Preparation of Sulfur Crosslinkable EVA and Blend With Rubbers

황가황형 EVA의 제조 및 고무와의 블렌드

In this study, double bond, unsaturated group was introduced to the main chain of EVA by chemically treating EVA, nondiene polymer. Benzene sulfonic acid, ENB and DCPD were used as a third element. Also, from blending CR and SBR, conventional synthetic rubber we prepared vulcanizates and examined their physical properties. The datum lead to the following conclusion that some problems were modified; limited temperature in use and mechanical properties like hardness, tensile strength, tensile stress, and elongation rate of thermoplastic EVA, keeping the following advantages of original EVA; green strength, injection molding by Pressure, adhesion, tackiness, dimensional stability, and ozone resistance, etc. It is expected that continuous research of the modification between nondiene and diene polymer will improve what were shown disadvantages in synthetic polymer; processing, oxidation resistance, and adhesion. In addition, it will be possible to continue process of rubber products by utilizing possible fluidity for fusion of EVA.

본 연구에서는 제3의 성분으로 벤젠 술폰산계열 반응성 화합물과 ENB 및 DCPD를 사용하여 비diene계 고분자인 EVA를 특수 화학적 처리에 의하여 EVA의 주쇄에 불포화기 즉, 이중결합을 도입시켰다. 또한 이중결합도입 EVA와 diene계 범용합성고무인 CR, SBR과의 블렌드를 통하여 황가 황체를 제조하여 가황체들의 물리적 특성을 비교 검토하였다. 검토결과 원래의 EVA가 갖고 있는 green strength, 사출 압출 성형성, 접착성, 점착성, 치수안정성, 오존저항성 등의 장점은 그대로 살리면서도 황가황이 가능하여 열가소성의 EVA가 갖는 사용온도의 한계 문제와 기계적 특성 즉, 경도, 인장강도, 인장 응력, 신장율 등온 향상시켰다. 비diene계 고분자와 diene계 고분자의 블렌드에 있어서 개질에 대한 연구가 더 수행되어진다면 합성고무에서 나타나는 부족한 가공성, 내산화 안정성, 접착성 등을 크게 향상시킬 수 있을 것이며 아울러 EVA의 융해유동성을 이용한 고무제품 가공공정의 연속화가 가능하게 될 것이다.