Fatigue Crack Propagation Characteristics of Duplex-Stainless Steel Weldments (II) -Crack Propagation on Near-Threshold Region-

2상계 스테인리스강 용접부의 피로크랙 전파특성 (II) -하한계치 근접에서의 전파특성-

  • 권종완 (경북산업대학교 기계공학과) ;
  • 김상대 (영남대학교 공대 정밀기계공학과) ;
  • 이택순 (영남대학교 공대 정밀기계공학과)
  • Published : 1989.01.01
Download PDF
⟨ Previous Next ⟩

Abstract

Near-threshold fatigue crack-growth behavior at room temperature for a duplex stainless steel weldments was investigated to evaluate the effect of load ratio, microstructural change, and residual stresses. Near-threshold fatigue crack propagation behavior is found to show a marked sensitivity to .alpha./.gamma. phase ratio, and little residual stress effects. Threshold values in the heat affected zones are higher than those of base metals and threshold values for crack growth decrease with increasing the load ratio in the base metals and weldments. The fractrographic features in base metals, weldments and heat affectred zones were discussed in terms mechanism of crack growth.

본 연구에서는 2상계 스테인리스강의 모재,용접재 및 용접후 열처리재 3종류의 경우에 대하여 피로크랙 전파특성을 피로크랙의 하한계치 근방에서 금속조직적인 영향을 검토하기 위하여, 각 조건에 대한 피로크랙 전파속도의 하한 계치를 구하였고 피로식검후의 파단면을 주사전자현미경(SEM)으로 관찰하였다. 용접재에 대하여는 용착부 부근 용접열영향부의 입경측정, .alpha./.gamma.상의 체적비교율의 변화량 측정 및 용접재와 용접후열처리재의 잔유응력분포측정을 통하여 피로크랙의 하한계특성에 미치는 여러가지 영향인자에 대하여 검토하였다.