• Korean Journal of Materials Research
• /
• v.16 no.12
• /
• pp.719-724
• /
• 2006

Ultrafine mullite powder was prepared from aluminium-secbutoxide and tetraethyl orthosilicate(TEOS) in the molar $Al_2O_3/SiO_2$=3/2. Sol-gel method by partial hydrolysis technique, as it were, first, TEOS was partially hydrolysized and then mixed with Al-secbutoxide for complete hydrolysis was used. X-ray diffraction, infrared spectroscopy and transmission electron microscopy, etc. confirmed that the mullite powder prepared by this method is in the stoichiometric $Al_2O_3/SiO_2$ ratio. Al-Si spinel was formed at $980^{\circ}C$ and ultrafine mullite powder with about 20 nm particle size was obtained above $1,200^{\circ}C$. Also mullite powders calcined at $1,600^{\circ}C$ had a stoichiometric composition, $3Al_2O_3{\cdot}2SiO_2$ and the lattice constants of the mullite powders calcined above $1,200^{\circ}C$ were almost coincided with theoretical values.

• Korean Journal of Materials Research
• /
• v.11 no.9
• /
• pp.797-801
• /
• 2001

In this study, the solution combustion method was employed to synthesize stoichiometric mullite, and hence the attrition process was employed to prepare ultrafine mullite particles with nano size. The thermal decomposition behavior and partial pressure of equilibrium species of both oxidizer and fuel were considered during solution combustion process. The synthesized product was mullite phase with 40 nm crystalline size, and the alumina contents of the product by TEM/EDS quantity analysis was 3.12$\pm$04 mole. The result showed that the synthesized mullite was almost close to the it's stoichiometric composition. For attrition process, the dispersion behavior of the mullite suspension was controlled and was comminuted with the condition of 800 rpm for 4 hours using 0.3 mm zirconia ball media. As a result of comminution, the mean particle size was 80 nm.