Recently the usage of galvanealed steel sheet was increased in order to protect corrosion in automobile industry. So, the alternative of steel sheet was investigated in a point of formability. Generally it was known that uncoated steel sheet has better mechanical properties than coated steel sheet. But, contrary results were sometimes occurred in workplace. This reason is the effect of friction. In this study, the formability of steel sheet considering friction characteristics was investigated with tensile test, cup drawing test and finite element method.

• 한국표면공학회지
• /
• 제36권2호
• /
• pp.176-184
• /
• 2003

New lubricant film of organic and inorganic composite resin was developed to improve the press formability of galvannealed steel sheets (GA) for automotive body panels. The frictional coefficient of lubricant GA steel sheets is about 20% superior to that of uncoated GA. The current range of spot welding of lubricant GA is similar to that of the uncoated GA, but the burning trace of spot welding is inferior to that of the uncoated GA in the oiling condition. The alkaline degreasability of lubricant GA shows 100% in alkaline degreasing condition of automotive company. The size and shape of the phosphated coating layer are similar to those of the uncoated GA sheet. The powdering property of the lubricant GA gives rise to 20∼50% improved property compared with the uncoated GA sheet.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2006년도 춘계학술대회 논문집
• /
• pp.251-252
• /
• 2006

Tensile and anisotropy test were performed to evaluate the mechanical properties of coated and uncoated steel. These results were used to predict the deference of formability between two sheets. Cup-drawing test was performed to verify formability of two sheets. Also, Cup-drawing test could predict the coefficient of friction and the forming limit. Finite Element Method of cup-drawing was performed to assess the deference between two sheets considering frictional characteristics. This result was compared with the former results.

• 소성∙가공
• /
• 제31권1호
• /
• pp.17-22
• /
• 2022

Hot stamping is widely used to manufacture structural parts to satisfy requirements of eco-friendly vehicles. Recently, hot forming technology using uncoated steel sheet is being studied to reduce cost and solve patent problems. In particular, research is focused on process technology capable of suppressing the generation of an oxide layer. To evaluate the oxide layer in the hot stamping process, Gleeble testing machine can be used to evaluate the oxide layer by controlling the temperature history and the atmosphere condition. At this time, since cooling by gas injection is impossible to protect the oxide layer on the surface of a specimen, research on a method for securing a quenching speed through natural cooling is required. This paper proposes a specimen shape design method to secure a target quenching speed through natural cooling when evaluating the oxide layer of an un-coated boron steel sheet by Gleeble test. For the evaluation of the oxide layer of the un-coated steel sheet through the Gleeble test, dog-bone and rectangular type specimens were used. In consideration of the hot stamping process, the temperature control conditions for the Gleeble test were set and the quenching speed according to the specimen shape design was measured. Finally, the quenching speed sensitivity according to shape parameter was analyzed through regression analysis. A quenching speed prediction equation was then constructed according to the shape of the specimen. The constructed quenching speed prediction equation can be used as a specimen design guideline to secure a target quenching speed when evaluating the oxide layer of an un-coated boron steel sheet by the Gleeble test.

• 소성∙가공
• /
• 제32권3호
• /
• pp.160-165
• /
• 2023

As the supply of eco-friendly vehicles increases, the application rate of hot stamping components is rising to reduce vehicle weight and improve safety. Although Al-Si coated steel sheets are commonly used in hot stamping processes, their manufacturing costs are elevated due to process patents and royalties. Various hot stamping studies have been conducted to reduce these production costs. In this study, we derived a process control method for suppressing the oxide layer of hot stamping parts using uncoated boron steel sheets. Firstly, hat-shaped parts were hot stamped under atmospheric conditions to analyze the tendency of oxide layer formation by location. Then, the Gleeble system was used to observe oxide layer formation based on oxygen content under various atmospheric conditions. Finally, the oxide layer thickness was quantitatively measured using SEM images.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 춘계학술대회 논문집
• /
• pp.182-185
• /
• 2004

Based on the experimental observation, the mathematical friction model, which is an essential information for analyzing the forming process of sheet metal, is developed considering lubricant viscosity, surface roughness and hardness, punch corner radius, and punch speed. By comparing the punch load found by FEM with a proposed friction model with experimental measurement when the coated and uncoated steel sheets are formed in 2-D geometry in dry and lubricant conditions, the validity and accuracy of the developed friction model are demonstrated.

• 소성∙가공
• /
• 제13권5호
• /
• pp.461-465
• /
• 2004

Based on the experimental observation, the mathematical friction model, which is an essential information for analyzing the forming process of sheet metal, is developed considering lubricant viscosity, surface roughness and hardness, punch comer radius, and punch speed. By comparing the punch load found by FEM with a proposed friction model with experimental measurement when the coated and uncoated steel sheets are formed in 2-D geometry in dry and lubricant conditions, the validity and accuracy of the developed friction model are demonstrated.

• 소성∙가공
• /
• 제24권6호
• /
• pp.405-410
• /
• 2015

Sheet-forming of Mg alloys is conducted at elevated temperatures (250℃) due to the low formability at room temperature. The high-temperature process often gives rise to surface damage on the alloy (i.e. galling.) In the current study, the frictional characteristics of DLC coating slid against an AZ31 Mg alloy at various temperatures were investigated. The coating has been used widely for low-friction processes. Dry-sliding friction and galling characteristics of an AZ31 Mg alloy (disk), which slid against uncoated and a DLC-coated STD-61 steel (pin), were investigated using a reciprocating-sliding tribometer at room temperature and 250℃. To represent the real sliding phenomena during a sheet metal forming process, single-stroke tests were used (10mm stroke length) rather than a reciprocating long sliding-distance test. The DLC coating suppressed adhesion between the alloy and the tool steel at room temperature, and exhibited a low friction coefficient. However, during sliding at 250℃, severe adhesion occurred between the two surfaces, which resulted in a high friction coefficient and galling.

• 한국레이저가공학회지
• /
• 제4권3호
• /
• pp.30-39
• /
• 2001

This work was tamed out to apply a laser welding technique in joining between a Zn coated low carbon steel plate(SECC) and a free cutting carbon steel shaft(SUM24L) with or without W coating. Experiments were carried out and analysed by applying the FD(factorial design)method to obtain the optimum Laser welding condition. Optical microscopy, SEM, TEM and XRD analyses were performed in order to observe the microstructures in the fusion zone and the HAZ. Mechanical properties of the welded specimens were examined by microhardness test, tensile test and twist test. There was no flawed Zn in the fusion zone by EDS analysis. This means that during the welding process, Zn gas could be eliminated by appropriate shielding gas flow rate and butt welding gap. Ni coating itself did not influence on the tensile strength and hardness. However, twist bending strength and the weld depth of the Ni-coated free cutting carbon steel were lower as compared with those of the uncoated free cutting carbon steel. It was attributed to a lower absorbance of laser beam to the shin Ni surface. According to the results of the factorial design tests, the twist bending strength of welded specimens was primarily affected by pulse width, laser power, frequency and speed.