Microstructure and Properties of High Tc Superconductor fabricated by Hot Isostatic Pressing

열간정수압소결(HIP) 시킨 고온초전도체의 조직과 특성

$YBa_2Cu_3O_{7-x}$ oxide superconductors were fabricated by the hot isostatic pressing (HIP). It was shown that their structures were orthorombic and constited of a single (123) phase. While as-sintered compacts had many pores, they were remarkably reduced by Hiping. The on-set and off set temperature of (123) compound sintered at $950^{\circ}C$ in oxygen and hiping at $880^{\circ}C$ were the highest and it showed 0 resistance at $90^{\circ}K$. The critical current density ($J_c$) of the above superconductor was $27A/cm^2$ and it also showed a number of twin structures, which are typical of high $T_c$ superconductor. It seemed that the low current density may be due to the many pores of starting-sintered compacts.