A Study on the magnetic properties of Mn-Zn Ferrite

Mn-Zn Ferrite의 자기적 특성에 관한 연구

In this paper, effect of ceramic processing was investigated on the magnetic properties of low loss Mn-Zn ferrite. High frequency characteristics, high saturated magnetic flux density and high magnetic permeability and low magnetism loss are required for the development of Mn-Zn ferrite, which is parts in the communication. therefore, in order to improve Mn-Zn ferrite with a high frequency , it is important to have a minimal change of particles and to control the eddy current loss caused by high resistance of the stratum of particles and to reduce the hysteresis loss by uniform change of detailed structure. In this paper, we added $V_2O_5\;and\;CaCo_3$ to Mn-Zn Ferrite to achieve a high efficiency, low loss core material. The compositions are MnO : ZnO : $Fe_2O_3$ = 21 : 10 : 69 mol%. They were sintered at $1250^{\circ}C$ for Three hours. Initial permeability was measured at 0.1MHz. At 50mT, Power loss was measured by temperature changing at 100kHz.

본 논문에서는 저손실 Mn-Zn 페라이트의 제조공정과 첨가제가 코어의 자기적 특성에 미치는 영향을 조사하였다. 통신부품재료로 Mn-Zn 페라이트 개발에는 필요한 높은 포화자속밀도 및 투자율을 가진 고주파 특성이 양호하고 자기손실도 적은 재료의 필요하다. 따라서, Mn-Zn 페라이트의 고주파 자기 특성의 개선을 위해서는 결정입자의 소경화와 입자계층의 고저항화에 따른 와전류 손실의 억제 및 미세 구조의 균일화에 따른 히스테리시스 손실의 저감이 중요하다. 본 논문에서는 고성능, 저손실의 자심재료를 위해 Mn-Zn Ferrite에 $V_2O_5$와 $CaCo_3$를 첨가하였다. 조성은 MnO : ZnO : $Fe_2O_3$ = 21 : 10 : 69 mol%로 하였다. 이 시료를 $1250^{\circ}C$에서 3시간 소결하였다. 측정은 0.1MHz에서 초투자율을 측정하였으며, 전력손실은 50mT에서 100kHz 및 온도를 변화시켜 측정하였다.