A study on Fabrication of Ferroelectric SST Thin Films by Liquid Delivery MOCVD Process

Liquid Delivery MOCVD공정을 이용한 강유전체 SBT 박막의 제조기술에 관한 연구

  • Kang, Dong-Kyun (Department of Materials Science and Engineering, Korea University) ;
  • Paik, Seung-Kyu (Department of Materials Science and Engineering, Korea University) ;
  • Kim, Hyoeng-Ki (Department of Materials Science and Engineering, Korea University) ;
  • Kim, Byong-Ho (Department of Materials Science and Engineering, Korea University)
  • 강동균 (고려대학교 재료공학과) ;
  • 백승규 (고려대학교 재료공학과) ;
  • 김형기 (고려대학교 재료공학과) ;
  • 김병호 (고려대학교 재료공학과)
  • Published : 2003.05.16
Download PDF
⟨ Previous Next ⟩

Abstract

200nm 정도의 두께를 가진 SBT 박막이 liquid delivery MOCVD 공정에 의해 (111) oriented Pt/Ti/$SiO_2$/Si 기판 위에 증착되었다 이 실험에서는 $Sr(TMHD)_2$tetraglyme, $Bi(ph)_3$ 그리고 $Ta(O^iPr)_4$(TMHD)를 출발 물질로 사용하였다. Sr 출발 물질의 열적 안정화를 위해서 adduct로 tetraglyme를 사용하여 실험하였고 유기 용매로는 n-butyl acetate를 사용하였다 Substrate temperature와 reactor pressure는 각각 $570^{\circ}C$와 5Torr로 유지시켰다. 또한 vaporizer의 용도는 $190-200^{\circ}C$, 그리고 delivery line 의 온도는 vaporizer 보다 높게 유지 $(220-230^{\circ}C)$하여 출발 용액을 분당 0.1ml로 50분간 주입하였다. 수송가스로 Ar, 산화제로 $O_2$ 가스를 사용하였다. 제조한 SBT 박막은 $750^{\circ}C$에서 열처리한 후 인가전압 3V와 5V에서 $2P_r$값이 각각 6.47, $8.98{\mu}C/cm^2$이었으며, $2E_c$값은 인가전압 3V와 5V에서 각각 2.05, 2.31V이었다 그리고 $800^{\circ}C$에서는$750^{\circ}C$에서 열처리한 SBT 박막보다 다소 우수한 이력특성을 나타내어 $2P_r$ 값은 인가전압 3V와 5V에서 각각 7.59, $10.18{\mu}C/cm^2$ 이었으며, $2E_c$값은 인가 전압 3V와 5V에서 각각 2.00, 2.21V 이었다.