Sputering Pressure and Temperature Effects on Magnetization Reversal Behaviors of $Co(2\AA)/Pd(13\AA)$ Multilayers

스퍼터링압력 및 온도 효과에 의한 $Co(2\AA)/Pd(13\AA)$ 다층박막의 자화반전 거동

To study the magnetization reversal behavior of Co/Pd multilayers, we first demagnetized the samples by the field-demagnetized method and then measured initial curves and minor loops. The coercivity and the perpendicular magnetic anisotropy were obtained from the perpendicular and parallel magnetization curves measured at different temperatures. We interpret our experimental results by applying several qualitative and semiquantative approaches. From these study, we found that the magnetization reversal behavior is dominated by the domain wall pinning for all samples and the coercivity incremental tendency can be explained by Kronmuller's formula $H_c(T)\;{\propto}\;r_0.K_u$.

Co/Pd 다층박막의 자화반전 거동을 조사하기 위하여, 먼저 시료를 자기장 소거법으로 탈자시킨 다음 초기자화 곡선과 minor loops 를 측정하였다. 또한 보자력 및 포화자화는 수직자화곡선으로부터 구하였으며, 수직자기이방성은 온도별로 측정한 수직 및 수평자화곡선의 면적차이를 이용하여 구하였다. 자화반저거동의 분석을 위하여 여러가지 정상적이고 반정량적인 방법을 측정결과에 적용하였다. 이들 결과로부터 본 실험에 사용된 시료의 자화반전의 지배적인 거동은 자벽의 pinning이며, 스퍼터링 압력이 증가할수록 보자력이 증가하는 경향은 Kronmuller 식 $H_{c}$ (T) .var. $r_{o}$ .center dot. $K_{u}$에 의해 설명될 수 있었다.다.다.