• Textile Coloration and Finishing
• /
• v.27 no.2
• /
• pp.126-131
• /
• 2015

Silica-polyurethane hybrid breathable films were prepared and their breathabilities were assessed. Appropriately aggregated silica was prepared through sol-gel reaction of water glass and its particle size ranged 360~500nm. The polyurethane dispersion was prepared by the reaction of isophorone diisocyanate(IPDI) as diisocyanate and polytetramethylene glycol(PTMG) and dimethylol propionic acid(DMPA) as polyol, particle size ranging 30~120nm. The reaction between isocyanate and hydroxyl group to form urethane bonding was checked by the intensity of the stretch peak of isocyanate at $2270cm^{-1}$ in the FT-IR. The silica was incorporated into polyurethane dispersion and casted into film. It was shown that the incorporated silica(1~5wt.%) increased water vapour permeability of the films by 30~100%, and decreased the hydrostatic pressure by 10~40%. From the results, it could be concluded that the appropriate hybridization of silica can increase the breathability of polyurethane dispersion film, while minimizing the loss of hydrostatic pressure.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.13 no.3
• /
• pp.955-960
• /
• 2012

In this study, pure Polyurethane and commonly used flame retardants $Al(OH)_3$ and $Mg(OH)_2$, the add-in sample and Cloisite Na+, Cloisite 15A added sample of flammability and mechanical properties are compared. Sodium silicate and a mixture of polyurethane that the lightweight filler Vermiculite, Perlite addition of flame retardant and mechanical properties of the sample was confirmed. As a result, the flame retardant additive in the Vermiculite and Perlite in a flame-retardant grade sample except sample were identified. Tensile strength is degrade accord to the filler amount. But, Sodium silicate in the case of the sample add-in, other than confirmed that the sample strength increases.

• Journal of Microbiology and Biotechnology
• /
• v.12 no.1
• /
• pp.14-17
• /
• 2002

To increase the efficiency of a two-stage anaerobic wastewater digestion system, various polymers were added to the methanogenic reactor as supports. The addition of polyurethane addition (6%, w/v) to the methanogenic reactor facilitated the organic loading rate (2-day Hydraulic Retention Time), higher than that of the conventional methanogenic reactor (6-day HRT). During the operation of the polyurethane-added reactor, a significant decrease in the organic mass in the effluent (COD 5-6 kg/l) was achieved, compared to that of the conventional reactor (COD 15-20 kg/l). The methane gas production rate also improved about 3-fold in the polyurethane-added reactor. More biomass was found to accumulate in the polyurethane-liquid phase (volatile solid, 26-28kg) than in the free-liquid phase (volatile solid, 5- 7 kg/l) after 90 days of operation. A scaled-up experiment with a polyurethane-added 2.5-1 reactor confirmed the previous results, and no adverse effects such as plugging or channeling due to decreased efficiency was observed even after 4 months of operation.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2008.05a
• /
• pp.221-226
• /
• 2008

Novel synthetic routes were proposed for hydroxy-terminated Poly(EO-co-THF) by Cationic ring-opening copolymerization of Tetrahydrofuran(THF) and Ethylene oxide(EO). It was carried out using Boron trfluoride tetrahydrofuranate($BF_3$ THF complex) as catalyst in the presence of 1,4-butandiol. The resultant products are well-defined linear polyetherpolyol. Polyurethane(TPU) were prepared using resultant polyetherpolyol with IPDI/N-100 as curing agent and TPB(Triphenylbismuth) /MA(Maleic anhydride) mixture as cure catalyst. Mechanical properties of TPU prepared from poly(EO-co-THF) polyol were investigated and compared with polyurethane using ATK HTPE.

• Korean Chemical Engineering Research
• /
• v.48 no.4
• /
• pp.434-439
• /
• 2010

NCO terminated polyurethane prepolymers were synthesized from isophorone diisocyanate(IPDI), poly(tetramethyleneglycol)(PTMG) and dimethylol propionic acid(DMPA). Subsequently, aminosilane terminated prepolymers were prepared by capping the NCO groups of polyurethane prepolymers with different moles of aminopropyl triethoxysilane(0~0.02 mole) as a coupling agent. The average particle size of the silylated polyurethane solutions increased with increasing APS content. Also, the prepared coating films showed better thermal stability and pencil hardness than pure waterborne polyurethane.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.25 no.2
• /
• pp.350-357
• /
• 2001

In this study, seam strength, seam elongation and seam efficiency of polyurethane coated fabrics were examined under various sewing conditions using three kinds of fabrics, four kinds of sewing threads and three kinds of stitch lengths. And the sewability of polyurethane coated fabrics were evaluated by FAST system. The results were as follows: 1. Seam strength decreased with the increase of stitch length. The loop strength of sewing thread and the type of base fabric than the type of coated surface had an effect on seam strength. 2. Seam elongation also decreased with the increase of stitch length and was affected by the type of base fabric. The tensile elongation of polyurethans coated fabric had an effect on seam elongation. 3. Sean efficiency also was related to stitch length, the type of base fabric, and seam strength. The suitable seam efficiency was within 50%∼65% in which polyurethane coated fabric and sewing thread broke at the same time. Therefore PS thin and PPC thin sewing threads and 3mm stitch length were suitable to polyurethane coated fabrics. 4. The relaxation shrinkage(RS) of polyurethane coated fabric was smaller than the smallest value of control chart in FAST system. And the extensibility(E) and the shear rigidity(G) were larger than the largest value.

• Journal of the Korean Applied Science and Technology
• /
• v.27 no.4
• /
• pp.461-469
• /
• 2010

Polyurethane adhesive is used in various fields as flexible packaging materials including a food packaging field. Therefore, the purpose of this study is synthesis of polyurethane adhesive which uses aliphatic isocyanate, and compares with aromatic isocyanate. The isocyanates for this test are toluene-2,4-diisocyanate(TDI), hexamethylene diisocyanate(HDI), 4,4-dicyclohexyl ethane diisocyanate($H_{12}MDI$), and isophorone diisocyanate(IPDI). And, the effect of any other diisocyanate are evaluated by several methods as for curing rate test, accelerate weathering test, and peel strength test. The polyurethane adhesive using curing catalyst and HDI has adhesion strength of about 560 g/15 mm between aluminium foil and nylon, about 1,520 g/15 mm between nylon and CPP. Those parameters are similar to polyurethane adhesive with TDI. Also, in case of curing rate, those are similar to TDI type polyurethane adhesive. Moreover, data of ${\Delta}E$ as color variation by QUV tester is equal to 4.12, as 48% against those of TDI type.

• Textile Coloration and Finishing
• /
• v.32 no.3
• /
• pp.121-127
• /
• 2020

The analysis method of relative adsorption of disperse dyes on impregnated polyurethane resin and polyester fiber separately was investigated. The solvents for extracting the dyes from polyurethane resin and polyester fiber were determined by acetone and DMF, respectively. By extracting the dyed fibers with acetone at room temperature within 30 minutes, the dyes adsorbed only on the polyurethane resin could be extracted. And then by additional extracting the same fabrics with DMF at 95℃ for longer than 1 hour, the dyes adsorbed on polyester fabrics was extracted. This means that the dyes adsorbed on polyurethane and polyester could be extracted separately and that relative adsorption of the dyes on the both components could be analyzed quantitatively. Using this analysis method, the relative adsorption of a disperse dye was investigated after reduction clearing with various conditions.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2008.11a
• /
• pp.231-236
• /
• 2008

The well-defined copolymers derived from Epichlorohydrin(ECH), Tetrahydrofuran(THF) were synthesized by Cationic ring-opening polymerization(CROP) with 1,4-Butandiol, a initiator, and $BF_3THF$ Complex, a catalyst via Activated monomer mechanism, which could lead to hydroxyl-terminated polyethers. The molecular weight of polymers were dependant on the ratio of [monomer]/[diol], Copolymer structures were controlled by monomers feed ratio, ECH and THF added. This polymers were functionalized from Chlorine group to Azide group using $S_N2$ reaction. Synthesized polymers were found to be as the prepolymer for polyurethane. Polyurethane was synthesized in the presence of N-100/IPDI mixture, a curing agent, and TPB(triphenyl bismuth)/MA(Maleic anhydride) mixture, a catalyst system. The curing behavior and mechanical properties of polyurethane after mixing with various prepolymer’s composition and the molecular weight were studied.

• Elastomers and Composites
• /
• v.35 no.3
• /
• pp.227-235
• /
• 2000

This study focused on the recycling technology and application of waste polyurethane scrap($5{\sim}7mm$) and waste urethane form from the footware scrap. Firstly we suggest the waste polyurethane can be used as a component of medium for hydroponic rose culture. Secondly, recycled thermoplastic polyurethane(RTPU) was produced and blended it with high impact polystyrene(HIPS). And also, in order to extend application of recycling field, the former was produced with adding the amine foaming agent to RTPU/HIPS alloy. The main purpose of this study is to diverse of the recycling of the waste polyurethane.