• Korean Chemical Engineering Research
• /
• 제51권6호
• /
• pp.727-732
• /
• 2013

본 연구는 역오팔 지지체를 이용하여 인간지방유래 줄기세포의 연골 분화를 촉진하는 내용을 담고 있다. 비 다공성 구조를 가진 지지체에서 세포를 분화 시도하였을 경우 분화가 잘 촉진되지 않는 것에 비해 200 nm 정도의 균일한 구멍을 가지는 poly(D,L-lactide-co-glycolide)로 구성된 역오팔 지지체는 그 다공성 구조로 인하여 지지체의 내부까지 산소와 유기물의 수송을 가능하게 하여 지지체 내에서 어떤 유전적, 약물적 처리 없이 인간지방유래 줄기세포가 분화가 잘 되게 하는 것을 확인하였다.

• 전기화학회지
• /
• 제15권3호
• /
• pp.149-153
• /
• 2012

The $Cu_2O/TiO_2$ inverse opal heterojunction arrays were developed by electrochemical deposition of $Cu_2O$ nanoparticles on $TiO_2$ inverse opal arrays. The $Cu_2O$ nanoparticles completely filled the inner pores of $TiO_2$ inverse opal film (prepared by liquid phase deposition with an average thickness of 400 nm) and covered the entire area; exhibiting high crystalline properties of anatase and cubic phase from $TiO_2$ and $Cu_2O$, respectively. From asymmetric current-voltage profile, it was noticeable that a heterojunction was well formed for charge transport from $Cu_2O$ to $TiO_2$ film resulting from the enhanced charge separation yield. In addition, increased photocurrent of 0.19 $mA/cm^2$ (versus 0.08 $mA/cm^2$ under dark condition) was obtained at -0.35 V from the heterojunction structure in the 0.5M $Na_2SO_4$ solution.

• 멤브레인
• /
• 제26권6호
• /
• pp.421-431
• /
• 2016

최근 들어 정렬구조의 나노구조체를 이용한 분리막 응용기술이 큰 관심을 받고 있다. 나노구조체 분리막은 낮은 흐름저항을 통해 높은 투습성을 유지하면서도 매우 균일한 기공크기 특성으로 인해 높은 분리선택비를 가질 수 있다는 장점을 지닌다. 특히 콜로이드 입자의 자기조립체인 오팔상 및 그 역구조인 역오팔상 구조체를 이용한 분리막 기술이 각광을 받고 있는데, 기공크기를 자유롭게 제어하면서도 내부에 다양한 기능기의 도입이 가능하여 크기선별 분리 뿐 아니라 반응성 분리막의 응용에까지 폭넓게 적용이 가능하다. 더불어 다양한 멀티스케일 구조화 기술을 이용하여 기존의 분리막 소재에서는 다룰 수 없었던 다양한 형태의 기공 및 채널구조를 도입할 수 있어, 차세대 고부가가치 분리막 소재기술에 있어 큰 활용이 기대된다. 본 기고에서는 다양한 소재를 활용한 역오팔상 구조체 분리막 기술과 더불어 계층구조화를 통한 기능성 분리막의 개발에 대해 총괄적으로 살펴보고 논의하고자 한다.

• 한국분말재료학회지
• /
• 제23권3호
• /
• pp.189-194
• /
• 2016

We report a facile method for preparing KIT-1 mesoporous silicates with two different macroporous structures by dual templating. As a template for macropores, polystyrene (PS) beads are assembled into uniform three dimensional arrays by ice templating, i.e., by growing ice crystals during the freezing process of the particle suspension. Then, the polymeric templates are directly introduced into the precursor-gel solution with cationic surfactants for templating the mesopores, which is followed by hydrothermal crystallization and calcination. Later, by burning out the PS beads and the surfactants, KIT-1 mesoporous silicates with macropores are produced in a powder form. The macroporous structures of the silicates can be controlled by changing the amount of EDTANa4 salt under the same templating conditions using the PS beads and inverse-opal or hollow structures can be obtained. This strategy to prepare mesoporous powders with controllable macrostructures is potentially useful for various applications especially those dealing with bulky molecules such as, catalysis, separation, drug carriers and environmental adsorbents.

• 한국광학회:학술대회논문집
• /
• 한국광학회 2006년도 하계학술발표회 논문집
• /
• pp.53-54
• /
• 2006

• 한국재료학회지
• /
• 제29권8호
• /
• pp.491-496
• /
• 2019

In this study, we prepare pure $WO_3$ inverse opal(IO) film with a thickness of approximately $3{\mu}m$ by electrodeposition, and an ultra-thin $TiO_2$ layer having a thickness of 2 nm is deposited on $WO_3$ IO film by atomic layer deposition. Both sets of photoelectrochemical properties are evaluated after developing dye-sensitized solar cells(DSSCs). In addition, morphological, crystalline and optical properties of the developed films are evaluated through field-emission scanning electron microscopy(FE-SEM), High-resolution transmission electron microscopy(HR-TEM), X-ray diffraction(XRD) and UV/visible/infrared spectrophotometry. In particular, pure $WO_3$ IO based DSSCs show low $V_{OC}$, $J_{SC}$ and fill factor of 0.25 V, $0.89mA/cm^2$ and 18.9 %, achieving an efficiency of 0.04 %, whereas the $TiO_2/WO_3$ IO based DSSCs exhibit $V_{OC}$, $J_{SC}$ and fill factor of 0.57 V, $1.18mA/cm^2$ and 50.1 %, revealing an overall conversion efficiency of 0.34 %, probably attributable to the high dye adsorption and suppressed charge recombination reaction.

• 한국분말재료학회지
• /
• 제18권4호
• /
• pp.347-358
• /
• 2011

Two different schemes were adopted to fabricate ordered macroporous structures with face centered cubic lattice of air spheres. Monodisperse polymeric latex suspension, which was synthesized by emulsifier-free emulsion polymerization, was mixed with metal oxide ceramic nanoparticles, followed by evaporation-induced self-assembly of the mixed hetero-colloidal particles. After calcination, inverse opal was generated during burning out the organic nanospheres. Inverse opals made of silica or iron oxide were fabricated according to this procedure. Other approach, which utilizes ceramic precursors instead of nanoparticles was adopted successfully to prepare ordered macroporous structure of titania with skeleton structures as well as lithium niobate inverted structures. Similarly, two different schemes were utilized to obtain disordered macroporous structures with random arrays of macropores. Disordered macroporous structure made of indium tin oxide (ITO) was obtained by fabricating colloidal glass of polystyrene microspheres with low monodispersity and subsequent infiltration of the ITO nanoparticles followed by heat treatment at high temperature for burning out the organic microspheres. Similar random structure of titania was also fabricated by mixing polystyrene building block particles with titania nanoparticles having large particle size followed by the calcinations of the samples.

• Journal of Electrochemical Science and Technology
• /
• 제9권4호
• /
• pp.282-291
• /
• 2018

The pristine fluorine-doped $SnO_2$ (abbreviated as FTO) inverse opal (IO) was developed using a 410 nm polystyrene bead template. The nanolayered copper tungsten oxide ($CuWO_4$) was decorated on the FTO IO film using a facile electrochemical deposition, subsequently followed by annealing at $500^{\circ}C$ for 90 min. The morphologies, crystalline structure, optical properties and photoelectrochemical characteristics of the FTO and $CuWO_4$-decorated FTO (briefly denoted as $FTO/CuWO_4$) IO film were investigated by field emission scanning electron microscopy, X-ray diffraction, UV-vis spectroscopy and electrochemical impedance spectroscopy, showing FTO IO in the hexagonally closed-pack arrangement with a pore diameter and wall thickness of about 300 nm and 20 nm, respectively. Above this film, the $CuWO_4$ was electrodeposited by controlling the cycling number in cyclic voltammetry, suggesting that the $CuWO_4$ formed during 4 cycles (abbreviated as $CuWO_4$(4 cycles)) on FTO IO film exhibited partial distribution of $CuWO_4$ nanoparticles. Additional distribution of $CuWO_4$ nanoparticles was observed in the case of $FTO/CuWO_4$(8 cycles) IO film. The $CuWO_4$ layer exhibits triclinic structure with an indirect band gap of approximately 2.5 eV and shows the enhanced visible light absorption. The photoelectrochemical (PEC) behavior was evaluated in the 0.5 M $Na_2SO_4$ solution under solar illumination, suggesting that the $FTO/CuWO_4$(4 cycles) IO films exhibit a photocurrent density ($J_{sc}$) of $0.42mA/cm^2$ at 1.23 V vs. reversible hydrogen electrode (RHE, denoted as $V_{RHE}$), while the FTO IO and $FTO/CuWO_4$(8 cycles) IO films exhibited a $J_{sc}$ of 0.14 and $0.24mA/cm^2$ at $1.23V_{RHE}$, respectively. This difference can be explained by the increased visible light absorption by the $CuWO_4$ layer and the favorable charge separation/transfer event in the cascading band alignment between FTO and $CuWO_4$ layer, enhancing the overall PEC performance.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 추계학술발표대회
• /
• pp.13.1-13.1
• /
• 2011

Photoelectrochemical solar cells such as dye-sensitized cells (DSSCs), which exhibit high performance and are cost-effective, provide an alternative to conventional p-n junction photovoltaic devices. However, the efficiency of such cells plateaus at 11~12%, in contrast to their theoretical value of 33%. The majority of research has focused on improving energy conversion efficiency of DSSC by controlling nanostructure and exploiting new materials in photoelectrode consisting of semiconducting oxide nanoparticles and a transparent conducting oxide electrode (TCO) [1-5]. In this presentation, we introduce inverse opal-based scattering layers containing highly crystalline anatase nanoparticles and their feasibility for use as bi-functional light scattering layer is discussed in terms of optical reflectance and charge generation properties as a function of optical wavelength. A new ITO nanowire-based photoelecrode is also introduced and its unique charge collection property is presented, demonstrating potential use for highly efficient charge collection in DSSC.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 춘계학술발표대회
• /
• pp.7.2-7.2
• /
• 2011

Photoelectrochemical solar cells such as dye-sensitized cells (DSSCs), which exhibit high performance and are cost-effective, provide an alternative to conventional p-n junction photovoltaic devices. However, the efficiency of such cells plateaus at 11~12%, in contrast to their theoretical value of 33%. The majority of research has focused on improving energy conversion efficiency of DSSC by controlling nanostructure and exploiting new materials in photoelectrode consisting of semiconducting oxide nanoparticles and a transparent conducting oxide electrode (TCO). In this presentation, we introduce monodisperesed TiO2 nanoparticles prepared by forced hydrolysis method and their superiority as photoelectrode materials was characterized with aids of optical and electrochemical analysis. Inverse opal-based scattering layers containing highly crystalline anatase nanoparticles are also introduced and their feasibility for use as bi-functional light scattering layer is discussed in terms of optical reflectance and charge generation properties as a function of optical wavelength.