• 공업화학
• /
• 제3권4호
• /
• pp.627-638
• /
• 1992

분자량과 관능기수가 각각 다른 4가지의 polypropylene glycol(PPG)과 toluene-2, 4-diisocyanate(2, 4-TDI)를 이용하여 polyurethane prepolymer(NCO terminated)를 합성한 후 NCO기 말단에 2-hydroxyethyl methacrylate(2-HEMA)를 반응시켜 PPG계 polyurethane methacrylates 수지를, PPG대신에 bisphenol A(BPA)를 이용하여 BPA계 polyurethane dimethacrylate 수지를 합성하였다. 합성된 PPG계 polyurethane dimethacrylate 수지에 반응성희석제인 triethylene glycol dimethacrylate(TEGDMA), 중합개시제인 cumene hydroperoxide(CHP) 중합금지제인 hydroquinone(HQ)를 첨가하였을 때, 첨가량변화에 따른 토오크강도의 변화를 고찰하였고, BPA계 polyurethane dimethacrylate 수지와 블렌드하였을때의 조성비에 따른 토오크강도의 변화를 고찰하였다. 토오크 측정결과, TEGDMA 40wt%, cumene hydroperoxide 4wt%, hydroquinone 200 ppm이 첨가되었을 때, 가장 큰 토오크강도를 나타내었으며, PPG계와 BPA계를 블렌딩하였을 때는 PPG/BPA가 4/6일 때 가장 큰 토오크강도를 나타내었다. 반응성희석제인 triethylene glycol dimethacrylate(TEGDMA), 중합개시제인 cume hydroperoxide(CHP), 중합금지제인 hydroquinone(HQ)를 동일하게 첨가한 후, 분자량과 관능기수가 다른 PPG계 polyurethane dimethacrylate 수지들의 열경화시의 토오크강도를 측정한 결과, 관능기수가 같은 수지들(PD750, PD1000, PD2000)의 경우에는 분자량이 적은 수지(PD750)일수록 큰 토오크강도를 나타내었고, 관능기수가 많을수록(PT 700) 큰 토오크강도를 나타내었다. 개시제만을 첨가한 후, 열경화를 통해서 얻어진 PPG계 수지들의 겔들을 DSC분석을 통해서 Tg변화를 측정하여 본 결과, 경화시 분자량이 가장 적고, 관능기수가 가장 많은 PT 700이 가장 큰 폭의 Tg증가를 나타내었으며, 분자량이 가장 큰 수지인 PD 2000이 가장 적은 폭의 Tg증가를 나타내었다. 그리고, Tg를 통해서 가교점간 분자량 Mc를 측정한 결과, 가장 큰 폭의 Tg를 보인 PT 700가 가장 적은 Mc를 가지고 있었다. 따라서, PT 700이 경화시 가장 조밀한 망목구조를 형성한다는 것을 확인할 수 있었다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2005년도 춘계학술발표대회 논문집
• /
• pp.226-230
• /
• 2005

본 논문에서는 MWCNT 분산도가 증가된 새로운 전도성 형상 기억 폴리우레탄을 연구하였고 전기적 특성을 검출하기 위한 실험과 작동 성능을 측정하기 위한 실험들을 수행하였다. 전이온도 이하 범위에서의 온도변화에 따른 저항변화는 거의 없었으며, 시편이 100% 신장됨에 따라 저항값도 100% 증가하였다 (비저항 300% 증가). 작동변위는 페이로드가 증가함에 따라 선형적으로 줄어들었다. 그리고, CSMPU 작동기의 보다 세부적인 특성 및 성능을 알기 위해서는 더 많은 연구와 실험이 필요하다.

• 한국염색가공학회지
• /
• 제30권2호
• /
• pp.90-97
• /
• 2018

Hydrophilic reactive hot-melt polyurethane adhesive(HRHA) using a hydrophilic polyol having different molecular weight and NCO index was synthesized. This HRHA was synthesized using Polyethylene glycol(PEG) as a hydrophilic polyol, Polypropylene glycol(PPG) and Polycaprolactone diol(PCL) as hydrophobic polyols, and Methylene diphenyl diisocyanate(MDI) as an isocyanate. The changes in IR spectrum, viscosity and thermal properties of HRHA with different PEG molecular weights and NCO index were investigated, and the tensile strength and elongation of the HRHA casting film and the peel strength, moisture permeability and water pressure of the HRHA coated fabric were confirmed. In this experiment, as the molecular weight of PEG and NCO index increased, the adhesive strength, tensile strength, elongation and moisture permeability was increased but viscosity and Tg was decreased.

• Korean Chemical Engineering Research
• /
• 제50권4호
• /
• pp.639-645
• /
• 2012

Isophorone diisocyanate, polycarbonate diol, dimethylol propionic acid를 출발물질로 하여 제조된 폴리우레탄 prepolymer의 미반응 NCO 기를 실란커플링제인 aminopropyl trietoxysilane (APS)로 capping시켜 수분산 폴리우레탄(waterborne polyurethane dispersion, PUD)을 합성하였다. 그 후 이 PUD에 아크릴 단량체인 2-hydroxyethyl methacrylate와 methyl methacrylate의 혼합물을 첨가하고 중합시켜 silylated acrylic polyurethane dispersion을 제조하였다. 동적 빛 산란법에 의해 측정된 silylated acrylic polyurethane dispersion의 평균 직경은 APS 첨가량이 증가됨에 따라 39.0 nm에서 399.8 nm로 크게 증가하였다. 또한 코팅 도막의 연필경도는 APS의 첨가량이 증가되면서 B에서 F로 향상되었다.

• Archives of Plastic Surgery
• /
• 제42권2호
• /
• pp.186-193
• /
• 2015

Background Polyurethane coating of breast implants has been shown to reduce capsular contracture in short-term follow-up studies. This 30-year study is the longest examination of the use of polyurethane-coated implants and their correlation with capsular contracture. Methods This study evaluates the senior surgeon's (F.D.P.) experience with the use of polyurethane-coated implants in aesthetic breast augmentation in 382 patients over 30 years. Follow-up evaluations were conducted for six months after surgery. After the six-month follow-up period, 76 patients returned for reoperation. The gross findings, histology, and associated capsular contracture were noted at the time of explantation. Results No patient during the six-month follow-up period demonstrated capsular contracture. For those who underwent reoperation for capsular contracture, Baker II/III contractures were noted nine to 10 years after surgery and Baker IV contractures were noted 12 to 21 years after surgery. None of the explanted implants had macroscopic evidence of polyurethane, which was only found during the first five years after surgery. The microscopic presence of polyurethane was noted in all capsules up to 30 years after the original operation. Conclusions An inverse correlation was found between the amount of polyurethane coating on the implant and the occurrence of capsular contracture. Increasingly severe capsular contracture was associated with a decreased amount of polyurethane coating on the surface of the implants. No contracture occurred in patients whose implants showed incomplete biodegradation of polyurethane, as indicated by the visible presence of polyurethane coating. We recommend research to find a non-toxic, non-biodegradable synthetic material as an alternative to polyurethane.

• 한국염색가공학회지
• /
• 제28권1호
• /
• pp.40-47
• /
• 2016

As a coating material for loudspeaker dampers, resilient polyurethane/epoxy hybrid resins were synthesized to replace conventional phenol resin and examined the physical properties, which are not only environmentally friendly but also not harmful to human. Five types of polyurethane resins were synthesized in the step-shot method using methylene diisocyanate, three polyols such as poly tetramethylene ether glycol(PTMEG, MW:2000), poly(1,4-buthylene adipate(PBAP, MW:2000), and poly carbonatediol(PCD, MW:2000), and three chain extenders such as ethylene glycol(EG), neopentyl glycol(NPG), and 1,4-buthandiol(1,4-BD). The five types of synthesized polyurethane resins and commercially available bisphenol A type epoxy resin were blended in weight ratios of 90:10, 70:30, and 50:50 to synthesize 15 types of polyurethane/epoxy hybrid resins. Among the polyurethane resins, the one that was synthesized using PCD and 1,4-BD showed excellent tensile strength, 100% modulus, low extension, and relatively high viscosity. Polyurethane/epoxy hybrid resins with higher epoxy resin contents showed better thermal properties and water resistance while those with higher polyurethane contents showed higher flexibility. The polyurethane/epoxy hybrid resin made by blending the polyurethane based on PCD and 1,4-BD with a bisphenol A type epoxy resin in a weight ratio of 70:30 was identified to be the most suitable to be used in speaker dampers.

• 한국건설순환자원학회논문집
• /
• 제8권3호
• /
• pp.263-268
• /
• 2020

이 연구의 목적은 폐타이어 고무분말을 혼입한 폴리우레탄 복합재료와 굵은 골재를 사전채움하고 폴리우레탄을 주입한 폴리우레탄 복합재료의 감쇠성능을 평가하는 것이다. 이를 위하여 총 4 종류의 폴리우레탄 기반 복합재료를 제조하였고, 충격 가진 실험을 실시하였다. 실험을 통하여 시간 영역과 주파수 영역에서의 진동특성을 계측한 후 감쇠비를 계산하였다. 실험 결과, 고무분말을 혼입하여 폴리우레탄의 양이 각각 10.6%와 21.2% 줄어든 실험체들의 감쇠비는 순수한 폴리우레탄 실험체에 비하여 각각 8.4%와 4.6% 낮은 것으로 나타났다. 프리팩트 콘크리트 제조 방법과 유사한 방법으로 제조한 폴리우레탄 복합재료의 감쇠비는 순수 폴리우레탄에 비하여 22% 낮은 것으로 나타났지만 폴리우레탄 혼입량은 50% 감소하였으며, 강성은 25.7배 높은 것으로 나타났다.

• International Journal of Safety
• /
• 제1권1호
• /
• pp.47-51
• /
• 2002

This study was performed by measuring the minimum ignition temperature of polyurethane form recovered from the recycling process of the end-of-life home appliances. The critical ignition temperature of polyurethane form was lower as the size of the sample vessel was increased, and that of polyurethane form using cyclopentane as the forming agent was relatively lower than the polyurethane form using CFC and the combustion of cyclopentane-polyurethane form occurred fiercely. It is considered that the recycling process of end-of-life home appliances using cyclopentane-polyurethane form as the insulator would require a special fire and dust explosion prevention measures since there exists a high potential hazard of fire and dust explosion during crushing and storage processes.

• 한국의류학회지
• /
• 제21권8호
• /
• pp.1346-1352
• /
• 1997

The purpose of this study was to help the consumer as well as the producer by investigating the properties such as tensile strength, extention, tear strength, wrinkle recovery, drapability, bending property, moisture regain, and shrinkage on commercial polyurethane coated fabrics. Seven commercial polyurethane coated fabrics having various base fabrics were used. The performance properties of base fabrics and polyurethane coated fabrics were measured. The relationships between base fabrics and polyurethane coated fabrics on the performance properties were identified. It was concluded that the properties of polyurethane coated fabric mainly depend on the characteristics of base fabric. Therefore the proper use of base fabric is recommended in order to improve the performance of polyurethane coated fabric.

• 한국안전학회지
• /
• 제32권1호
• /
• pp.108-114
• /
• 2017

According to an increase in demand for polyurethane soft foam for thermally insulated containers, the purpose of this study is based on redefining existing rigid polyurethane foam insulation KS standard which has been limited to building material-based authentication techniques. Since there are arising concerns of consumer rights and safety due to humidifier fungicides and urethane track incidents, there are elements to be further researched on rigid polyurethane foam insulation for refregerated containers. Thus, we reviewed the prior standards for rigid polyurethane foam insulation and verified the validity of certification testing method for the new standard with self-foamed polyurethane.