In our previous publication, the problem of particle deformation and coagulation at the nucleation stage in the presence of cross-linker was intensely studied by seeded batch dispersion polymerization of methyl methacrylate (MMA). In the present work, highly cross-linked, monodisperse PMMA particles were prepared under various reaction conditions by seeded semi-continuous process. Monodisperse, $6.5{\mu}m$-diameter PMMA particles containing up to 8 wt% of DVB or EGDMA were successfully made by seeded semi-continuous process and multi-semi-continuous addition process, respectively. Therefore, this study shows that seeded semi-continuous process is more effective and efficient to prepare highly cross-linked, monodisperse particles than non-seeded and seeded batch processes.

• Korean Chemical Engineering Research
• /
• v.54 no.6
• /
• pp.792-799
• /
• 2016

Monodisperse silica nanospheres were synthesized by Stober method using rotating cylinder systems with batch or continuous manner. The particle size could be controlled by adjusting the reactant compositions such as the amount of monomer, catalyst, and water in the reaction mixture. The size and monodispersity of the ceramic particles could be controlled by changing the reaction medium with different alcohols other than ethanol or changing the reaction temperature. The effect of Taylor number (Ta) on the average diameter and standard deviation of silica particles were also studied by adjusting the rotation speed of inner cylinder, and the maximum diameter of particles was observed at Ta ${\approx}3,000$.

• Proceedings of the Korea Air Pollution Research Association Conference
• /
• 2001.11a
• /
• pp.101-102
• /
• 2001

Monodisperse aerosols containing spherical particles of known size, shape and density are the most widely used to calibrate particle-size measuring instruments and to determine the effects of particle size on the sampling device. However, these tests are time-consuming because monodisperse aerosols with different particle sizes are generated and tested in a series of experiments. Polydisperse aerosols may be used to determine the calibration or to simulate equipment under controlled laboratory condition. (omitted)

• Polymer(Korea)
• /
• v.30 no.1
• /
• pp.50-55
• /
• 2006

When the monodisperse polystyrene(PS)/HDDA polymer particles were synthesized via one-step polymerization using polystyrene seed particles by dispersion polymerization, the effects of 1) the molecular weight of seed polymer particles, 2) the ratio of the absorbed HDDA to the seed polymer particles (swelling ratio) and 3) seeded polymerization rate on the surface morphology of PS/HDDA polymer particles were investigated. It was observed that the creation of the crater shaped defect on the surface of PS/HDDA polymer particles was irrespective of the molecular weight of seed polymer ant swelling ratio. But its surface morphology could be controlled by the change of the seeded polymerization rate.

• Korean Chemical Engineering Research
• /
• v.45 no.6
• /
• pp.677-679
• /
• 2007

Nearly monodisperse spherical silica particles, 200~300 nm in diameter, were produced via a dry route for the first time through a two-stage hydrolysis of $SiCl_4$ vapor. In the first stage, the $SiCl_4$ was partially hydrolyzed in a batch reactor at $150^{\circ}C$ to form nearly monodisperse silicon oxychloride particles. In the second stage, the oxychlorides were hydrolyzed further in a tubular reactor to have produced silica with the morphology and size nearly conserved.

• Journal of the Korean Ceramic Society
• /
• v.46 no.5
• /
• pp.472-477
• /
• 2009

Monodisperse spherical $SiO_2$ particles of various sizes ($\sim$350 nm and $\sim$800 nm) and size distributions were synthesized from TEOS and MTMS. The particle size and size distribution were controlled by changing the volume ratio of water to ethanol and the reaction temperature. Narrow-sized $SiO_2$ particles with $\sim$3% size distribution were obtained. Self-assembly of the $SiO_2$ particles for photonic crystals were performed by the solvent evaporation method. The number of ordered $SiO_2$ layers can be controlled by changing the amount of the dispersed $SiO_2$ volume fraction in the solvent.

• Polymer(Korea)
• /
• v.30 no.4
• /
• pp.332-337
• /
• 2006

Monodisperse polymer particles were prepared via one-step seeded polymerization using PMMA seed particles and HDDA (or EGDMA) as crosslinking monomer. For the study, the effects of 1) the ratio of the absorbed monomer or monomer mixture to the seed polymer particles (swelling ratio), 2) the ratio of EGDMA in absorbed monomer mixture, 3) the dosage of initiator, and 4) electro less Ni plating on the variation of mechanical properties of monodisperse polymer particles, such as recovery rate, K-values, breaking strength and breaking displacement, were investigated by using MCT (micro compression test). It was observed that monomer swelling ratio influenced only breaking strength, but EGDMA ratio in monomer mixture, dosage of initiator and electroless Ni plating affected both K-values and breaking strength.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.1
• /
• pp.129-132
• /
• 2009

Monodisperse ZnS colloidal particles with precisely specified diameters over a broad size range were synthesized by controlled aggregation. Sub-10nm ZnS seed crystals were first nucleated at ambient temperature and then grown at an elevated temperature, which produced large polydisperse colloidal particles. Subsequent rapid thermal quenching and heating processes induced a number of secondary nucleations in addition to growing the large polydisperse microparticles which were finally removed by centrifugation and discarded at the completion of the reaction. The secondary nuclei were then aggregated further at elevated temperatures, resulting in colloidal particles which exhibited a nearly monodisperse size distribution. Particle diameters were controlled over a wide size range from 50 nm to 1 μm. Mie simulations of the experiment extinction spectra determined that the volume fraction of the ZnS is 0.66 in an aggregated colloidal particle and the colloidal particle effective refractive index is approximately 2.0 at 590 nm in water. The surface of the colloidal particles was subsequently coated with silica to produce ZnS@silica core-shell particles.

• Macromolecular Research
• /
• v.16 no.5
• /
• pp.399-403
• /
• 2008

Monodisperse, micron-sized, hybrid particles having a core-shell structure were prepared by coating the surface of poly(methyl methacrylate)(PMMA) microspheres with silica and by copolymerizing acrylamide (AAm) to supply the hydrogen bonding effect by means of the amide groups. Tetraethoxysilane (TEOS) was then slowly dropped onto the medium under certain conditions. Because of the hydrogen bonding between the amide of the PMMA particles and the hydroxyl group of the hydrolyzed silanol, a silica shell was generated on the PMMA core particles. The morphology of the hybrid particles was investigated with transmission (TEM) and scanning (SEM) electron microscopy as a function of the medium conditions and the amount of TEOS. Improved thermal properties were observed by TGA analysis.

• Polymer(Korea)
• /
• v.31 no.5
• /
• pp.410-416
• /
• 2007

Monodisperse polymer particles were prepared via one- step seeded polymerization using PMMA as seed particles, and HDDA, triEGDMA or EGDMA as crosslinking monomer. For the study, the effects of 1) the ratio of the absorbed monomer to the seed polymer particles (swelling ratio), 2) the characteristics of crosslinking monomer, 3) electroless Ni plating, and 4) electroless Au Plating on the variation of mechanical properties of polymer particles, such as recovery rate, K-values, breaking strength and breaking displacement were investigated by using MCT (micro compression test). It was observed that swelling ratio of polymer particles influenced only on breaking strength of polymer Particles, while electroless plating did on recovery rate, K-values ($K_{10}\;and\;K_{20}$) and breaking strength of electroless plated polymer particles. However, breaking displacement and K-values ($K_{30}{\sim}K_{50}$) were more or less insensitive to electroless plating.