Abstract
A silver indium sulfide $(AgInS_{2})$ epilayer was grown by the hot wall epitaxy method, which has not been reported in the literature. The grown $AgInS_{2}$ epilayer has found to be a chalcopyrite structure and evaluated to be high quality crystal. From the photocurrent measurement in the temperature range from 30 K to 300 K, the two peaks of A and B were only observed, whereas the three peaks of A, B, and C were seen in the PC spectrum of 10 K. These peaks are ascribed to the band-ta-band transition. The valence band splitting of $AgInS_{2}$ was investigated by means of the photocurrent measurement. The crystal field splitting, $\Delta_{cr}$, and the spin orbit splitting, $\Delta_{so.}$ have been obtained to be 0.150 eV and 0.009 eV at 10 K, respectively. And, the energy band gap at room temperature has been determined to be 1.868 eV. Also, the temperature dependence of the energy band gap, $E_{g}(T)$, was determined.
Hot wall epitaxy 방법을 이용하여 chalcopyrite 구조를 가진 고품질의 $AgInS_{2}$ 박막을 성장 하였다. 광전류 스펙트럼을 측정한 결과， 30K에서 300K까지는 단지 A 와 B 두개의 봉우리가 관측되었고 반면에 10K에서는 A,B,C 세 개의 봉우리가 관측되었다. 이때 이들 봉우리들은 band-to-band 전이에 기인하는 것으로 관측되었다. 광전류 측정으로부터 $AgInS_{2}$의 가전자대 갈라짐이 측정되었고 이로부터 10k에서 결정장에 의한 갈라짐 $D_{cr}$과 스핀궤도에 의한 갈라짐 $D_{so}$은 각각 0.150eV와 0.009eV로 관측되었다. 또한 에너지 밴드갭의 온도 의존성 $E_{g}(T)$에 대하여 연구하였고 성장된 $AgInS_{2}$ 박막의 에너지 밴드갭은 1.868eV 임을 알았다.