• Current Photovoltaic Research
• /
• v.5 no.3
• /
• pp.83-88
• /
• 2017

The growth of intermetallic compounds is an important factor in the reliability of solar cells. Especially, the temperature change in the soldering process greatly affects the thickness of the intermetallic compound layer. In this study, we investigated the intermetallic compound growth by Sn-diffusion in solder joints of solar cells. The thickness of the intermetallic compound layer was analyzed by IR lamp power and hot plate temperature control, and the correlation between the intermetallic compound layer and the adhesive strength was confirmed by a $90^{\circ}$ peel test. In order to investigate the growth of the intermetallic compound layer during isothermal aging, the growth of the intermetallic compound layer was analyzed at $85^{\circ}C$ and 85% for 500 h. In addition, the activation energy of Sn was calculated. The diffusion coefficient of the intermetallic compound layer was simulated and compared with experimental results to predict the long-term reliability.

• Journal of Welding and Joining
• /
• v.20 no.1
• /
• pp.97-102
• /
• 2002

The growth kinetics of intermetallic compound layers formed between the eutectic Sn-3.5Ag solder and the Cu and Ni/Cu pad by solid stateisothermal aging were examined. The interfacial reaction between the eutectic Sn-3.5Ag solder and the Cu and Ni/Cu pad was investigated at 70, 120, 150, $170^{\circ}C$ for various times. The intermetallic compound layer was composed of two phase: $Cu_6Sn_5$(${\varepsilon}-phase$) adjacent to the solder and $Cu_6Sn_5$(${\varepsilon}-phase$) adjacent to the copper and on solder/Ni pad the intermetallic compound layer was $Ni_3Sn_4$. Because the values of time exponent(n) have approximately 0.5, the layer growth of the intermetallic compound was mainly controlled by volume diffusion over the temperature range studied. The apparent activation energy for layer growth of total Cu-Sn($Cu_6Sn_5 + Cu_6Sn$), $Cu_6Sn_5$, $Cu_3Sn$ and $Ni_3Sn_4$ intermetallic compound were 64.82kJ/mol, 48.53kJ/mol, 89.06kJ/mol and 71.08kJ/mol, respectively.

• Journal of Korea Foundry Society
• /
• v.31 no.2
• /
• pp.66-70
• /
• 2011

Hot dip aluminizing (HDA) is widely used in industry for improving corrosion resistance of material. The formation of intermetallic compound layers during the contact between dissimilar materials at high temperature is common phenomenon. Generally, intermetallic compound layers of $Fe_2Al_5$ and $FeAl_3$ are formed at the Al alloy and Fe substrate interface. In case of cast iron, high contact angle of graphite existed in the matrix inhibits the formation of intermetallic compound layer, which carry with it the disadvantage of a reduced reaction area and mechanical properties. In present work, the process for the removal of graphite existed on the surface of specimen has been investigated. And also HDA was proceeded at $800^{\circ}C$ for 3 minutes in aluminum alloy melt. The efficiency of graphite removal was increased with the reduction of particle size in sanding process. Graphite appears to be present both in the region of melting followed by re-solidification and in the intermetallic compound layer, which could be attributed to the fact that the surface of cast iron is melted down by the formation of low melting point phase with the diffusion of Al and Si to the cast iron. Intermetallic compound layer consisted of $Fe(Al,Si)_3$ and $Fe_2Al_5Si$, the layer formed at cast iron side contained lower amount of Si.

• Journal of the Korean institute of surface engineering
• /
• v.12 no.2
• /
• pp.75-83
• /
• 1979

The Rates of formation and heats of activation for the intermatallic Compound Layers between Cold rolled sheet and molten aluminium &ath (adding small amounts of silicon) has been determined by Continous aluminizing method in the temperature range of 680$^{\circ}$ to 760$^{\circ}C$ and with immerssion time. The structure of the intermetallic Compound Layers was the shape of "Tongues" in pure Al-Bath and Al-Bath Containing 1% Si, But in Al-5% Si Bath was "Band" the Composition of the intermetallic Compound Layers were checked by microhardness measurements and X-Ray probe micro analyzer. FeAl intermetallic Compound layer was found to be uniform in pure Al-Bath and Al-5% Si Bath, But Fe Al intermetallic Compound Layer was shown in Al-1% Si Bath. The growth Rates of the intermetallic Compound Layers was most rapidly increased at Temperatures from 720$^{\circ}$ to 760$^{\circ}C$, at the immorsion time above 60 Second in pure Al-Bath, But in Al-1% Si Bath was solwly increased for the same conditions, and then in Al-5% Si Bath was hardly effected by these experimental condition. Heasts of activation of 29, 46 Kcal per mole which calculuted from Layer growth experiments were found in pure Al-Bath, Al-1% Si Bath respectively.

• Journal of the Korean institute of surface engineering
• /
• v.20 no.4
• /
• pp.144-153
• /
• 1987

In the case of dipping the Ni-Resist cast iron into molten aluminum with iron content, the thickness of intermetallic compound was remarkably increased with increasing iron content. The thickness was shown by following equation in the range of 1-3% iron content; $x=22.5t^{1/2}+4.47{\cdot}t{\cdot}(Fe%)$. where, x is thickness(${\mu}m$), t the time (minute), Fe% the iron w/o. When the Ni-Resist cast iron was dipped into the molten aluminum containing zinc content, the intermetallic compound thickness was also increased with increasing zinc contents. And thickness was represented by the following equation in the range of 2-10% zinc content; $x=3.46t^{1/2}+0.27{\cdot}t{\cdot}(Zn%)$. However, in the case of dipping the Ni-resist cast iron into molten aluminum with silicon content, the thickness of intermetallic compound was decreased with increasing silicon content, as shown in the following equation; $x=7.17t^{1/2}-0.15{\cdot}t{\cdot}(Si%)$. The intermetallic compound formed onto Ni-Resist cast iron was identified to be $FeAl_3\;and\;Fe_3Al$. As the result of hardness measurement, the peak hardness appeared in the intermetallic compound at near interface of the cast iron and the compound.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.487-492
• /
• 2002

The growth kinetics of intermetallic compound layers formed between eutectic Sn-58Bi solder and (Cu, electroless Ni-P/Cu) substrate were investigated at temperature between 70 and 120 C for 1 to 60 days. The layer growth of intermetallic compound in the couple of the Sn-58Bi/Cu and Sn-58Bi/electroless Ni-P system satisfied the parabolic law at given temperature range. As a whole, because the values of time exponent (n) have approximately 0.5, the layer growth of the intermetallic compound was mainly controlled by volume diffusion over the temperature range studied. The apparent activation energies of Cu$_{6}$Sn$_{5}$ and Ni$_3$Sn$_4$ intermetallic compound in the couple of the Sn-58Bi/Cu and Sn-58Bi/electroless Ni-P were 127.9 and 81.6 kJ/mol, respectively.ely.

• Journal of the Korean institute of surface engineering
• /
• v.37 no.2
• /
• pp.128-136
• /
• 2004

Effects of alloying elements on the surface characteristics of Fe-38Al intermetallic compounds were investigated using potentiostat. The specimens were casted by the vacuum arc melting. The subsequent homogenization and the stabilization led to the homogeneous DO$_3$ structure of the specimen. After the corrosion tests, the surface of the tested specimen was observed by the optical microscopy and scanning electron microscopy(SEM). For Fe-38 at.% Al intermetallic compound, the addition of Cr and Mo proved to be beneficial in decreasing the grain boundary attack by decreasing the active current density. Addition of Band Nb resulted in a higher active current density and also a higher passive current density. These results indicated the role of Cr and Mo in improving the pitting corrosion resistance of Fe-38 at.%Al intermetallic compound. Band Nb addition to Fe-38 at.%Al accelerated the granular corrosion. Fe-38 at.%Al containing Cr and Mo showed remarkably improved pitting corrosion resistance in comparison with Band Nb addition to Fe-38 at. %Al.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.1
• /
• pp.47-52
• /
• 2002

Intermetallic compound on the soldered interface plays important role on the bondability and mechanical properties of soldered joint. The formation of intermetallic compounds are influenced by many factors such as temperature, holding time, base metals and so on. On this study the effect of number of reflow times on the intermetallic growth was investigated. For the experimental materials, Sn-3.5Ag-0.7Cu solder ball of 0.3mm diameter and RMA-type flux were used. Thickness of intermetallic compound of solder ball by 2nd reflow showed nearly 60% higher than that of 1st reflow, and shear strength showed 10% higher value. Thickness and shear strength according to the position of interface such as upper side or lower side between two substrates were also investigated.

• Journal of the Korean institute of surface engineering
• /
• v.22 no.2
• /
• pp.47-54
• /
• 1989

The effects of intermetallic compound growt on the sheet resistance and soldreability as functions of the aging time, the temperature, and the conditions of substrates have been investi-gated in the electroplallic compound (mainy Cu6Sn5and Ni3Sn4) and the number of phase interface increased, the sheet resistance increased. Spread tests showed that the solderability was dereased with the intermetallic compounds growth and increased with the thickness of electroplated Sn. The surface morphology or agin size of the compound layer singificantly affect the solderability. The solderability of Sn/Ni system was superiot to Sn/Ni system was sperior to that of Sn/Cu system and the intermetallic compounds growth was solwer in the former system.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.463-468
• /
• 2002

This study investigates the variations of shear force, displacement, and fracture surface with the shear speed and the number of reflows. The experimental data of shear tests indicate that the shear force increases as increasing the number of reflows and the shear speed due to the formation of a kind of intermetallic compound, Ni$_3$Sn$_4$, on Au/Ni/Cu pad, and the work-hardening. However, general trends show that the shear force decreases due to increasing the thickness of the intermetallic compound over 4x reflow. It is observed that the intermetallic compound which is formed between solder and pad increases according to increasing the number of reflows, and the growth rate of the intermetallic compound at central region on the interface is faster than one at edge part. The general tendencies of shear force and displacement with different shear speeds are almost identical as an increase of the number of reflows.