• 한국염색가공학회지
• /
• 제16권3호
• /
• pp.31-38
• /
• 2004

Polyester fabrics, which is a major product in Daegu and Kyungbuk district, recently have a frequent warp streak phenomenon of sizing textiles for peach skin. So, this paper intensively focuses on the analysis of finding causes of poor products which may be produced in the process of sizing. Depending on the changes of sizing yarn's physical characteristic varying on sizing conditions, results of the research are as followed. 1. Sizing add-on rate, following tension changes of originally supplied yarn in sizing, does not fluctuate until 30g sizing tension, but marks high on the increase of sizing speed. 2. Sizing add-on amount increases approximately by 2.5% when interlacing pressure is raised from 1.5kg/$cm^2$ to 3.5kg/$cm^2$ at $130^{\circ}C$ sizing temperature. 3. Following the increase of sizing tension from 10g to 50g, boiling shrinkage rate of desizing yarn changes approximately from 7% to 11%. But the more sizing temperature and speed increases, the bigger the change rate becomes. 4. The thermal stress of desizing yarn is sensitively influenced by sizing tension in the sizing degree of above $130^{\circ}C$. 5. The deviation rate of sizing yarn's initial modulus value, which is influenced by air pressure in interlacing raw yarn, marks the highest at 40g and 50g strength.

• 펄프종이기술
• /
• 제37권5호통권113호
• /
• pp.1-7
• /
• 2005

The objective of this work was to investigate the effect of spreading behavior of the sizing agents (AKD or dialkyl ketone) on the sizing development of AKD-sized paper. There was a direct relationship between the spreading behavior of the sizing agents and their melting points. Both AKD and dialkyl ketone showed no substantial spreading until the temperature reaches to their melting points. Consequently, dialkyl ketone did not provide sizing development when the paper was heat-treated below $75^{\circ}C$, while AKD provided sizing effect even the paper heated at $50^{\circ}C$. The ketone, however, provided rather higher sizing effect than that of AKD, when the paper was heat-treated over $100^{\circ}C$. This result means that the ketone also gives sizing development to paper, moreover the ketone could give higher sizing effect to paper than AKD when it was melted and well spreaded on the fiber surface. While the ketone introduced to papers from hydrolyzed AKD emulsion could not contribute to sizing development.

• 한국염색가공학회지
• /
• 제20권3호
• /
• pp.1-7
• /
• 2008

Three kinds of 135D/108F ITY were produced from raw yam 85D/72F + SDY 50D/36F with. interlacing pressure $1.5kg/cm^2$, $2.5kg/cm^2$, $3.5kg/cm^2$ respectively. 72 kinds of sized yams were manufactured from three ITYs by altering sizing speed, sizing temperature and sizing tension. The mechanical characteristics of 72 kinds of plain fabrics which were woven using the sized yam as a warp were analyzed after scouring. The initial modulus of scoured fabric responded sensitively to the sizing speed in high tension. The WT of scoured fabric recorded the. highest1n the conditions of sizing tension 30g, and air pressure $2.5kg/cm^2$ in interlacing treatment. When sizing temperature was high, the WT value appeared low, but when sizing speed was high, the WT value was much affected by air pressure in interlacing raw yam. The MIU value of fabric according to sizing tension variations increased up to sizing tension 40g, but decreased above it. The bulk density decreased up to sizing tension 30-40g, but increased above it. In addition, the bulk density decreased as sizing temperature increased.

• 펄프종이기술
• /
• 제38권2호
• /
• pp.9-15
• /
• 2006

Neutral sizing is required for linerboard to solve the troubles in strength and process caused by recycled raw materials. AKD sizing efficiency can be influenced by process condition like white water quality, fines retention and so on. Therefore, this study was aimed to evaluate sizing performance of general and fast cure type AKDs using process water obtained from linerboard mill. To evaluate effect of process water quality on AKD sizing, white water was diluted with tap water at the different dilution ratios and UKP slurry was sized using the prepared water. Also, effects of inorganic and organic ion material on sizing were examined. When white water was used for stock forming, UKP sheet showed very low sizing degree. Sizing degree of sheet was increased with increase of dilution ratio because water quality was improved. Especially anionic organic material had a greater influence on AKD sizing than inorganic material. When white water quality was deteriorated, fast cure type AKD showed superior sizing performance to general type AKD.

• 펄프종이기술
• /
• 제42권2호
• /
• pp.95-101
• /
• 2010

For the development of higher-sizing performance of paper, a sizing agent using recycled PET was synthesised. Polyester resin was extracted from wasted PET by subcritical hydrolysis and finally modified to synthetic sizing agent by mixing water-disperse PET with triphenyl phosphite(TPP). The modified PET was considered as an internal sizing agent in different wet-end papermaking conditions. The optimum condition in sizing efficiency was obtained in initial pH of 6.5 in case of rosin+alum system, and 7.5 in case of rosin+alum+PET system, respectively, and in addition amount of PET 3%. The sizing efficiency was also closely related according to the fiber properties of wet-end slurry, such as virgin fibres from UKP and recycled fibres from KOCC. The application of modified PET was good in strength improvement of paper, specially in tensile strength.

• 폴리머
• /
• 제25권2호
• /
• pp.293-301
• /
• 2001

새로운 복합재료 제조 기술인 electron-ion technology (EIT)를 이용하여 전도성 탄소섬유/고밀도 폴리에틸렌 (CF/HDPE) 복합필름을 제조하고 탄소섬유 에폭시 sizing이 제조된 필름의 체적비저항과 인장강도 그리고 계면 특성에 미치는 영향에 대하여 연구하였다. 에폭시 sizing은 tunneling 효과를 좋게 해서 복합재료 필름의 전도성을 향상시키는 반면, 극성인 에폭시 sizing은 무극성인 폴리에틸렌과의 친화성이 없어서 탄소섬유와 폴리에틸렌간의 계면결합력을 감소시키므로 에폭시 sized 탄소섬유(CF(S))는 unsized 탄소섬유(CF(U))에 비하여 필름의 체적비저항과 인장강도를 감소시켰다. 에폭시 sizing은 탄소섬유의 nucleating efficiency를 떨어뜨려서 CF(S)/HDPE 필름이 CF(U)/HDPE 필름보다 불규칙적이고 덜 발달된 transcrystalline layer를 형성함을 관찰할 수 있었다.

• 펄프종이기술
• /
• 제38권1호통권113호
• /
• pp.1-8
• /
• 2006

To overcome troubles in strength and process of linerboard caused by raw materials, a neutral sizing which is usual in fine paper making can be considered. A new sizing agent is necessary to show good performance in a system with high conductivity and COD. In this study, fast cure type AKD was examined as a new sizing agent and compared with conventional AKD. The effects of fixing agent addition and drying condition were also investigated. Fast cure type AKD which has a higher cationicity showed better sizing degree than conventional AKD in spite of low addition level and no curing treatment. And when fixing agent of sufficient amount was added, sizing degree was improved for both AKDs. High cationicity is a crucial factor for neutral sizing of linerboard for obtaining fast and stable sizing degree. Drying with temperature over $100^{\circ}$ was desirable for developing sizing degree.

• 펄프종이기술
• /
• 제37권2호
• /
• pp.11-20
• /
• 2005

This study was carried out to investigate the influence of paper stock type and heat treatment on sizing effect. Various types of pulps were used to make handsheets sized internally with AKD(alkyl ketene dimer) and externally with CMC(carboxyl methyl cellulose). Most of the handsheets were treated with heat by dry oven $(100^{\circ}C,\;30min)$ to evaluate the effect of heat treatment on sizing development. Internal sizing development of newsprint was very bad, but the effect of heat treatment was much higher than those of NBKP, BCTMP. In case of surface sizing, newsprint was more effective compared to the other pulps. Considering above mentioned results, it seems that internal sizing slows down water into paper by molecular diffusion much more than capillary penetration, but surface sizing slows down capillary penetration. With regard to density, a higher thickness sheets showed high heat treatment effect on sizing, therefore it assumed that heat treatment effect on sizing had very close relationship with sheet density.

• 펄프종이기술
• /
• 제34권1호
• /
• pp.1-6
• /
• 2002

Alkaline sizing characteristics of TMP (thermomechanical pulp) handsheets with AKD (alkylketene dimer) were studied under various conditions. The sizing degree of TMP handsheet was much lower than that of chemical pulp. Especially, the sized TMP handsheet dried at $20^{\circ}C$ showed no sizing features, but sizing degree of TMP handsheet was clearly Increased by heat treatment at $105^{\circ}C$. The sizing effect of TMP was also improved by addition of $CaCO_3$, but it was not affected by pH. Therefore, sizing effect of TMP with AKD can be improved to some extent by controlling stock condition and heat treatment of handsheet.

• Journal of Welding and Joining
• /
• 제13권4호
• /
• pp.132-146
• /
• 1995

Flaw classification(determination of the flaw type) and flaw sizing (prediction of the flaw shape, orientation and sizing parameters) are very important issues in ultrasonic nondestructive evaluation of weldments. In this work, new techniques for both classification and sizing of flaws in weldments are described together with extensive review of previous works on both topics. In the area of flaw classification, a methodology is developed which can solve classification problems using probabilistic neural networks, and in the area of flaw sizing, a time-of-flight equivalent(TOFE) sizing method is presented.