Abstract
Composition and process conditions for low temperature sintered NiCuZn ferrites were investigated, so as to fabricate multilayered chip inductor. The$Fe_2O_3$ deficiency for low temperature sintering was decreased with NiO contents of NiCuZn ferrites. The permeability of NiCuZn ferrites can be controlled in the range of 12~562 with the variation of NiO and $Co_3O_4$ contents. The $Q_{max} $ frequency of NiCuZn ferrites was decreased from 50 MHz to 3 MHz linearly with permeability increase from 60 to 560. The relation between the $Q_{max}$ frequency(Y) and permeability(X) of NiCuZn ferrites was expressed with the following empirical equation, logY=4.2-1.4logX.
적층형 chip inductor 소재인 NiCuZn ferrite의 제조 공정 조건 및 조성을 선정하였다. NiCuZn ferrite의 NiO 함량이 증가할 수록 저온 소결에 필요한 Fe$_{2}$O$_{3}$ 결핍량은 점차 증가하였고, NiO 함량과 Co$_{3}$O$_{4}$ 첨가량을 변화하여 투자율을 12 ~ 562 범위에서 제어할 수 있었다. NiCuZn ferrite의 투자율이 562에서 60으로 변화함에 따라서 Q$_{max}$ 주파수는 3 MHz에서 50 MHz 범위로 제어할 수 있었다. 이때 Q$_{max}$ 주파수(Y)와 투자율(X)은 log Y = 4.2-1.4 log X의 상관관계를 나타내었다.