Degradation characteristics of Praseodymium-based ZnO Varistor

프라세오디윰계 산화아연 바리스터의 노화특성

Degradation characteristics of the Pr-based ZnO varistor with $Y_2O_3$content (0.0-4.0 mol!%j were investigated. It was appeared that the variation of the J-E characteristics in the reverse direction before and after the applied stress with increasing $Y_2O_3$ content was larger than that of the forward direction but the variation was extrernly small. For all varistor, the leakage current with the stress time during the applied stress somewhat increased initialy but afterthat was almost constant or slightly decreased. The overall varistor voltage and nonlinear coefficient were less than 5%. Especially, in the case of Pr-based ZnO varistor containing 2.0 mol% to 4.0 mol% $Y_2O_3$, the variation of breakdown voltage and nonlinear coefficient was less than 1% and 5%. respectively. As a result, they showed good stability.