Research on the copper diffusion process in germanium metal induced crystallization by different thickness and various temperature

Germanium (Ge) with higher carrier mobility and a lower crystallization temperature has been considered as the channel material of thin-film transistors for display applications. Various methods were studied for crystallizaion of poly-Ge from amorphous Ge at low temperature. Especially Metal induced crystalliazation (MIC) process was widely studied because low process cost. In this paper, we investigate copper diffusion process of different thick (70 nm, 350 nm) poly-Ge film obtained by MIC process at various temperatures (250, 300, and $350^{\circ}C$) through atomic force microscopy (AFM), Raman spectroscopy, and secondary ion mass spectroscopy (SIMS) measurement. Crystallization completeness and grain size was similar in all the conditions. Copper diffusion profile of 370 nm poly-Ge film show simirly results regardless of process temperature. However, copper diffusion profile of 70 nm poly-Ge film show different results by process temperature.