Effects of $v_2O_5$ Addition on the Magnetic Properties of Mn-Zn Ferrites

Mn-Zn Ferrites 의 자기적 성질에 미치는 $V_2O_5$의 첨가효과

  • Jo, Deok-Ho (Department of Metallurgical Engineering, Taejon National Univ. of Technology)
  • 조덕호 (대전공업대학 금속공학과)
  • Published : 1992.11.01
Download PDF
⟨ Previous Next ⟩

Abstract

The effects of $V_2O_5$ addition as an additive on the densification, the microstructure and the magnetic properties of Mn-Zn ferrites were studied. The maximum density was observed at 0.1 wt% $V_2O_5$ content and it was recognized that a small content of $V_2O_5$ prohibited the discontinuous grain growth. The initial permeability showed maximum at 0.1 wt% $V_2O_5$ content and the power loss minimum at 0.03 wt% $V_2O_5$ content. It was found that a small content of $V_2O_5$ went into solid solution in the Mn-Zn ferrites, but above that extent $V_2O_5$ formed a second phase to be segregated at the grain boundaries.

소량의 $V_2O_5$ 첨가가 Mn-Zn 훼라이트의 치밀화, 미세조직 및 자기적 성질에 미치는 영향에 대하여 연구하였다. 최대밀도는 0.1 wt% $V_2O_5$ 첨가시 관측되며, $V_2O_5$ 첨가는 불균일입자성장을 억제하는 것으로 확인되었다. 초투자율은 0.1 wt% $V_2O_5$ 첨가시 최대값을 나타내었고, 손실은 0.03 wt% $V_2O_5$ 첨가시 최소값을 나타내었다. 소량의 $V_2O_5$ 는 Mn-Zn 훼라이트에 고용되지만, 일정량 이상이 되면 2차상을 형성하여 입계에 편석하였다.