• Journal of Powder Materials
• /
• v.24 no.5
• /
• pp.395-399
• /
• 2017

Solder paste is widely used as a conductive adhesive in the electronics industry. In this paper, nano and microsized mixed lead-free solder powder (Sn-Ag-Cu) is used to manufacture solder paste. The purpose of this paper is to improve the storage stability using different types of solvents that are used in fabricating the solder paste. If a solvent of sole acetate is used, the nano sized solder powder and organic acid react and form a Sn-Ag-Cu malonate. These formed malonates create fatty acid soaps. The fatty acid soaps absorb the solvents and while the viscosity of the solder paste rises, the storage stability and reliability decrease. When ethylene glycol, a dihydric alcohol, is used the fatty acid soaps and ethylene glycol react, preventing the further creation of the fatty acid soaps. The prevention of gelation results in an improvement in the solder paste storage ability.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.74-74
• /
• 2009

카본나노튜브(CNT) 복합체는 우수한 기계적 성질을 가지고 있어 다양한 분야에서 연구되고 있다. 본 연구에서는 카본나노튜브(CNT)를 간단한 볼밀공정을 사용하여 Sn3.5Ag solder ball과 SAC305 powder 표면에 혼합하고 이를 통해 접합부 특성을 관찰하였다. 볼밀을 실시하기 전 카본나노튜브(CNT)는 초음파을 이용하여 분산을 실시하였다. Sn3.5Ag solder ball의 직경은 450um이고 SAC305 powder의 직경은 약 30um이었으며 이때 사용한 볼밀볼의 직경은 각각 3mm, 1mm이다. 볼밀 회전속도는 약 300rpm이고 6, 12, 18, 24시간동안 볼밀을 실시하였다. 24시간 볼밀 후에도 solder ball과 solder powder의 모양은 크게 변하지 않았다. SEM을 통해 표면을 관찰한 결과 분산된 카본나노튜브(CNT)는 solder ball과 solder powder의 표면에서 관찰되었다. 카본나노튜브(CNT)가 삽입된 solder ball은 BGA coupon 위에 놓고 Reflow를 실시하여 접합하였고 solder powder은 flux를 첨가하여 paste로 제조하여 2012 chip에 대한 접합특성을 관찰하였다. 카본나노튜브(CNT)는 solder ball 내부의 표면근처에서 관찰되었으며 카본나노튜브(CNT)가 혼합된 solder ball은 Aging 실시 후에 IMC 두께가 카본나노튜브(CNT)가 혼합되지 않은 solder ball에 비해 두께가 작고 접합강도는 약 10% 증가하였다. 또한 카본나노튜브(CNT)가 혼합된 solder paste와 카본나노튜브(CNT)가 혼합되지 않은 solder paste를 비교한 결과 인쇄성은 모두 양호하였으며 카본나노튜브(CNT)가 혼합된 paste를 사용한 chip의 전단강도가 높게 나타났다.

• ETRI Journal
• /
• v.32 no.3
• /
• pp.414-421
• /
• 2010

The interconnection mechanisms of a smart anisotropic conductive adhesive (ACA) during processing have been characterized. For an understanding of chemorheological mechanisms between the fluxing polymer and solder powder, a thermal analysis as well as solder wetting and coalescence experiments were conducted. The compatibility between the viscosity of the fluxing polymer and melting temperature of solder was characterized to optimize the processing cycle. A fluxing agent was also used to remove the oxide layer performed on the surface of the solder. Based on these chemorheological phenomena of the fluxing polymer and solder, an optimum polymer system and its processing cycle were designed for high performance and reliability in an electrical interconnection system. In the present research, a bonding mechanism of the smart ACA with a polymer spacer ball to control the gap between both substrates is newly proposed and investigated. The solder powder was used as a conductive material instead of polymer-based spherical conductive particles in a conventional anisotropic conductive film.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1207-1208
• /
• 2006

We developed the copper core ball electroplated with Sn-Ag-Cu of the eutectic composition which used mostly as Pb free solder ball with high reliability. In order to search for the practicality of this developed copper core ball, the evaluation was executed by measuring the initial joint strength of the sample mounted on the substrate and reflowed and by measuring the joint strength of the sample after the high temperature leaving test and the constant temperature and the humidity leaving test. This evaluation was compered with those of the usual other copper core balls electroplated with (Sn,Sn-Ag,Sn-Cu,Sn-Bi) and the Sn-Ag-Cu solder ball.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.4
• /
• pp.65-68
• /
• 2013

A novel bumping process using solder bump maker (SBM) is developed for fine-pitch flip chip bonding. It features maskless screen printing process. A selective solder bumping mechanism without the mask is based on the material design of SBM. Maskless screen printing process can implement easily a fine-pitch, low-cost, and lead-free solder-on-pad (SoP) technology. Its another advantage is ternary or quaternary lead-free SoP can be formed easily. The process includes two main steps: one is the thermally activated aggregation of solder powder on the metal pads on a substrate and the other is the reflow of the deposited powder on the pads. Only a small quantity of solder powder adjacent to the pads can join the first step, so a quite uniform SoP array on the substrate can be easily obtained regardless of the pad configurations. Through this process, an SoP array on an organic substrate with a pitch of 130 ${\mu}m$ is, successfully, formed.

• ETRI Journal
• /
• v.32 no.2
• /
• pp.342-344
• /
• 2010

A novel, maskless, low-volume bumping material, called solder bump maker, which is composed of a resin and low-melting-point solder powder, has been developed. The resin features no distinct chemical reactions preventing the rheological coalescence of the solder, a deoxidation of the oxide layer on the solder powder for wetting on the pad at the solder melting point, and no major weight loss caused by out-gassing. With these characteristics, the solder was successfully wetted onto a metal pad and formed a uniform solder bump array with pitches of 120 ${\mu}m$ and 150 ${\mu}m$.

• ETRI Journal
• /
• v.35 no.6
• /
• pp.1152-1155
• /
• 2013

A cost-effective and simple solder on pad (SoP) process is proposed for a fine-pitch microbump interconnection. A novel solder bump maker (SBM) material is applied to form a 60-${\mu}m$ pitch SoP. SBM, which is composed of ternary Sn3.0Ag0.5Cu (SAC305) solder powder and a polymer resin, is a paste material used to perform a fine-pitch SoP through a screen printing method. By optimizing the volumetric ratio of the resin, deoxidizing agent, and SAC305 solder powder, the oxide layers on the solder powder and Cu pads are successfully removed during the bumping process without additional treatment or equipment. Test vehicles with a daisy chain pattern are fabricated to develop the fine-pitch SoP process and evaluate the fine-pitch interconnection. The fabricated Si chip has 6,724 bumps with a 45-${\mu}m$ diameter and 60-${\mu}m$ pitch. The chip is flip chip bonded with a Si substrate using an underfill material with fluxing features. Using the fluxing underfill material is advantageous since it eliminates the flux cleaning process and capillary flow process of the underfill. The optimized bonding process is validated through an electrical characterization of the daisy chain pattern. This work is the first report on a successful operation of a fine-pitch SoP and microbump interconnection using a screen printing process.

• ETRI Journal
• /
• v.37 no.2
• /
• pp.387-394
• /
• 2015

A novel interconnection technology based on a 52InSn solder was developed for flexible display applications. The display industry is currently trying to develop a flexible display, and one of the crucial technologies for the implementation of a flexible display is to reduce the bonding process temperature to less than $150^{\circ}C$. InSn solder interconnection technology is proposed herein to reduce the electrical contact resistance and concurrently achieve a process temperature of less than $150^{\circ}C$. A solder bump maker (SBM) and fluxing underfill were developed for these purposes. SBM is a novel bumping material, and it is a mixture of a resin system and InSn solder powder. A maskless screen printing process was also developed using an SBM to reduce the cost of the bumping process. Fluxing underfill plays the role of a flux and an underfill concurrently to simplify the bonding process compared to a conventional flip-chip bonding using a capillary underfill material. Using an SBM and fluxing underfill, a $20{\mu}m$ pitch InSn solder SoP array on a glass substrate was successfully formed using a maskless screen printing process, and two glass substrates were bonded at $130^{\circ}C$.

• Journal of Sensor Science and Technology
• /
• v.22 no.2
• /
• pp.130-135
• /
• 2013

This study proposed a noble process to fabricate TSV (Through Silicon Via) structure which has lower cost, shorter production time, and more simple fabrication process than plating method. In order to produce the via holes, the Si wafer was etched by a DRIE (Deep Reactive Ion Etching) process. The via hole was $100{\mu}m$ in diameter and $400{\mu}m$ in depth. A dielectric layer of $SiO_2$ was formed by thermal oxidation on the front side wafer and via hole side wall. An adhesion layer of Ti and a seed layer of Au were deposited. Soldering process was applied to fill the via holes with solder paste and metal powder. When the solder paste was used as via hole metal line, sintering state and electrical properties were excellent. However, electrical connection was poor due to occurrence of many voids. In the case of metal powder, voids were reduced but sintering state and electrical properties were bad. We tried the via hole filling process by using mixing solder paste and metal powder. As a consequence, it was confirmed that mixing rate of solder paste (4) : metal powder (3) was excellent electrical characteristics.

• ETRI Journal
• /
• v.37 no.3
• /
• pp.523-532
• /
• 2015

Recently, we have witnessed the gradual miniaturization of electronic devices. In miniaturized devices, flip-chip bonding has become a necessity over other bonding methods. For the electrical connections in miniaturized devices, fine-pitch solder bumping has been widely studied. In this study, high-volume solder-on-pad (HV-SoP) technology was developed using a novel maskless printing method. For the new SoP process, we used a special material called a solder bump maker (SBM). Using an SBM, which consists of resin and solder powder, uniform bumps can easily be made without a mask. To optimize the height of solder bumps, various conditions such as the mask design, oxygen concentration, and processing method are controlled. In this study, a double printing method, which is a modification of a general single printing method, is suggested. The average, maximum, and minimum obtained heights of solder bumps are $28.3{\mu}m$, $31.7{\mu}m$, and $26.3{\mu}m$, respectively. It is expected that the HV-SoP process will reduce the costs for solder bumping and will be used for electrical interconnections in fine-pitch flip-chip bonding.