$(1-x)(SrPb)(CaMg)TiO_3-xBi_2O_3{\cdot}3TiO_2$ 세라믹의 하전입자 거동에 관한 연구

A Study on the Behavior of Charged Particles of $(1-x)(SrPb)(CaMg)TiO_3-Bi_2O_3{\cdot}3TiO_2$ Ceramics

In this paper, the $(SrPb)(CaMg)TiO_3$-xBi_2O_3{\cdot}3TiO_2$ ceramics with paraelectric properties were fabricated by the mixed oxide method. In order to investigate the behavior of charged particles, the characteristics of electrical conduction and thermally stimulated current were measured respectively. As a result on characteristics of the electrical conduction, the leakage current was increased as measuring temperature was increased. At room temperature, the conduction current was divided into the three steps as a function of DC electric field. The first step was Ohmic region due to ionic conduction, below 15[kV/cm]. The second step was showed a saturation which seems to be related to a depolarizing field occuring in field-enforced ferroelectric phase, between 15[kV/cm] and 40[kV/cm]. The third step was attributed to Child's law related to spare charge which injected from electrode, above 40[kV/cm]. Thermally stimulated currents(TSC) spectra with various biasing fields exhibited three distinguished peaks that were denoted as ${\alpha}$, ${\alpha}'$ and ${\beta}$ peak, each of which appeared at nearby -30, 20 and 95[$^{\circ}C$] respectively. It is confirmed that the a peak was due to trap electron trapped in the grainboundary, and ${\alpha}'$ peak that was observed above only 1.5[kV/mm] was attributed to field-enforced ferroelectric polarization. The origin of ${\beta}$ peak was identified as ion migration which caused the degradation.