• 한국염색가공학회지
• /
• 제27권2호
• /
• pp.126-131
• /
• 2015

Silica-polyurethane hybrid breathable films were prepared and their breathabilities were assessed. Appropriately aggregated silica was prepared through sol-gel reaction of water glass and its particle size ranged 360~500nm. The polyurethane dispersion was prepared by the reaction of isophorone diisocyanate(IPDI) as diisocyanate and polytetramethylene glycol(PTMG) and dimethylol propionic acid(DMPA) as polyol, particle size ranging 30~120nm. The reaction between isocyanate and hydroxyl group to form urethane bonding was checked by the intensity of the stretch peak of isocyanate at $2270cm^{-1}$ in the FT-IR. The silica was incorporated into polyurethane dispersion and casted into film. It was shown that the incorporated silica(1~5wt.%) increased water vapour permeability of the films by 30~100%, and decreased the hydrostatic pressure by 10~40%. From the results, it could be concluded that the appropriate hybridization of silica can increase the breathability of polyurethane dispersion film, while minimizing the loss of hydrostatic pressure.

• 한국산학기술학회논문지
• /
• 제13권3호
• /
• pp.955-960
• /
• 2012

본 연구는 순수 Polyurethane과 일반적인 난연제인 $Al(OH)_3$ 및 $Mg(OH)_2$를 첨가한 sample과 Cloisite Na+, Cloisite 15A를 첨가한 sample의 난연성 및 기계적 특성을 비교하였다. 또한 Sodium silicate와 Polyurethane을 혼합한 것에 경량성 충진제인 Vermiculite, Perlite를 충진한 sample의 난연성 및 기계적 특성을 확인하였다. 그 결과, Cloisite Na+와 Cloisite 15A를 첨가한 sample과 Sodium silicate를 혼합한 sample에서 난연제를 첨가한 것과 같은 등급의 난연성을 확인하였다. 인장강도는 filler의 양이 증가함에 따라 저하 되었으나, sodium silicate를 첨가한 sample의 경우 다른 sample 보다 강도가 향상됨을 확인하였다.

• Journal of Microbiology and Biotechnology
• /
• 제12권1호
• /
• pp.14-17
• /
• 2002

To increase the efficiency of a two-stage anaerobic wastewater digestion system, various polymers were added to the methanogenic reactor as supports. The addition of polyurethane addition (6%, w/v) to the methanogenic reactor facilitated the organic loading rate (2-day Hydraulic Retention Time), higher than that of the conventional methanogenic reactor (6-day HRT). During the operation of the polyurethane-added reactor, a significant decrease in the organic mass in the effluent (COD 5-6 kg/l) was achieved, compared to that of the conventional reactor (COD 15-20 kg/l). The methane gas production rate also improved about 3-fold in the polyurethane-added reactor. More biomass was found to accumulate in the polyurethane-liquid phase (volatile solid, 26-28kg) than in the free-liquid phase (volatile solid, 5- 7 kg/l) after 90 days of operation. A scaled-up experiment with a polyurethane-added 2.5-1 reactor confirmed the previous results, and no adverse effects such as plugging or channeling due to decreased efficiency was observed even after 4 months of operation.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2008년도 제30회 춘계학술대회논문집
• /
• pp.221-226
• /
• 2008

Hydroxy-terminated polyether의 새로운 합성방법인 양이온 개환 공중합에 의해서 Ethylene oxide와 Tetrahydrofuran을 공중합 하였다. 중합은 1,4-Butandiol 존재 하에 $BF_3$ THF를 촉매로 반응이 진행되어 잘 제어된 Polyetherdiol을 합성할 수 있었다. Polyurethane 반응은 Polyetherdiol과 경화제로써 I-PDI/N-100 혼합물을 사용하였고, 경화촉매로 TPB/MA 혼합물을 사용하여 합성하였다. 이렇게 합성된 Polyurethane은 현재 미국에서 시판중인 ATK HTPE를 이용한 Polyurethane과 기계적 특성과 경화 거동을 비교 분석하였다.

• Korean Chemical Engineering Research
• /
• 제48권4호
• /
• pp.434-439
• /
• 2010

Isophorone diisocyanate(IPDI), poly(tetramethyleneglycol)(PTMG), dimethylol propionic acid(DMPA)를 출발물질로 하여 NCO terminated prepolymer가 합성되었다. 이 prepolymer의 NCO기를 silane으로 capping하기 위해 0~0.02 mole로 첨가량이 조절된 aminopropyl triethoxysilane(APS)이 첨가되었다. 제조된 용액의 평균 입경은 APS의 첨가량이 증가함에 따라 증가하였다. 또한 제조된 코팅 필름의 연필 경도 및 열적안정성은 순수한 수분산 폴리우레탄보다 우수하였다.

• 한국의류학회지
• /
• 제25권2호
• /
• pp.350-357
• /
• 2001

In this study, seam strength, seam elongation and seam efficiency of polyurethane coated fabrics were examined under various sewing conditions using three kinds of fabrics, four kinds of sewing threads and three kinds of stitch lengths. And the sewability of polyurethane coated fabrics were evaluated by FAST system. The results were as follows: 1. Seam strength decreased with the increase of stitch length. The loop strength of sewing thread and the type of base fabric than the type of coated surface had an effect on seam strength. 2. Seam elongation also decreased with the increase of stitch length and was affected by the type of base fabric. The tensile elongation of polyurethans coated fabric had an effect on seam elongation. 3. Sean efficiency also was related to stitch length, the type of base fabric, and seam strength. The suitable seam efficiency was within 50%∼65% in which polyurethane coated fabric and sewing thread broke at the same time. Therefore PS thin and PPC thin sewing threads and 3mm stitch length were suitable to polyurethane coated fabrics. 4. The relaxation shrinkage(RS) of polyurethane coated fabric was smaller than the smallest value of control chart in FAST system. And the extensibility(E) and the shear rigidity(G) were larger than the largest value.

• 한국응용과학기술학회지
• /
• 제27권4호
• /
• pp.461-469
• /
• 2010

Polyurethane adhesive is used in various fields as flexible packaging materials including a food packaging field. Therefore, the purpose of this study is synthesis of polyurethane adhesive which uses aliphatic isocyanate, and compares with aromatic isocyanate. The isocyanates for this test are toluene-2,4-diisocyanate(TDI), hexamethylene diisocyanate(HDI), 4,4-dicyclohexyl ethane diisocyanate($H_{12}MDI$), and isophorone diisocyanate(IPDI). And, the effect of any other diisocyanate are evaluated by several methods as for curing rate test, accelerate weathering test, and peel strength test. The polyurethane adhesive using curing catalyst and HDI has adhesion strength of about 560 g/15 mm between aluminium foil and nylon, about 1,520 g/15 mm between nylon and CPP. Those parameters are similar to polyurethane adhesive with TDI. Also, in case of curing rate, those are similar to TDI type polyurethane adhesive. Moreover, data of ${\Delta}E$ as color variation by QUV tester is equal to 4.12, as 48% against those of TDI type.

• 한국염색가공학회지
• /
• 제32권3호
• /
• pp.121-127
• /
• 2020

The analysis method of relative adsorption of disperse dyes on impregnated polyurethane resin and polyester fiber separately was investigated. The solvents for extracting the dyes from polyurethane resin and polyester fiber were determined by acetone and DMF, respectively. By extracting the dyed fibers with acetone at room temperature within 30 minutes, the dyes adsorbed only on the polyurethane resin could be extracted. And then by additional extracting the same fabrics with DMF at 95℃ for longer than 1 hour, the dyes adsorbed on polyester fabrics was extracted. This means that the dyes adsorbed on polyurethane and polyester could be extracted separately and that relative adsorption of the dyes on the both components could be analyzed quantitatively. Using this analysis method, the relative adsorption of a disperse dye was investigated after reduction clearing with various conditions.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2008년도 제31회 추계학술대회논문집
• /
• pp.231-236
• /
• 2008

양이온 개환중합법을 이용하여 Epichlorohydrin(ECH)과 Tetrahydrofuran(THF)을 공중합 하였다. 중합은 1,4-Butandiol 존재 하에 $BF_3THF$를 촉매로 사용하여 잘 제어된 Copolyetherdiol을 합성하였다. 분자량은 [monomer]/[diol]비를 조절하였고, 공중합체 조성은 ECH와 THF의 투입몰비를 변화하여 조절하였다. 합성된 Copolyetherdiol의 Chlorine기는$S_N2$반응을 이용하여 Azide기로 치환하였다. 합성된 고분자를 프리폴리머로 사용하여 경화제인 N-100/IPDI와 경화촉매인 TPB/MA 혼합촉매를 이용하여 Polyurethane을 합성하여 경화거동과 기계적 특성은 비교 분석하였다.

• Elastomers and Composites
• /
• 제35권3호
• /
• pp.227-235
• /
• 2000

신발스크랩으로부터 발생되는 폐우레탄 발포체(waste urethane foam)와 폐우레탄(waste urethane scrap, $5{\sim}7mm$)의 재활용을 위하여 첫째, 양액재배용 배지의 구성 요소로 사용하여 장미 재배 적용가능성을 조사하였으며, 둘째, 폐우레탄으로부터 재생우레탄(Recycled Thermoplastic Polyurethane : RTPU)을 제조하여 RTPU와 HIPS(High Impact Polystyrene)를 블렌드한 후 이의 적용성을 확장하기 위하여 RTPU/HIPS 블렌드물에 amine계 발포제를 사용하여 발포체를 제조하였다. 양액재배용 배지의 구성요소로서 폐고무의 재활용에 있어서는 식물의 성장에 영향을 미치는 pH, 전기전도도, 생육 등을 조사하였으며, 폐우레탄 발포체의 물성은 TGA, DSC, FT-IR, SEM등을 이용하여 조사하였다. 본 연구는 폐우레탄 재활용 가능성의 다각화에 목적을 두었다.