DCA-MOD 법에 의한 High $J_c$ YBCO 박막의 제조

The Preparation of High $J_c$ YBCO Films by DCA-MOD Method

High $J_c$ $YBa_2Cu_3O_x$, superconducting films were fabricated by MOD method using fluorine-free dichloroacetic acid(DCA) as chelating solvent for preparing precursor solution. DCA-MOD precursor solution was coated on a single crystal (001) $LaAlO_3$(LAO) substrate by a dip coating method with a speed of 25 mm/min. Coated films were calcined at lower temperature up to $500^{\circ}C$ and Conversion heat treatment was performed at various temperatures of $780{\sim}810^{\circ}C$. SEM observations showed that films have very dense microstructures for the films prepared at the temperature higher than $800^{\circ}C$ regardless of diluting solvent; methanol or 2-methoxyethanol. A High critical current density ($J_c$) of 1.28 $MA/cm^2$ (@77 K and self-field) was obtained for the YBCO film prepared using 2-methoxyethanol as a solvent.