$BCl_3/Cl_2$/Ar 고밀도 플라즈마에서 (Ba,Sr)$TiO_3$ 박막의 식각 특성에 관한 연구

The Characteristics of (Ba,Sr)$TiO_3$ Thin Films Etched With The high Density $BCl_3/Cl_2$/Ar Plasma

(Ba,Sr)$TiO_3$ thin films have attracted groat interest as new dielectric materials of capacitors for ultra-large-scale integrated dynamic random access memories (ULSI-DRAMs) such as 1 Gbit or 4 Gbit. In this study, inductively coupled $BCl_3/Cl_2$/Ar plasmas was used to etch (Ba,Sr)$TiO_3$ thin films. RF power/dc bias voltage = 600 W/-250 V and chamber pressure was 10 mTorr. The $Cl_2/(Cl_2+Ar)$ was fixed at 0.2, the (Ba,Sr)$TiO_3$ thin films were etched adding $BCl_3$. The highest (Ba,Sr)$TiO_3$ etch rate is 480$\AA/min$ at 10 % $BCl_3$ adding to $Cl_2$/Ar. The characteristics of the plasmas were estimated using optical emission spectroscopy (OES). The change of Cl, B radical density measured by OES as a function of $BCl_3$ percentage in $Cl_2$/Ar. The highest Cl radical density was shown at the addition of 10% $BCl_3$ to $Cl_2$/Ar. To study on the surface reaction of (Ba,Sr)$TiO_3$ thin films was investigated by XPS analysis. Ion enhancement etching is necessary to break Ba-O bond and to remove $BaCl_2$. There is a little chemical reaction between Sr and Cl, but Sr is removed by physical sputtering. There is a chemical reaction between Ti and Cl, and Tic14 is removed with ease. The cross-sectional of (Ba,Sr)$TiO_3$ thin film was investigated by scanning electron microscopy (SEM), the etch slope is about $65\;{\sim}\;70$.