Abstract
The study was performed to study the effects of strain rate on acoustics emission( AE) during bulging test in corrosive environmentsynthetic sea water. The strain rates used were in the range $4 \times 10^{-6}S^{-1}$ to $1 \times 10^{-4} \times S^{-1}$ and the parameters used to evaluate AE signal characteristics were AE hit and amplitude. It can be observed that the cumulative AE hit and average amplitude during fracture process increase highly at decreasing strain rates while the equivalent fracture strain and the crack length of circumferencial direction become decrease. The peak point of AE signal characteristic parameters approach to the first half of test. When the average amplitude per unit equivalent fracture strain was above 20dB, it was definitly observed stress corrosion cracking phenomena. Additional, we knew that the AE test had the possibility to evaluate SCC susceptibility with various strain rates.
본 연구에서는 부식환경하에서 bulging 시험동안 음향방출거동에 미치는 변형률속도에 대한 영향을 알아보았다. 시험에 사용된 변형률속도의 범위는 $4 \times 10^{-6}S^{-1}$에서 $1 \times 10^{-4} \times S^{-1}$까지이며, AE신호 특성을 평가하기 위해 사용된 인자는 AE hit수와 진폭으로 하였다. 시험결과, 변형률속도가 감소함에 따라 등가파괴변형률과 원주방향의 균열 길이는 감소하였으나, 파괴과정동안 총 누적 AE hit수와 평균진폭은 크게 증가하였다. 그리고 AE신호 특성치의 최대점은 시험전분부에 접근하였으며, 단위 등가파괴변형률당 평균진폭이 20dB 이상에서는 뚜렷하게 응력부식륜열 현상을 관찰할 수 있었다. 또한 음향방출시험법은 변형률속도에 따른 재료의 응력부식균열 감수성 정도를 평가하는데 있어 그 적용 가능성이 있음을 알 수 있었다.