초록
In this paper, xPb(Zn$\_$1/3/Nb$\_$2/3/)O$_3$-yPbTiO$_3$-zPbZrO$_3$-zPbZrO$_3$ (0.5wt%)MnO$_2$ ceramics were fabricated by the mixed oxide method sintered at 1250$^{\circ}C$ for 2[hrs] and then the dielectric and pyroelectric properties were investigated. In 0.10PZN-0.45PT-0.47PZ sample, dielectric constant was 829 and in the case of 01.5PZN-0.45PT-0.40PZ sample, pyroelectric current and pyroelectric coefficient were 0.95 x 10$\^$-7/ [A] and 7.6 x 10$\^$-1/ [C/$\textrm{cm}^2$$.$$^{\circ}C$]. Figure of merits of pyroelectric current and voltage and detectivity, in same sample, has shown good properties, that were 2.4 x 10$\^$-8/[C$.$cm/J], 5.5 x 10$\^$-11/[C$.$cm/J], 1.6 x 10$\^$-8/ [C$.$cm/J].