• Polymer(Korea)
• /
• v.25 no.4
• /
• pp.460-467
• /
• 2001

Inverse suspension polymerization of acrylamide (AM) in cyclohexane was carried out to study the effects of concentrations of sorbitan ester (Span) stabilizers and 2,2'-azobis (2-methyl propionamidine) dihydrochloride (AIBA) initiator, amount of monomer, shaking speed, and polymerization temperature on the particle size of the resulting poly (acrylamide) (PAM) beads and their molecular weights. It was found that the particle diameter. in general, decreased with increasing concentration of stabilizer, shaking speed, and water content in the aqueous phase, and with decreasing concentration of initiator and polymerization temperature. The average molecular weight of the resulting PAM beads was also found to increase with increasing concentrations of monomer and stabilizer, and also with decreasing concentration of initiator, polymerization temperature, and water content in the aqueous phase. In this study, PAM beads ranging 2 ~ 50 ${\mu}$m in diameter, with 8000000 ~ 12000000 in the weight average molecular weight were successfully prepared in almost 100% conversion.

• Polymer(Korea)
• /
• v.30 no.4
• /
• pp.286-292
• /
• 2006

Super water-absorbent resins were prepared by inverse suspension copolymerization of sodium acrylate, acrylamide and 2-hydroxyethyl acrylate using N, N'-methylene-bis-acrylamide as cross-linker. For the suspension copolymerization, monohexadecyl phosphate was employed as the dispersing agent, cyclohexane as the dispersing medium and potassium persulfate as the initiator. The dependence of water-absorption capacity on the amount of crosslinking agent, oil/water ratio, degree of neutralization and the composition of the copolymer were systematically investigated. Furthermore, the swelling kinetics of the super water-absorbent copolymer was carried out. The absorption of the resins is more than 1800 g/g for deionized water and 100 g/g for 0.9% NaCl solution, respectively. The copolymers showed an increased salt resistance and enhanced water retention of soil.

• Journal of Powder Materials
• /
• v.18 no.4
• /
• pp.347-358
• /
• 2011

Two different schemes were adopted to fabricate ordered macroporous structures with face centered cubic lattice of air spheres. Monodisperse polymeric latex suspension, which was synthesized by emulsifier-free emulsion polymerization, was mixed with metal oxide ceramic nanoparticles, followed by evaporation-induced self-assembly of the mixed hetero-colloidal particles. After calcination, inverse opal was generated during burning out the organic nanospheres. Inverse opals made of silica or iron oxide were fabricated according to this procedure. Other approach, which utilizes ceramic precursors instead of nanoparticles was adopted successfully to prepare ordered macroporous structure of titania with skeleton structures as well as lithium niobate inverted structures. Similarly, two different schemes were utilized to obtain disordered macroporous structures with random arrays of macropores. Disordered macroporous structure made of indium tin oxide (ITO) was obtained by fabricating colloidal glass of polystyrene microspheres with low monodispersity and subsequent infiltration of the ITO nanoparticles followed by heat treatment at high temperature for burning out the organic microspheres. Similar random structure of titania was also fabricated by mixing polystyrene building block particles with titania nanoparticles having large particle size followed by the calcinations of the samples.

• Fibers and Polymers
• /
• v.5 no.2
• /
• pp.95-104
• /
• 2004

A series of superabsorbents based on acrylic acid (AA), sodium acrylate, 2-acrylamido-2-methylpropane sulphonic acid, N,N'-methylene bis-acrylamide (MBA) were prepared by inverse suspension polymerization. These hydrogels were further crosslinked on the surface with polyethylene glycol-600 (PEG-600). The water absorbency or swelling behaviors for these xerogels in water and 0.9% saline solutions, both under free condition and under load were investigated. Absorption characteristics of these hydrogels were found to depend on nature and concentration of crosslinker in the system. It was also found that the saline absorption was significantly improved as the incorporation of AMPS in the polymer was increased. The surface crosslinking introduced in the polymers was found to improve the absorption under load characteristics without lowering the free water absorption capacities of the polymer to a considerable extent.

• Polymer(Korea)
• /
• v.28 no.1
• /
• pp.18-23
• /
• 2004

Superabsorbent poly(potassium acrylate-co-acrylamide)s were synthesized in particle form using inverse suspension polymerization technique. Mean diameter of the prepared polymer particles decreased from 300 to 50 $\mu\textrm{m}$ with increasing surfactant concentration. The dynamic and equilibrium swelling behaviors during water absorption and drying process were investigated by weight measurement. The swelling ratio of polymer particles in water changed according to not only polymer crosslinking density, but particle size, saline concentration of aqueous medium, and copolymer compositions. Water sorption amount was increased with decreasing particle size, crosslinking agent concentration, and ion concentration in bulk solution. Being different from the water sorption process, the drying process was not significantly affected by particle size, polymer composition, or crosslinking amount.

• Polymer(Korea)
• /
• v.38 no.6
• /
• pp.760-766
• /
• 2014

Bead type super-absorbent resins to be used for release-control were prepared by modification of the inverse suspension polymerization, and their physical properties were characterized. Acrylic acid and acrylamide were used as monomers, and N,N-methylenebisacrylamide was used as crosslinker, controlling the viscosity of monomer solution by adding hydroxyethylcellulose (HEC). SEM studies of the synthesized beads verified that the bead surfaces had many pores with their diameters of several tens nm. The bead sizes were in the range of $500{\sim}3000{\mu}m$, depending on the viscosity of the monomer solution. Both absorbent amount and absorbent rate of the beads were inversely proportional to the bead size, and the maximum water absorbent amount of 1 g beads was determined to be ca. 170~200 g for 5 hrs. The absorbent rate was also dependent on pH change of the aqueous solution, exhibiting the maximum rate in pH ranging from 5 to 11. The absorbent rate decreased as the concentration of salt (NaCl and $MgCl_2$) or ethanol and ethylene glycol increased. Release time of the water absorbed into the bead resins was 700 hrs, confirming the usefulness of the resin for the good release-control materials.

• Applied Chemistry for Engineering
• /
• v.7 no.1
• /
• pp.136-144
• /
• 1996

Polyacrylic super absorbent polymer(SAP) containing sorbitol was synthesized by inverse-suspension polymerization method. Sodium acrylate and acrylic acid were used as a monomer, ethylene glycol dimethacrylate(EGDMA) and glycerol polyglycidyl ether(GPGE) were used as a crosslinking agent, potassium persulfate(PPS) was used as an initiator, and cyclohexane was used as a solvent. Content of sorbitol was from 10mol% to 50mol% according to the mol ratio of acrylic acid monomer. The size distribution of the round shaped polymeric particle was $177{\sim}707{\mu}m$. Absorption amount of the polymer containing sorbitol was 785 to 1086 times of the polymer weight in distilled water, was 50 to 83 times in 0.9 % NaCl solution. Absorption and retention amount of the polymer were decreased with increasing the amount of sorbitol, but the polymer has an endothermic property which is +5 cal/g SAP.