극미세 Bi-Sn 솔더 범프와 UBM과의 계면반응

The reaction of ultra-small eutectic 58Bl-42Sn solder bump with Au/Ni/Ti and Au/Cu/Ti UBMs during reflow was studied. The eutectic Bi-Sn solder bumps of $46{\mu}m$ diameter were fabricated by using the evaporation method and were reflowed using the rapid thermal annealing system. The intermetallic compound was characterized using a SEM, an EDS, and an XRD. The $(Cu_xAu_{1-x})_6Sn_5$ compounds formed at the interface between Bi-Sn solder and Au/Cu/Ti UBM. On the other hand, in the Bi-Sn solder bump on Au/Ni/Ti UBM, the faceted and rectangular intermetallic compounds were observed on the solder bump surface and inside the solder bump as well as at the UBM interface. These intermetallic compounds were Identified as $(Au_{l-x-y}Bi_xNi_y)Sn_2$ phase.