The growth of large KTP crystal and the study of its optical inhomogeneity

대형 KTP 단결정 성장 및 광학적 불균일성에 관한 연구

  • Han, J.Y. (Samsung Advanced Institute of Technology) ;
  • Lee, S.K. (Samsung Advanced Institute of Technology) ;
  • Ma, D.J. (Samsung Advanced Institute of Technology) ;
  • Kim, Y.H. (Samsung Advanced Institute of Technology) ;
  • Park, S.S. (Samsung Advanced Institute of Technology) ;
  • Lee, S.H. (Samsung Advanced Institute of Technology)
  • 한재용 (삼성종합기술원) ;
  • 이성국 (삼성종합기술원) ;
  • 마동준 (삼성종합기술원) ;
  • 김용훈 (삼성종합기술원) ;
  • 박성수 (삼성종합기술원) ;
  • 이상학 (삼성종합기술원)
  • Published : 1994.03.01
Download PDF
⟨ Previous Next ⟩

Abstract

Single crystals of Potassium Titanyl Phosphate (KTP) were grown from the flux of $K_6P_4O_13(K_6)$ using a high temperatures solution growth method. To grow the large KTP crystal without inclusion, the temperature gradient in furnace, crystal rotation, orientation of seed crystal, and the cooling rate were controled. The KTP crystals are up to $10(a){\times}28(b){\times}33(c)mm^3$ in size. We investigated the optical inhomogeneity in this KTP crystal by the SHG power measurement and TEM analysis.

고온용액법(high temperature solution grwth)에 의해 $K_6P_4O_13$의 flux로 부터 KTP 단결정을 성장시켰다. Inclusion이 없는 KTP 단결정을 성장시키기 위해 성방로내 온도기울기, 결정의 회전, 종자결정의 방위, 냉각속도를 조절하였다. 성장된 KTP 단결정은 inclusion이 없었으며, 크기는 $10(a){\times}28(b){\times}33(c)mm^3$ 이었다. 또한 KTP 단결정 boule의 위치에 따른 SHG 출력 특성 측정 및 TEM 분석에 의해 종자결정 주위의 광학적 불균일성의 원인을 조사하였다.