DGEBA-MDA-SN-Hydroxyl Group System and Composites : 2. Fracture Energy of Fiber Reinforced Composites

DGEBA-MDA-SN-Hydroxyl Group System의 합성 및 복합재료 제조 : 2. 섬유강화 복합재료의 파괴에너지

  • 이재영 (서울시립대학교 화학공학과) ;
  • 심미자 (서울시립대학교 생명과학과) ;
  • 김상욱 (서울시립대학교 화학공학과)
  • Received : 1994.06.07
  • Accepted : 1994.06.20
  • Published : 1994.08.01

Abstract

The fracture energy of glass fiber/carbon fiber/epoxy resin hybrid composite system was investigated in the aspect of fracture mechanism. Epoxy resin matrix was DGEBA-MDA-SN-HQ system. On the interface of glass fiber and matrix, post debone friction energy provided a major contribution to the fracture energy, and debonding energy and pull-out energy were of the similar value. In the case of fracture on the interface of carbon fiber and matrix, pull-out energy was the major contributor.

유리섬유/탄소섬유/에폭시 수지 hybrid 복합재료의 파괴에너지를 파괴메카니즘 측면에서 연구하였다. 에폭시 수지 매트릭스는 DGEBA(diglycidyl ether of bisphenol A)-MDA(4,4'-methylene dianiline)-SN(succinonitrile)-HQ(hydroquinone)를 사용하였다. 섬유강화 복합재료의 파괴에너지를 연구한 결과, 유리섬유와 매트릭스의 계면에서는 post debond friction energy가 가장 크게 나타났으며, debonding energy와 pull-out energy는 비슷한 값을 나타내었다. 탄소섬유와 매트릭스의 계면에서 파괴가 일어나는 경우에는 pull-out energy가 가장 큰 영향을 나타내었다.

Keywords

Acknowledgement

Supported by : 교육부