초록
Electrical properties and thermal annealing effects of $C_{22}$-quinolium(TCNQ) Langmuir-Blodgett(LB) films were studied. Typical current-voltage(I-V) characteristics along the perpendicular direction chow an anomalous behavior of breakdown near the electric-field strength of $10^{6}$V/cm. To see the thermal influence of the specimen, current was measured as a function of temperature(20∼$180^{\circ}C$). It shows that the current increases about 4 orders of magnitude near 60∼$70^{\circ}C$ and remains constant far a while up to ∼$150^{\circ}C$ and then suddenly drops. Such increase of current near 60∼$70^{\circ}C$ seems tn be related to a softness of alkyl chains. Besides the electrical measurements, UV/visible absorption(300∼800 nm) of the thermally annealed sample was measured to see the internal-structure change. It is found that there are four characteristic peaks. At 494 nm, the optical absorption of the thermally annealed specimen at $60^{\circ}C$ starts increase and stays almost constant upto∼ $140^{\circ}C$. And eventually it disappears above $180^{\circ}C$. After heat treatment of the specimen up to $150^{\circ}C$, Uv/visible absorption was measured while cooling.