The effect of strain rate on the instability of sheet metal

변형율속도가 판재의 불안정에 미치는 영향

The forming limit diagram is assessed as a means of estimating the forming characteristics of sheet metal and is usually determined experimentally. The strain rates used in the determination are likely to be low. However, often in practice, the strain rates are much higher, so if forming limit diagram is determined at low rates, it may not be appropriate. This paper reconsiders the forming limit diagram for mild steel and aluminum sheet up to variation in strain rate from 10$^{-2}$ sec to 20/sec where its forming has been carried out under oil pressure using a hydraulic bulge test with circular and elliptical dies. To obtain higher strain rate, an impact bulge test had been employed with the same die sets as those used for a hydraulic bulge test. The results obtained are as follows: (1) As the strain rate increases, the fracture pressure increases and the polar height at fracture decreases. (2) Experiment has shown that, in the positive quadrant of the forming limit diagram, the diagram is lowered with increasing strain rate and the effect of strain rate changes according to strain paths and materials..

본 연구에서는 유압벌지시험기를 이용한 저속 벌지시험과 낙하해머(drop hammer)를 응용한 충격벌지시험기를 제작, 사용하여 충격벌지시험을 하여 저속변형과 충격변형에서 판재금속의 성형한계선도를 구하고 변형율속도가 판재의 불안정 및 성형 성에 미치는 영향을 조사하고 다이의 형상비(단축/장축)를 0.5, 0.75, 1.0 등으로 달 리하여 실험하므로써 변형경로에 따른 한계변형율의 변화를 관찰하고 아울러 기존의 성형한계이론과 비교, 검토하였다.