• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2000.04a
• /
• pp.81-86
• /
• 2000

To evaluate the possibility of the partial melting soldering. wettability of partial melted solders was measured using wetting balance. Off eutectic Sn-Pb allows are wettable in their partial melting zone. Especially, Pb rich alloys showed excellent wettability while wettability of Sn rich alloys were adequate or poor. It is found that wettability increases over $200^{\circ}C$ regardless of composition liquid fraction and phases of the original alloy Sn-7Ag alloy showed good wettability in their partial melting zone, while Sn-65Bi alloy was non-wettable under their melting points.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.791-797
• /
• 2002

This paper introduces the partial melting process for solder application and characterization of its feasibility using Sn-Ag, and Sn-Cu solder alloys. ill order to show that the liquid phase in the semi-liquid state maintains the similar wettability as single-phase liquid, the wetting balance tests are conducted with varying temperatures and compositions. Also, as a new soldering technology, the microstructural and mechanical test were investigated. The results from this research indicate that the partial melting can yield satisfactory sider joints as long as the liquid phase acquires sufficient chemical activity. At a condition where the partial melting is effective, a direct correlation between the wettability and the surface tension is found to exist.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.37 no.1
• /
• pp.39-47
• /
• 2021

Compared to conventional method, if metal framework of removable partial denture is fabricated by selective laser melting, various laboratory works are omitted, saving time and simplifying the process. In addition, metal framework with homogeneous density can be obtained, expecting excellent mechanical properties, especially resistance to fatigue fracture. In these cases, impression were taken using conventional methods in partial edentulous patients, master casts were fabricated and scanned to obtain digital data. After designing the metal frameworks on the scanned data, removable partial dentures were fabricated using selective laser melting methods. Through these procedure, satisfactory outcomes were achieved both in functional and esthetic aspects.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.63-68
• /
• 2000

This paper introduces the partial melting process for solder application and characterization of its possibility using off-eutectic Pb-Sn alloy. In order to show that the liquid phase in the semi-liquid state maintains the wettability as the single-phase liquid, the wetting balance test are conducted with varying temperatures and compositions. The results are then compared with the surface tension of liquid, both measured and calculated, to examine the correlation. The results from this investigation indicate that the partial melting can yield satisfactory solder joints as long as the liquid phase acquires sufficient chemical activity. At a condition where the partial melting is effective, a direct correlation between the wettability and the surface tension is found to exist. All alloys are found to show a reasonable wettability in semi-liquid state.

• Transactions on Electrical and Electronic Materials
• /
• v.3 no.2
• /
• pp.24-27
• /
• 2002

The NdBaCuO superconductor samples were zone-melted in low oxygen partial pressure (1%O$_2$+99%Ar). The zone-melting temperature was decreased about 12$0^{\circ}C$ film 1,06$0^{\circ}C$, the zone-melting temperature in air. Thus the loss of liquid phase (BaCuO$_2$ and CuO) was reduced during: the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased and, therefore, the substitution of Nd for Ba was occurred. The superconductivity of zone-melted Nd$_{1+x}$Ba$_{2-x}$Cu$_3$O$_{y}$ prepared under low oxygen partial pressure was distinctively improved.d.d.d.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.85-88
• /
• 2001

The NdBaCuO superconductor samples were Zone-melted in low oxygen partial pressure (1% $O_{2}+ 99% Ar$ ). The Zone-melting temperature was decreased about $120^{\circ}C$ from $1060^{\circ}C$ the zone-melting temperature in air. Thus the loss of liquid phase ($BaCuO_{2}$ and CuO) was reduced during the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased, so was the substitution of Nd for Ba. The superconductivity of zone-melted $Nd_{1+x}Ba_{2-x}Cu_{3}O_{y}$ prepared under low oxygen partial pressure was distinctively improved.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.85-88
• /
• 2001

The NdBaCuO superconductor samples were Zone-melted in low oxygen partial pressure (1% O$_2$+99% Ar). The Zone-melting temperature was decreased about 120$^{\circ}C$ from 1060$^{\circ}C$ the zone-melting temperature in air. Thus the loss of liquid phase (BaCuO$_2$ and CuO) was reduced during the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased, so was the substitution of Nd for Ba. The superconductivity of zone-melted Nd$\sub$1+x/Ba$\sub$2-x/Cu$_3$O$\sub$y/ prepared under low oxygen partial pressure was distinctively improved.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.11a
• /
• pp.263-266
• /
• 2003

The fine $YBa_2Cu_3O_x$ powder ($0.2{\sim}1.0\;{\mu}m$) is produced by sol-gel method, and electrophoresis deposition is used for the preparation of $YBa_2Cu_3O_x$ thick films which are deposited on Ag wire. The oriented $YBa_2Cu_3O_x$ was tried to be prepared by the zone-melting method under low oxygen partial pressure. The orientation and the phase composition were examined by the X-ray diffraction and the superconductivities were measured by 4 line method. The critical current densities are still quite low, which may be due to unsuitable technical parameters for zone-melting of $YBa_2Cu_3O_x$ thick films. Therefore the heat treatment condition and controlling of low oxygen partial pressure should be improved in the future experiment.

• 한국초전도학회:학술대회논문집
• /
• 2007.07a
• /
• pp.68-68
• /
• 2007

• Progress in Superconductivity
• /
• v.10 no.2
• /
• pp.103-107
• /
• 2009

$Bi_2Sr_2Ca_1Cu_2O_x$(BSCCO 2212) superconductors for current lead were fabricated by centrifugal melting process(CMP). BSCCO 2212 powder was melted at $1200^{\circ}\C$ in a resistance furnace using a Pt crucible and poured in a rotating cylindrical mold preheated at $550^{\circ}\C$ for 2 hour. The solidified BSCCO-2212 samples were heat-treated by partial melting process in oxygen atmosphere. The current-voltage curves at 77 K of the samples were obtained by transport measurement, and the microstructure was investigated by scanning electron microscope. The $J_c$ values at 77 K of the tubes partially melted at $840^{\circ}C,\;860^{\circ}C\;and\;880^{\circ}C$ were 492, 430 and 398 $A/cm^2$, respectively. It was observed that the plate-like grains in BSCCO 2212 tube was more developed in the sample heat-treated at $840^{\circ}C$. It was found that the critical current of the BSCCO 2212 samples was dependent on the partial melting schedule regarding the grain shape and size of the BSCCO 2212.