• Journal of the Korean Wood Science and Technology
• /
• v.44 no.5
• /
• pp.677-684
• /
• 2016

This study was carried out to confirm the effects of the knife-incising and longitudinal kerfing treatment on high-temperature drying characteristics of red pine square timber with dimensions of thickness 15 cm. The range of final moisture content was investigated 5.6% to 7.5% after drying. The differences did not exist in the moisture content and distribution according to the pretreatment condition. In the case of longitudinal kerfing treatment, the surface check occurrence was reduced than the control. In addition, the twist had a tendency to decrease due to the longitudinal kerfing treatment. The knife-incising and longitudinal kerfing treatment were investigated to be ineffective on internal checks and drying shrinkage.

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.4
• /
• pp.51-60
• /
• 1997

We investigated the characteristics of air-and vacuum-drying heated by hot plates for 8~14cm-diameter logs or 6~12cm-thick pillars of Pinus koraiensis. And we evaluated the effects of longitudinal kerf and vacuum drying heated by hot plates. The vacuum drying times from green to 10.9~18.6% MC were 15 days, and these times were one-fifth compared to the air-drying times. The longitudinal kerfing had no significant, effect on drying rates during both air-drying and vacuum drying. But drying defects such as surface checks and V-shaped cracks were effectively prevented during air-drying and vacuum drying by longitudinal kerfing. The vacuum drying was more advantageous than air-drying for preventing of surface checks, end checks and V-shaped cracks, and especially, the vacuum dried pillars with longitudinal kerf were almost free from drying defects. In accelerated weathering conditions the resin did not exude for all specimens.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.5
• /
• pp.726-735
• /
• 2016

This study was carried out to evaluate the high-temperature drying characteristics of douglas-fir, hemlock, and radiata pine square timber with dimensions of thickness 15 cm and 18 cm. As a result, radiata pine showed the lowest final moisture content followed by douglas-fir and hemlock without reference to the timber size. Moreover, when the longitudinal kerfing is processed, the final moisture content was lower than control. The kerfing treatment was effective to decreasing the twist of radiata pine and hemlock. When douglas-fir is processed to the shape like the edge-grained timber that does not include the pith, the decrease of drying defect was possible.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.3
• /
• pp.345-363
• /
• 2020

This study was conducted to identify the effect of kerfing and incising pretreatments on high-temperature drying characteristics of cedar and larch boxed-heart timbers with a cross section of less than 150 mm. The result showed that the pretreatments have made a significant difference regarding surface check and shrinkage. Although the kerfing was suitable as a pretreatment to reduce the occurrence of surface check, the incising was not suitable as a pretreatment since the knives of timber joined together, causing the conversion to the surface checks. The shrinkage showed a significant result that the final moisture content was reduced in the order of incising, kerfing, and kerfing-incising after the drying process based on the pretreatment condition. Twist was more affected by the grain angle than the anisotropy of the juvenile wood, and there was no effect of pretreatments.

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.2
• /
• pp.132-139
• /
• 2011

This study examined the characteristics of radio-frequency/vacuum dried Korean red pine ($Pinus$ $densoflora$) heavy timbers with 250 ${\times}$ 250 mm (S), 300 ${\times}$ 300 mm (L) in cross section and 300 mm in diameter, and 3,600 mm in length, which were subjected to compressive loading after a kerf pretreatment. The following results were obtained : The drying time was short and the drying rate was high in spite of the large cross section of specimens. The moisture gradient inall specimens was gentle in both longitudinal and transverse directions owing to dielectric heating. The shrinkage of the width in the direction perpendicular to was 21 percent ~ 76 percent of that of the thickness of square timbers in the direction parallel to the mechanical pressure. The casehardening for all specimens was very slight because of significantly reduced ratio of the tangential to radial shrinkage of specimens and kerfing. The surface checks somewhat severely occurred although the occurrence extent of the surface checks on the kerfed specimens was slight compared withthat on the control specimen.