Abstract
The thin plate of Co-Ni-P was deposited on the polyester film by the electroless plating method. Through present experiments, deposition rates and metal compositions of the plates were determined according to compositions of solution, pH and temperature. Also, magnetic properties of plates were examined according to metal compositions. Considering magnetic properties and deposition rates of electroless plating, the best condition was obtained as pH of 8.5 and 90℃. It was observed that metal compositions were evidently varied by the pH of solutions and the concentration of complex agents. However. they were not affected by other factors. At the optimum condition, the composition of the plate was Co(78%), Ni(16%), and P(6%). Also, it was found that the coercive force was 370 Oe, and squareness was 0.65 at this condition. Magnetic properties (hard or soft) of thin plates were determined by metal compositions. Therefore. the plate became soft magnetic plate as the composition of nickel increased over 30 per cents. The crystal structure of the soft magnetic plate was found to be amorphous in which it was strongly oriented to the (111)phahe of nickel. On the ohter hand, the hard magnetic place was found to be hcp crystalline of α-cobalt which was oriented to the (101)phase of cobalt and the (100)phase of cobalt.
본 연구에서는 무전해 도금범으로 polyester film 상에 Co-Ni-P 박막을 석출시키고, pH, 온도 그리고 도금용액의 농도에 따른 도금속도 및 석출된 도금박막의 합금조성과 합금조성에 따른 자기적 특성을 고찰하였다. 무전해도금의 석출속도는 pH 8.5, 온도 90℃일때 가장 좋았으며, 자기적 특성도 이 때가 가장 좋았다. 합금조성은 pH와 착화제의 농도에 따라서는 크게 변화하였으나, 그 밖의 인자들에 의해서는 변화하지 않았다. 최적조건에서 만들어진 박막의 합금조성은 코발트가 78%, 니켈이 16%, 인이 6%였고, 보자력은 370 Oe, 각형비는 0.65였다. 박막은 합금조성에 따라 경질자성막과 연질자성막의 두가지 형태로 변화했고, 니켈이 30% 이상 공석(共席)되었을 때, 연질자성막으로 되었다. 연질자성막일때, 합금박막의 결정구조는 니켈이 강하게 배향된 비정질 형태를 나타냈고, 경질자성 막일때는, 코발트(101)과 (100)면으로 배향된 α-코발트의 hcp 결정구조를 나타내었다.