• Korean Journal of Materials Research
• /
• v.23 no.11
• /
• pp.613-619
• /
• 2013

$Cu_2ZnSn(S_x,Se_{1-x})_4$ (CZTSSe) thin films were prepared by sulfurization of evaporated precursor thin films. Precursor was prepared using evaporation method at room temperature. The sulfurization was carried out in a graphite box with S powder at different temperatures. The temperatures were varied in a four step process from $520^{\circ}C$ to $580^{\circ}C$. The effects of the sulfurization temperature on the micro-structural, morphological, and compositional properties of the CZTSSe thin films were investigated using X-ray diffraction (XRD), Raman spectra, field emission scanning electron microscopy (FE-SEM), and transmission electron microscopy (TEM). The XRD and Raman results showed that the sulfurized thin films had a single kesterite crystal CZTSSe. From the FE-SEM and TEM results, the $Mo(S_x,Se_{1-x})_2$ (MoSSe) interfacial layers of the sulfurized CZTS thin films were observed and their thickness was seen to increase with increasing sulfurization temperature. The microstructures of the CZTSSe thin films were strongly related to the sulfurization temperatures. The voids in the CZTSSe thin films increased with the increasing sulfurization temperature.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.99.1-99.1
• /
• 2010

Many efforts on the surface sulfurization of $Cu(InGa)Se_2$ (CIGS)thin films have been reported as techniques to improve CIGS solar cell performance. We have investigated the sulfurization technique using the sulfur vapor. The co-evaporated $Cu(In,Ga)Se_2$ tin film was used for sulfurization. A thin $Cu(In,Ga)(S,Se)_2$ layer was grown on the surface of the CIGS thin film after high-temperature annealing in sulfur vapor. The structural and compositional properties of the thin films were studied by XRD, EDS and AES analysis. The obtained results revealed that the surface modification technique is promising method to S incorporated into CIGS absorber.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.97-97
• /
• 2014

The properties of thin film solar cells based on electrodeposited $CuIn(Se,S)_2$ were investigated. The proposed solar cell fabrication method involves a single-step $CuInSe_2$ thin film electrodeposition followed by sulfurization in a tube furnace to form a $CuIn(Se,S)_2$ quaternary phase. A sulfurization temperature of $450-550^{\circ}C$ significantly affected the performance of the $CuIn(Se,S)_2$ thin film solar cell in addition to its composition, grain size and bandgap. Sulfur(S) substituted for selenium(Se) at increasing rates with higher sulfurization temperature, which resulted in an increase in overall band gap of the $CuIn(Se,S)_2$ thin film. The highest conversion efficiency of 3.12% under airmass(AM) 1.5 illumination was obtained from the $500^{\circ}C$-sulfurized solar cell. The highest External Quantum Efficiency(EQE) was also observed at the sulfurization temperature of $500^{\circ}C$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.675-675
• /
• 2013

CIGS thin films have received a great attention as a promising material for solar cells due to their high absorption coefficient, appropriate bandgap, long-term stability, and low cost production. CIGS thin films have been deposited by various methods such as co-evaporation, sputtering, spray pyrolysis and electro-deposition. In this study, Cu(In,Ga)Se2(CIGS) thin films were prepared using a single quaternary target by rf magnetron sputtering. The effect of sulfurization on the structural, compositional and electrical properties of the films was examined in order to develop the deposition process. An optimal sulfurization process will be selected for the preparation of CIGS thin films with good structural, optical and electrical properties by applying various sulfurization processes. In addition, the electrical properties of CIGS thin films were investigated by post-deposition annealing process. The carrier concentration of CIG(SSe) thin films after sulfurization was increased from $10^{14}cm^{-3}$ to $10^{16}cm^{-3}$ and the resistivity was increased from 10 ${\Omega}cm$ to $10^3$ ${\Omega}cm$. It is confirmed that CIG(SSe) thin films prepared at optimal deposition condition have similar atomic ratio to the target value after sulfurization.

• Current Photovoltaic Research
• /
• v.3 no.1
• /
• pp.27-31
• /
• 2015

It is known that sulfide at the $Cu(In,Ga)Se_2$ ($CIGSe_2$) surface plays a positive role in $CIGSe_2$ solar cells. We investigated the substitution of S with Se on the $CIGSe_2$ surface in S atmosphere. We observed that the sulfur content in the $CIGSe_2$ films changed according to sulfurization temperature and Cu/(In+Ga) ratio. The sulfur content in the $CIGSe_2$ films increased with increasing the annealing temperature and Cu/(In+Ga) ratio. Also Cu migration toward the surface increased at higher temperature. Since high Cu concentration at the $CIGSe_2$ surface is detrimental role, it is necessary to reduce the S annealing temperature as low as $200^{\circ}C$. The cell performance was improved at $200^{\circ}C$ sulfurization.

• Korean Journal of Materials Research
• /
• v.23 no.6
• /
• pp.304-308
• /
• 2013

The effect of a sputter deposition sequence of Cu, Zn, and Sn metal layers on the properties of $Cu_2ZnSnS_4$ (CZTS) was systematically studied for solar cell applications. The set of Cu/Sn/Zn/Cu multi metal films was deposited on a Mo/$SiO_2$/Si wafer using dc sputtering. CZTS films were prepared through a sulfurization process of the Cu/Sn/Zn/Cu metal layers at $500^{\circ}C$ in a $H_2S$ gas environment. $H_2S$ (0.1%) gas of 200 standard cubic centimeters per minute was supplied in the cold-wall sulfurization reactor. The metal film prepared by one-cycle deposition of Cu(360 nm)/Sn(400 nm)/Zn(400 nm)/Cu(440 nm) had a relatively rough surface due to a well-developed columnar structure growth. A dense and smooth metal surface was achieved for two- or three-cycle deposition of Cu/Sn/Zn/Cu, in which each metal layer thickness was decreased to 200 nm. Moreover, the three-cycle deposition sample showed the best CZTS kesterite structures after 5 hr sulfurization treatment. The two- and three-cycle Cu/Sn/Zn/Cu samples showed high-efficient photoluminescence (PL) spectra after a 3 hr sulfurization treatment, wheres the one-cycle sample yielded poor PL efficiency. The PL spectra of the three-cycle sample showed a broad peak in the range of 700-1000 nm, peaked at 870 nm (1.425 eV). This result is in good agreement with the reported bandgap energy of CZTS.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.11a
• /
• pp.305-305
• /
• 2007

• Korean Journal of Materials Research
• /
• v.32 no.10
• /
• pp.408-413
• /
• 2022

The oxygen evolution reaction (OER) is very sluggish compared to the hydrogen evolution reaction (HER). Considering this difference is essential when designing and developing a cost-effective and facile synthesis method for a catalyst that can effectively perform OER activity. The material should possess a high surface area and more active sites. Considering these points, in this work we successfully synthesized sheets of cobalt phosphate hydrate (CP) and sulphurated cobalt phosphate hydrate (CPS) material, using simple successive ionic layered adsorption and reaction (SILAR) methods followed by sulfurization. The CP and CPS electrodes exhibited overpotentials of 279 mV with a Tafel slope of 212 mV dec^-1 and 381 mV with a Tafel slope of 212 mV dec^-1, respectively. The superior performance after sulfurization is attributed to the intrinsic activity of the deposited well-aligned nanosheet structures, which provided a substantial number of electrochemically active surface sites, speeded electron transfer, and at the same time improved the diffusion of the electrolyte.

• Transactions on Electrical and Electronic Materials
• /
• v.11 no.2
• /
• pp.73-76
• /
• 2010

The copper indium disulfide ($CuInS_2$) thin film was manufactured using sputtering and thermal evaporation methods, and the annealing with sulfurization process was used in the vacuum chamber to the substrate temperature on the glass substrate, the annealing temperature and the composition ratio, and the characteristics thereof were investigated. The $CuInS_2$ thin film was manufactured by the sulfurization of a soda lime glass (SLG) Cu/In/S stacked [1] elemental layer deposited on a glass substrate by vacuum chamber annealing [2] with sulfurization for various times at a temperature of substrate temperature of $200^{\circ}C$. The structure and electrical properties of the film was measured in order to determine the optimum conditions for the growth of $CuInS_2$ ternary compound semiconductor $CuInS_2$ thin films with a non-stoichiometric composition. The physical properties of the thin film were investigated under various fabrication conditions [3,4], including the substrate temperature, annealing temperature and annealing time by X-ray diffraction (XRD), field Emission scanning electron microscope (FE-SEM), and Hall measurement systems. [5] The sputtering rate depending upon the DC/RF power was controlled so that the composition ratio of Cu versus In might be around 1:1, and the substrate temperature affecting the quality of the film was varied in the range of room temperature (RT) to $300^{\circ}C$ at intervals of $100^{\circ}C$, and the annealing temperature of the thin film was varied RT to $550^{\circ}C$ in intervals of $100^{\circ}C$.

• Bulletin of the Korean Chemical Society
• /
• v.25 no.11
• /
• pp.1692-1694
• /
• 2004