• Journal of information and communication convergence engineering
• /
• v.9 no.5
• /
• pp.587-590
• /
• 2011

The absence of deep traps for electrons in the spectrum of $As_{40}Se_{30}S_30$ localized states films obtained by ion sputtering was determined. Bipolar drift of charge carriers was found in amorphous $As_{40}Se_{30}S_30$ films of chalcogenide glassy semiconductors, obtained by ion-plasma sputtering of high-frequency, unlike the films of these materials obtained by thermal evaporation.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.35-35
• /
• 2001

agnesium Oxide (MgO) with a NaCI structure is well known to exhibit high secondary electron emission, excellent high temperature chemical stability, high thermal conductance and electrical insulating properties. For these reason MgO films have been widely used for a buffer layer of high $T_c$ superconducting and a protective layer for AC-plasma display panels to improve discharge characteristics and panel lifetime. Up to now MgO films have been synthesized by lE-beam evaporation, Molecular Beam Epitaxy (MBE) and Metalorganic Chemical Vapor Deposition (MOCVD), however there have been some limitations such as low film density and micro-cracks in films. Therefore magnetron sputtering process were emerged as predominant method to synthesis high density MgO films. In previous works, we designed and manufactured unbalanced magnetron source with high power density for the deposition of high quality MgO films. The magnetron discharges were sustained at the pressure of O.lmtorr with power density of $110W/\textrm{cm}^2$ and the maximum deposition rate was measured at $2.8\mu\textrm{m}/min$ for Cu films. In this study, the syntheses of MgO films were carried out by unbalanced magnetron sputtering with various $O_2$ partial pressure and specially target power densities, duty cycles and frequency using pulsed DC power supply. And also we investigated the plasma states with various $O_2$ partial pressure and pulsed DC conditions by Optical Emission Spectroscopy (OES). In order to confirm the relationships between plasma states and film properties such as microstructure and secondary electron emission coefficient were analyzed by X-Ray Diffraction(XRD), Transmission Electron Microscopy(TEM) and ${\gamma}-Focused$ Ion Beam (${\gamma}-FIB$).

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.155.2-155.2
• /
• 2013

Strain-relaxed SiGe layer on Si substrate has numerous potential applications for electronic and opto- electronic devices. SiGe layer must have a high degree of strain relaxation and a low dislocation density. Conventionally, strain-relaxed SiGe on Si has been manufactured using compositionally graded buffers, in which very thick SiGe buffers of several micrometers are grown on a Si substrate with Ge composition increasing from the Si substrate to the surface. In this study, a new plasma process, i.e., the combination of PIII&D and HiPIMS, was adopted to implant Ge ions into Si wafer for direct formation of SiGe layer on Si substrate. Due to the high peak power density applied the Ge sputtering target during HiPIMS operation, a large fraction of sputtered Ge atoms is ionized. If the negative high voltage pulse applied to the sample stage in PIII&D system is synchronized with the pulsed Ge plasma, the ion implantation of Ge ions can be successfully accomplished. The PIII&D system for Ge ion implantation on Si (100) substrate was equipped with 3'-magnetron sputtering guns with Ge and Si target, which were operated with a HiPIMS pulsed-DC power supply. The sample stage with Si substrate was pulse-biased using a separate hard-tube pulser. During the implantation operation, HiPIMS pulse and substrate's negative bias pulse were synchronized at the same frequency of 50 Hz. The pulse voltage applied to the Ge sputtering target was -1200 V and the pulse width was 80 usec. While operating the Ge sputtering gun in HiPIMS mode, a pulse bias of -50 kV was applied to the Si substrate. The pulse width was 50 usec with a 30 usec delay time with respect to the HiPIMS pulse. Ge ion implantation process was performed for 30 min. to achieve approximately 20 % of Ge concentration in Si substrate. Right after Ge ion implantation, ~50 nm thick Si capping layer was deposited to prevent oxidation during subsequent RTA process at $1000^{\circ}C$ in N2 environment. The Ge-implanted Si samples were analyzed using Auger electron spectroscopy, High-resolution X-ray diffractometer, Raman spectroscopy, and Transmission electron microscopy to investigate the depth distribution, the degree of strain relaxation, and the crystalline structure, respectively. The analysis results showed that a strain-relaxed SiGe layer of ~100 nm thickness could be effectively formed on Si substrate by direct Ge ion implantation using the newly-developed PIII&D process for non-gaseous elements.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.178-178
• /
• 2016

Every display is equipped with a cover glass to protect the underneath displaying devices from mechanical and environmental impact during its use. The strengthened glass such as Gorilla glass.$^{TM}$ has been exclusively adopted as a cover glass in many displays. Conventionally, the strengthened glass has been manufactured via ion-exchange process in wet salt bath at high temperature of around $500^{\circ}C$ for hours of treatment time. During ion-exchange process, Na ions with smaller diameter are substituted with larger-diameter K ions, resulting in high compressive stress in near-surface region and making the treated glass very resistant to scratch or impact during its use. In this study, PIIID (plasma immersion ion implantation and deposition) technique was used to implant metal ions into the glass surface for strengthening. In addition, due to the plasmonic effect of the implanted metal ions, the metal-ion implanted glass samples got colored. To implant metal ions, plasma immersion ion implantation technique combined with HiPIMS method was adopted. The HiPIMS pulse voltage of up to 1.4 kV was applied to the 3" magnetron sputtering targets (Cu, Ag, Au, Al). At the same time, the sample stage with glass samples was synchronously pulse-biased via -50 kV high voltage pulse modulator. The frequency and pulse width of 100 Hz and 15 usec, respectively, were used during metal ion implantation. In addition, nitrogen ions were implanted to study the strengthening effect of gas ion implantation. The mechanical and optical properties of implanted glass samples were investigated using micro-hardness tester and UV-Vis spectrometer. The implanted ion distribution and the chemical states along depth was studied with XPS (X-ray photo-electron spectroscopy). A cross-sectional TEM study was also conducted to investigate the nature of implanted metal ions. The ion-implanted glass samples showed increased hardness of ~1.5 times at short implantation times. However, with increasing the implantation time, the surface hardness was decreased due to the accumulation of implantation damage.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1996.02a
• /
• pp.102-102
• /
• 1996

This paper represents a new type low power High Frequency technological ion source (HF TIS) for ion - beam processing: the surface modification of materials, cleaning of surface, sputtering, coating of thin films, and polishing. The operational principle of HF TIS is based on the excitation of electrostatic waves in plasma located in the external magnetic field. Low power HF TIS with diameter 92 rom gives the opportunity to obtain beams of inert and chemically reactive gases with currents range from 5 to 150 mA (current density $0.015\;~\;3.5\;mA/\textrm{m}^2$) and ion beam energy 100 ~ 2500 eV at a HF power level 10 ~ 150 W. Three grid concave type ion optical system (IOS) is used for extraction and formation ofion beam.n beam.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.212-212
• /
• 1999

Ar-O2 분위기의 Plasma 표면 처리된 OPP 의 polymer 위에 약 400$\AA$ 정도로 sputter 코팅된 Al의 부착력에 관하여 연구를 하였다. 금속과 polymer와 같이 성질이 서로 다른 물질이 서로 결합할 때 접착력은 제품의 성능과 신뢰도를 결정하는데 매우 중요한 인자이다. 최근 고분자재료의 표면을 플라즈마 처리 (plasma surface treatment)에 의해 고분자와 금속도포(coating) 층간의 접착력향상에 따라, 증착필름 및 인쇄용 필름 등의 기능도 향상시킬 수 있다. 저온 plasma를 이용한 표면처리는 plastic 재료가 가지고 있는 기본적인 특성을 저해하지 않고, 그 표면 층만을 개량하는 plasma 또는 sputter etching 갚은 electrical discharge 방법은 진공 증착 방식에서 많이 사용되고 있다. 7$\mu\textrm{m}$의 두께 OPP polymer를 10m/min의 속도로 OPP의 표면을 연속 plasma pretreatment를 하였다. 5$\times$10-2torr에서, PEM(Plasma Emission Monitor)를 이용하여 plasma intensity에 따른 Ar/O2비를 변화시키면서 test를 하였다. AFM과 XPS를 이용하여 OPP의 표면분석을 하였다. 이 plasma처리는 기존의 D.C plasma 처리 방식과는 달리 Midium frequency AC voltage hollow cathod 방식으로 plasma를 발생된 high energy plasma 분위기를 만들 수 있다. 이러한 방식은 -cycle일 때 plasma로부터 발생된 전자가 polymer 표면을 bombard 하게 되고, +cycle 일 때 polymer 표면이 cathod 가 되어 active ion에 의해 sputtering 이 된다. 이때 plasma 처리기의 polymer 기판 후면에 magnet를 설치하여 높은 ionization을 발생시켜 처리 효과를 한층 높여 주었다. 이 plasma 처리는 표면 청정화, 표면 etching 이 동시에 행하는 것과 함께 장시간 처리에 의해 표면에서는 미세한 과, C=C기, -C-O-의 극성기의 도입에 의한 표면 개량이 된다는 것을 관찰할 수 있다. OPP polymer 표면을 Ar 100%로 plasma 처리한 경우 C-O, C=O 등의 carbonyl가 발생됨을 알 수 있었다. C-O, C=O 등의 carbynyl polor group이 도입됨에 따라 sputter된 Al의 접착력이 향상됨을 알 수 있으며, TEM 관찰 결과 grain size도 상당히 작아짐을 알 수 있었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.107-107
• /
• 2017

전자제품의 성능이 향상됨에 따라서 전자제품에 사용되는 부품의 고집적화가 필연적으로 요구되고 있으며, 고집적화 된 전자제품의 방열(heat dissipation)에 관한 문제점이 대두되고 있다. 방열은 전자기기의 성능과 수명을 유지하는데 있어서 중요한 문제 중 하나로서 방열 효과를 높이기 위해 다양한 연구 개발이 진행 중이다. 방열에 사용되는 소재로는 Cu가 있으며, 저렴한 가격과 상대적으로 높은 방열 효율을 가지는 장점이 있다. Cu는 전기 도금 증착 방법을 사용하여왔으나, 전기도금 방식으로 증착된 Cu 방열판은 제품에 열이 축적될 경우 Cu와 substrate 사이의 residual stress로 인해 박리나 뒤틀림 현상 등이 발생하여 high power를 사용하는 device의 방열 소재로 사용하기에는 개선해야 할 문제점이 있다. 이러한 문제점을 극복하기 위한 방법으로 magnetron sputter 증착 방법이 있으며, magnetron sputter은 대면적화가 용이하고, 다양한 물질의 증착이 가능한 장점으로 인해 hard coating 또는 thin film 증착과 같은 공정에 사용되고 있다. 특히 증착된 film의 특성을 조절하기 위해서 magnetron sputter에 pulse 또는 ICP (inductively coupled plasma) assisted 등을 적용하여 plasma 특성을 조절하는 방법 등에 관한 연구가 보고되고 있다. 본 연구에서는 pulsed magnetron sputtering 방식을 이용하여 증착된 Cu film 특성 변화를 확인하였다. 다양한 pulsing frequency와 pulsing duty ratio 조건에서, Si substrate 위에 증착된 Cu film과의 residual stress 변화를 측정하였다. Pulse duty ratio가 90% 에서 60%로 감소함에 따라서 Cu film의 residual stress가 감소하였고, pulsing frequency가 증가함에 따라 Cu film의 residual stress가 감소하는 것을 확인하였다. 증착 조건에 따른 plasma의 특성 분석을 위하여 oscilloscope를 이용하여 voltage와 current를 측정하였고, Plasma Sampling Mass spectrometer 를 이용하여 ion energy의 변화를 측정하였다. 이를 통해 plasma 특성 변화가 증착된 Cu film에 미치는 영향과 residual stress의 변화에 대한 연관성에 대하여 확인할 수 있었다.