다양한 열처리 분위기에 따른 SBT 커패시터의 강유전체 특성

Ferroelectrical Properties of SBT Capacitors with various Annealing Atmosphere

The $Sr_{0.7}Bi_{2.6}Ta_2O_9$(SBT) thin films are deposited on Pt-coated electrode(Pt/$TiO_2/SiO_2$/Si) using RF magnetron sputtering method. The structural and electrical properties of SBT capacitors were influenced with annealing atmosphere. In the XRD pattern, the SBT thin films in all annealed atmosphere had (105) orientation. In the SEM images, Bi-layered perovskite phase was crystallized in all annealing atmosphere and grains largely grew in oxygen annealing atmosphere. The maximum remanent polarization and the coercive electric field in oxygen annealing atmosphere are $12.40[{\mu}C/cm^2]$ and 30[kV/cm] respectively. The fatigue characteristics of SBT capacitors did not change up to $10^{10}$ switching cycles.