(TCTA/$TCTA_{1/3}TAZ_{2/3}/TAZ):Ir(ppy)_3$ 발광층을 이용한 녹색 인광소자

Phosphorescent Organic Light Emitting Diodes using the Emission Layer of (TCTA/$TCTA_{1/3}TAZ_{2/3}/TAZ):Ir(ppy)_3$

We have fabricated and evaluated new high efficiency green light emitting phosphorescent devices with an emission layer of $[TCTA_{1/3}TAZ_{2/3}/TAZ]:Ir(ppy)_3$. The whole experimental devices have the basic structure of $2-TNATA(500 {\AA})/NPB(300{\AA})/EML(300{\AA})/BCP(50{\AA})/SFC137(500{\AA})$ between anode and cathode. We have also fabricated conventional phosphorescent devices with emission layers of $(TCTA_{1/3}TAZ_{2/3}):Ir(ppy)_3$ and $(TCTA/TAZ):Ir(ppy)_3$ and compared their electroluminescence characteristics with those of the device with an emission layer of $(TCTA/TCTA_{1/3}TAZ_{2/3}/TAZ):Ir(ppy)_3$. The current density(J), luminance(L), and current efficiency($\eta$) of the device with an emission layer of $(80{\AA}-TCTA/90{\AA}-TCTA_{1/3}TAZ_{2/3}/130{\AA}-TAZ):10%-Ir(ppy)_3$ were 95 $mA/cm^2$, 25000 $cd/m^2$, and 27 cd/A at an applied voltage of 10V, respectively. The maximum current efficiency was 52 cd/A under the luminance of 400 $cd/m^2$. The peak wavelength and FWHM(full width at half maximum) in the electroluminescence spectral were 513nm and 65nm, respectively. The color coordinate was (0.30, 0.62) on the CIE (Commission Internationale de l'Eclairage) chart. Under the luminance of 15000 $cd/m^2$, the current efficiency of the device with an emission layer of $(80{\AA}-TCTA/90{\AA}-TCTA_{1/3}TAZ_{2/3}/130{\AA}-TAZ):10%-Ir(ppy)_3$ was 34 cd/A, which has been improved 1.7 times and 1.4 limes compared to those of the devices with emission layers of $(300{\AA}-TCTA_{1/3}TAZ_{2/3}): 10%-Ir(ppy)_3$ and $(100{\AA}-TCTA/200{\AA}-TAZ):10%-Ir(ppy)_3$, respectively.