Abstract
Low resistance ohmic contacts to the Si-doped $\textrm{In}_{0.17}\textrm{Ga}_{0.83}\textrm{N}$(~$\times10^{19}\textrm{cm}^{-3}$) were obtained using the W metallization schemes. Specific contact resistance decreased with increasing annealing temperature. The lowest resistance is obtained after a nitrogen ambient annealing at $950^{\circ}C$ for 90 s, which results in a specific contact resistance of $2.75\times10^{-8}\Omega\textrm{cm}^{-3}$. Interfacial reactions and surface are analyzed using x-ray diffraction and scanning electron microscopy (SEM). The X-ray diffraction results show that the reactions between the W film and the $\textrm{In}_{0.17}\textrm{Ga}_{0.83}\textrm{N}$ produce a $\beta$-$W_2N$ phase at the interface. The SEM result shows that the morphology of the contacts is stable up to a temperature as high as $850^{\circ}C$. Possible mechanisms are proposed to describe the annealing temperature dependence of the specific contact resistance.
Si 도핑된 n-$\textrm{In}_{0.17}\textrm{Ga}_{0.83}\textrm{N}$($1.63\times10^{19}\textrm{cm}^{-3}$)에 W을 이용하여 낮은 접촉저항을 갖는 Ohmic 접촉을 형성시켰다. 열처리 온도를 증가시킴에 따라 비접촉 저항이 낮아졌으며, 가장 낮은 비접촉 저항은 $950^{\circ}C$의 질소분위기 하에서 90초간 열처리 해줌으로써 $2.75\times10^{-8}\Omega\textrm{cm}^{-3}$의 낮은 비접촉 저항값을 얻었다. 열처리 온도증가에 따른 $\textrm{In}_{0.17}\textrm{Ga}_{0.83}\textrm{N}$와 W의 계면반응과 W의 표면은 XRD와 SeM을 이용하여 분석하였다. XRD 분석을 통하여 W과 $\textrm{In}_{0.17}\textrm{Ga}_{0.83}\textrm{N}$이 반응하여 계면에 $\beta$-$W_2N$ 상을 형성시킴을 확인할 수 있었다. SEM 분석결과 W 표면은 $850^{\circ}C$의 높은 열처리온도에서도 안정한 상태를 유지하였다. W과 InGaN의 Ohmic 접촉에 있어 비접촉 저항은 열처리 온도를 증가시킴에 따라 낮아지게 되는 온도 의존성을 갖는데 이에 대한 가능한 기구를 제시하였다.