickel thin film was deposited onto the prepreg by radio frequency(RF) sputtering at room temperature. The ILSS of the nickel film interleaved hybrid composites was increased compared to that of the composites without interleaves. To understand the mechanism of enhancement of the ILSS, the fracture surface of the tested specimens was examined by scanning electron microscopy(SEM). The metal interleaves were acted as a reinforcement for the matrix rich interface and the shear property of their composites improved by enhancing the resistance to matrix cracking.

• Composites Research
• /
• v.28 no.3
• /
• pp.136-141
• /
• 2015

The stitching process has been widely utilized for the improvement of through-thickness property of the conventional laminated composites. This paper reports the effects of stitching on the flexural and interlaminar shear properties of multi-axial warp knitted (MWK) composites in order to identify the mechanical property improvements. In order to minimize the geometric uncertainties associated with the stacking pattern of fabrics, the regular lay-up was considered in the examination of the stitching effect. The key parameters are as follows: the stitch spacings, the stitching types, the stitching location, and the location of compression fixture nose. These parameters have little effect on the flexural and interlaminar shear properties, except for the case of stitching location. However, the geometry variations caused by the stitching resulted in minor changes to the mechanical properties consistently. Stitching on the $0^{\circ}$ fibers showed the lowest flexural strength and modulus (12% reduction for both properties). The stitch spacing of 5 mm resulted in 8% reduction for the case of interlaminar strength compared with that of 10 mm spacing.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.10a
• /
• pp.216-219
• /
• 2004

The stitching process has been widely utilized for the improvement of through-thickness property of the conventional laminated composites. This paper rep0l1s the effects of stitching on the flexural and interlaminar shear properties of multiaxial warp knitted composites in order to examine the performance improvements. Considered parameters are as follows: the stacking regularity of the multiaxial warp knits, the stitch spacings, the stitching types, the stitching location, and the location of compression fixture nose. These parameters have little effect on the flexural and interlaminar shear properties, except for the case of stitching location. Stitching on the $0^{\circ}$ fibers showed the lowest flexural strength and modulus ($12\%$reduction for both properties). The stitch spacing of 5mm resulted 8% reduction in interlaminar strength compared with 10mm spacing.

• Journal of Adhesion and Interface
• /
• v.5 no.1
• /
• pp.21-28
• /
• 2004

In this work, glass fiber/nylon 6 and woven glass fiber/nylon 6 composites have been fabricated using glass fiber reinforcements sized with 3-chloropropyltrimethoxysilane(CTMS) having a chloropropyl organo-functional group in the molecular chain end. The interfacial shear strength of glass fiber/nylon 6 composite was measured using a single fiber microbonding test and the interlaminar shear strength and the storage modulus of woven glass fabric/nylon 6 composites were measured using a short-warn shear test and a dynamic mechanical analysis, respectively, informing the effect of the concentration of CTMS on the properties. With increasing CTMS concentration, the interfacial properties of the composites were improved. The results on the interfacial shear strength, interlaminar shear strength, interlaminar failure pattern, and storage modulus with varying the CTMS concentration agree with each other.