• Composites Research
• /
• 제29권5호
• /
• pp.293-298
• /
• 2016

본 연구에서는 PPS(Polyphenylene sulfide) 수지와 단면이 원형(round type), 누에형(cocoon type), 플랫형(flat type)인 3종류의 유리섬유를 사용하여 컴파운딩 및 사출을 통해 차량 전조등 광원 모듈용 유리섬유 강화 열가소성 플라스틱(glass fiber reinforced thermoplastic : GFRTP)을 제조하였다. 섬유 단면형태 및 함유량에 따른 효과를 알아보기 위해 인장, 굴곡, 충격 특성을 평가하였고, 단면에 따른 유동성, 형태안정성 및 평탄성을 관찰하였다. 그 결과 플랫 단면의 유리섬유를 사용했을 때 기계적 특성이 가장 우수했고 섬유함유량이 증가할수록 강도가 향상되는 경향을 보였다. 또한, 형태안정성, 평탄성의 경우에도 플랫 단면 섬유 사용 시 더 좋은 결과를 나타내었다.

• 한국재료학회지
• /
• 제33권10호
• /
• pp.414-421
• /
• 2023

Infrared radiation (IR) refers to the region of the electromagnetic radiation spectrum where wavelengths range from about 700 nm to 1 mm. Any object with a temperature above absolute zero (0 K) radiates in the infrared region, and a material that transmits radiant energy in the range of 0.74 to 1.4 um is referred to as a near-infrared optical material. Germanate-based glass is attracting attention as a glass material for infrared optical lenses because of its simple manufacturing process. With the recent development of the glass molding press (GMP) process, thermal imaging cameras using oxide-based infrared lenses can be easily mass-produced, expanding their uses. To improve the mechanical and optical properties of commercial materials consisting of ternary systems, germanate-based heavy metal oxide glasses were prepared using a melt-cooling method. The fabricated samples were evaluated for thermal, structural, and optical properties using DSC, XRD, and XRF, respectively. To derive a composition with high glass stability for lens applications, ZnO and Sb₂O₃ were substituted at 0, 1, 2, 3, and 4 mol%. The glass with 1 mol% added Sb₂O₃ was confirmed to have the optimal conditions, with an optical transmittance of 80 % or more, a glass transition temperature of 660 ℃, a refractive index of 1.810, and a Vickers hardness of 558. The possibility of its application as an alternative infrared lens material to existing commercial materials capable of GMP processing was confirmed.

• 한국정밀공학회지
• /
• 제29권12호
• /
• pp.1267-1271
• /
• 2012

Demand for optical glass device used for lighting could increase rapidly because of LED lighting market growth. The optical glass devices that have been formed by hot press molding process the desired optical performance without being subjected to mechanical processing such as curve generation or grinding. EL-Max material has been used for many engineering applications because of their high wear resistance, high compressive strength, corrosion resistant and very good dimensional stability. EL-Max is very useful for a glass lens mold especially at high temperature and pressure. The performance and reliability of optical components are strongly influenced by the surface damage of EL-Max during grinding process. Therefore, the severe process condition optimization shall be necessary for the highly qualified EL-Max glass lens mold. To get the required qualified surface of EL-Max, the selection of type of the diamond wheel is also important. In this paper, we report best grinding conditions of ultra-precision grinding machining. The grinding machining results of the form accuracy and surface roughness have been analyzed by using Form Talysurf and NanoScan.

• Korean Chemical Engineering Research
• /
• 제50권2호
• /
• pp.264-269
• /
• 2012

플라스틱 제품의 다이슬라이드식 사출성형은 기존 사출공법의 부가공정을 삭제하여 제품 생산에 요구되는 비용과 시간을 현저히 줄여준다. 그러나 다이슬라이드식 사출성형은 사출제품의 백화, 수지침투, 기공, 수지넘침 등의 결함들을 해결해야한다. 본 연구에서는 사출성형의 공정파라미터들을 유한요소법과 다구치법을 사용하여 최적화하고자 한다. 사출 성형해석은 Moldflow insight 2010 코드로 해석하며 2차 사출에서는 다단 사출코드를 적용한다. 폴리프로필렌(PP)을 밀폐용기인 냉각수 보조탱크로 성형할 때 사용하는 공정파라미터들은 다구치법의 망소특성과 $L_{16}$ 직교배열을 사용한 실험계획을 통해 최적화된다. 한편 최적값은 유의수준 5% 수준의 분산분석을 통해 타당성을 검증한다. 그리고 최적화 조건에서 성형된 제품과 기존 제품의 치수정확도를 비교한 결과 치수안정성이 5% 이상 개선됨을 확인하였다.

• Composites Research
• /
• 제36권5호
• /
• pp.310-314
• /
• 2023

VaRTM(Vacuum assisted resin transfer molding)과 VAP(Vacuum assisted process) 공정은 RTM(Resin transfer modling) 공정의 한 종류로서, 대형구조물을 저가에 제작할 수 있는 대표적인 탈 오토클레이브(OOA, Out of Autoclave) 공정이다. 본 논문에서는 VaRTM과 VAP 공정을 상호 비교하기 위하여 수지 충진시험을 진행하였으며, 충진과정과 치수 안정성 등을 상호 비교하였다. 또한, 충진과정을 모사할 수 있는 해석기법을 개발하였으며, 유전센서를 사용하여 수지의 유동선단을 검출하여 이를 해석결과와 상호 비교하였다. 수지 충진시험 결과, 복합재 평판의 총 충진시간은 VAP공정은 48분, VaRTM 공정은 145분으로 측정되어, VAP 공정에 의한 충진시간이 VaRTM 대비 약 67% 단축되었으며, VAP공정이 VaRTM 공정에 비해 복합재 평판의 두께조절능력과 균일도가 우수함을 확인하였다.

• Design & Manufacturing
• /
• 제2권3호
• /
• pp.28-31
• /
• 2008

In recent, the demand of high-productivity injection mold is increased because of the growth of international packaging market which is induced by an increase of population. The increase of productivity leads to the large-capacity injection molding machine and peripheral devices. For solving this problem, the stack mold which is based on the exsiting machine and device has researched in advanced countries actively. In this paper, as the preliminary research of stack mold development, the stack mold which has 2 level ${\times}4$ cavity was designed and fabricated. Besides, the motion and structural analysis were performed to verify the stability of developed stack mold.

• 패션비즈니스
• /
• 제26권5호
• /
• pp.122-134
• /
• 2022

This study is conducted on hardening leather with improved firmness and stability of shape, based on research on types and thickness of leather. The purpose of this study is to test the physical properties of the leather for molding to prepare the foundation for leather molding based on the test results using four methods by thickness of Vegetable and Split. The tests were conducted using a total of five leather types, including three types of vegetable leathers and two types of split, by thickness. Based on the testing method for leathers in KS M 6882, the tests were performed at 27℃ with relative humidity of 65±20%. The samples were prepared with cowhide, size 9cm× 2cm. The measurement parameters are length and width. thickness, volume, mass, density. Regarding the hardening treatment method, changes in appearance and major physical characteristics of leather were reviewed by soaking in hot water, dry heating, hammering, waxing, and olive oil coating. The study results are as follows. In planar works, it is judged that hardening work using a hammer is more suitable for stiffness or density in order to prevent easy breakage with adult muscle density, rather than boiling water or baking. In conclusion, there is no curling, soot, or breaking phenomenon, and the densest curing method is 50℃ for 20 sec of V2 and 75℃ for 60 sec of V2 in boiling water. The combination of paraffin treatment improve waterproof and quality.

• 펄프종이기술
• /
• 제43권2호
• /
• pp.66-71
• /
• 2011

Biocomposites were fabricated with biodegradable polymers and natural fibers. Biocomposites have benefits of low cost, low density, and biodegradability over inorganic fiber composite, and give comparable strength properties. Hydrophobic polymer used for sizing in paper industry, AKD (Akenyl Keten Dimer), was applied to natural fibers, red algae fibers (RAF) in this study, to make fiber surfaces more compatible to hydrophobic nature of matrix polymers. Composites with RAF, kenaf, glass fibers, and carbon fibers have been fabricated by a compression molding method and their thermo-mechanical properties have been studied. Also, the thermal dimensional stability test was done from at 30 to $100^{\circ}C$. The storage moduli and the thermo-mechanical stabilities of polypropylene and poly lactic acid based biocomposites were improved by reinforcing with the RAF and much more with AKD treated fibers. Dimensional stability of biocomposite was also markedly improved by AKD pretrement on RAF.

• 한국산학기술학회논문지
• /
• 제12권7호
• /
• pp.2919-2924
• /
• 2011

자동서랍함용 완충기는 서랍을 여닫을 때 충격을 흡수하고 속도를 조절하는 역할을 해 준다. 완충기 튜브는 완충기의 구성품을 에워 쌓고 있는 원통 모양의 케이스이며 아세탈 재질로 되어있다. 본 연구는 사출 성형 공정에서 제작된 완충기 튜브의 품질 안정성을 평가하는 데 목적이 있다. 완충기 튜브는 4 캐비티 냉각장치를 갖춘 사출 성형공정에서 제작된다. 본 연구에서는 완충기 튜브의 품질 안정을 판단하기 위해 분석과 시험이 수행되었다. 분석과 시험은 컴퓨터 시뮬레이션을 통한 품질 분석과 연구된 튜브에 대한 외산품과의 성능 비교 시험이다. 사출 압력은 87.6 MPa로, 전체 휨량은 0.07~1.0 mm로 계산하였다. 연구된 튜브와 외산품을 비교해 볼 때 튜브의 최대 압축-하중은 231 kgf, 구간별 변위-하중은 0.05 kgf, 그리고 또 튜브 내경의 표면거칠기(Ra)는 $0.02\;{\mu}m$ 향상되었다. 결과적으로 사출 성형 공정에서 제작되어지는 연구된 튜브의 품질은 안정되었고 성능이 우수함을 알 수 있었다.

• 한국응용과학기술학회지
• /
• 제24권3호
• /
• pp.278-286
• /
• 2007

As a part of enhancing the performance of wood-plastic composites (WPC), polypropylene (PP)/ nanoclay (NC)/ wood flour (WF) nanocomposites were prepared using melt blending and injection molding process to evaluate their thermal stability. Thermogravimetric analysis (TGA) was employed to investigate thermal degradation kinetics of the nanocomposites both dynamic and isothermal conditions. Dynamic scans of the TGA showed an increased thermal stability of the nanocomposites at moderate wood flour concentrations (up to 20 phr, percentage based on hundred percent resin) while it decreased with the addition of 30 phr wood flour. The activation energy $(E_a)$ of thermal degradation of nanocomposites increased when nanoclay was added and the concentration of wood flour increased. Different equations were used to evaluate isothermal degradation kinetics using the rate of thermal degradation of the composites, expressed as weight loss (%) from their isothermal TGA curves. Degradation occurred at faster rate in the initial stages of about 60 min., and then proceeded in a gradual manner. However, nanocomposites with wood flour of 30 phr heated at $300^{\circ}C$ showed a drastic difference in their degradation behavior, and reached almost a complete decomposition after 40 min. of the isothermal heating. The degree of decomposition was greater at higher temperatures, and the residual weight of isothermal degradation of nanocomposites greatly varied from about 10 to 90%, depending on isothermal temperatures. The isothermal degradation of nanocomposites also increased their thermal stability with the addition of 1 phr nanoclay and of wood flour up to 20 phr. But, the degradation of PP100/NC1/MAPP3/WF30 nanocomposites with 30 phr wood flour occurs at a faster rate compared to those of the others, indicating a decrease in their thermal stability.