Variations of the Electrochemical Properties of LiMn2O4 with the Calcining Temperature

  • Song, Myoung-Youp (Division of Advanced Materials Engineering, The Research Center of Industrial Technology, Engineering Research Institute, Chonbuk National University) ;
  • Shon, Mi-suk (Division of Advanced Materials Engineering, The Research Center of Industrial Technology, Engineering Research Institute, Chonbuk National University)
  • 발행 : 2002.06.01

초록

LiMn$_2$O$_4$ compounds were synthesized by calcining a mixture of LiOH and MnO$_2$(CMD) at 47$0^{\circ}C$ for 10 h and then calcining again at $650^{\circ}C$ to 90$0^{\circ}C$ fur 48 h in air with intermediate grinding. All the synthesized samples exhibited XRD patterns for the cubic spinel phase with a space group Fd3m. The lattice parameter increased gradually as the sintering temperature rose. The electrochemical cells were charged and discharged fur 20 cycles at a current density 300$\mu$A/$\textrm{cm}^2$ between 3.5 V and 4.3 V. The voltage vs. discharge capacity curves for all the samples showed two plateaus. The LiMn$_2$O$_4$ sample calcined at 90$0^{\circ}C$ had the largest first discharge capacity. This sample exhibited the best crystallinity, had relatively large lattice parameter and had relatively large particles with rectatively homogeneous size. All the samples showed good cycling performances. Among all the samples, the LiMn$_2$O$_4$ calcined at 85$0^{\circ}C$ had relatively large first discharge capacity and very good cycling performance. The addition of excess LiOH and the mixing in ethanol considered to help the formation of the more LiMn$_2$O$_4$ phase per unit weight sample and the more stable LiMn$_2$O$_4$phase. These led to the larger discharge capacities and the better cycling performances. The cyclic voltammograms fur the second cycle of the LiMn$_2$O$_4$ samples showed the oxidation and reduction peaks around 4.05 V and 4.18 V and around 4.08 V and 3.94 V, respectively. The larger first discharge capacity of the sample calcined at the higher temperature is related to the larger lattice parameter.

키워드

참고문헌

  1. J. Solid State Chem. v.134 Structure and Electrochemical Properties of Boron-doped LiCoO₂ R. Alcantara;P. Lavela;J. L. Tirado;R. Stoyanova;E. Zhecheva https://doi.org/10.1006/jssc.1997.7552
  2. J. Powder Sources v.72 Synthesis by Sol-gel Process and Characterization of LiCoO₂Cathode Materials Z. S. Peng;C. R. Wan;C.Y. Jiang https://doi.org/10.1016/S0378-7753(97)02689-X
  3. J. Kor. Ceram. Soc. v.38 Effects of Drying Temperature on the LiCoO₂Thin Films Fabricated by Sol-gel Method(in Kor) M. K. Kim;K. S. Park;D. S. Kim;J. T. Son;H. G. Kim
  4. J. Electrochem. Soc. v.138 The Spinel Phase of$LiMn_2O_4$as a Cathode in Secondary Lithium Cells J. M. Tarascon;E. Wang;F. K. Shokoohi;W. R. McKinnon;S. Colson https://doi.org/10.1149/1.2085330
  5. J. Kor. Ceram. Soc. v.38 A Study on the Synthesis and the Electrochemical Properties of$LiNi_{1-y}CoyO_2$from$Li_2CO_3$and$CoCO_3$(in Kor) H. Rim;S. G. Kang;S. H. Chang;M. Y. Song
  6. J. Electrochem. Soc. v.138 Rechargeable$LiNiO_2$/Carbon Cells J. R. Dahn;U. von Sacken;M. W. Juzkow;H. Al-Janaby https://doi.org/10.1149/1.2085950
  7. Solid State Ionics v.112 no.21-2 On the Capacity Deterioration of Spinel Phase$LiMn_2O_4$with Cycling around 4V M. Y. Song;D. S. Ahn
  8. J. Powder Sources v.83 Capacity Fading of Spinel Phase$LiMn_2O_4$with Cycling M. Y. Song;D. S. Ahn;H. R. Park https://doi.org/10.1016/S0378-7753(99)00256-6
  9. J. Electrochem. Soc. v.147 no.3 Variations of the Electrochemical Properties of $LiMn_2O)4$with Cycling D. S. Ahn;M. Y. Song https://doi.org/10.1149/1.1393285
  10. J. Kor. Ceram. Soc. v.38 Combustion Synthesis of$LiMn_2O_4$with Citric Acid and the Effect of Post-heat Treatment(in Kor.) Y.S. Han;J. T. Son;H. G. Kim;H. T. Jung
  11. J. Power Sources v.68 Synthesis and Properties of Gallium-doped LiNiO₂as the Cathode Material for Lithium Secondary Batteries Y. Nishida;K. Nakane;T. Stoh https://doi.org/10.1016/S0378-7753(97)02535-4
  12. J. Electrochem. Soc. v.143 An Investigation of Lithium Ion Insertion into Spinel Structure Li-Mn-O Compounds Y. Xia;M. Yoshio https://doi.org/10.1149/1.1836544
  13. J. Power Sources v.41 Rechargeable Lithium Battery with Spinel-related$ MnO_2$Ⅱ. Optimization of the$LiMn_2O_4$Synthesis Conditions A. Momchilov;V. Manev;A. Nassalevska https://doi.org/10.1016/0378-7753(93)80048-T
  14. J. Electrochem. Soc. v.141 Synthesis Conditions and Oxygen Stoichiometry Effects on Li Insertion into the Spinel$LiMn_2O_4$ J. M. Tarascon;W. R. McKinnon;F. Coowar;T. N. Bowmer;G. Amatucci;D. Guyomard https://doi.org/10.1149/1.2054941
  15. J. Electrochem. Soc. v.143 Preparation and Electrochemical Characterization of Micron-sized Spinel$LiMn_2O_4$ Z. Jiang;K. M. Abraham https://doi.org/10.1149/1.1836684
  16. J. Electrochem. Soc. v.142 Some Aspects of$LiMn_2$Electrochemistry in the 4 Volt Range G. Pistoia;D. Zane;Y. Zhang https://doi.org/10.1149/1.2050052
  17. J. Electrochem. Soc. v.139 Li Metal-free Rechargeable$LiMn_2O_4$/Carbon Cells: Their Understanding and Optimization D. Guyomard;J. M. Tarascon https://doi.org/10.1149/1.2069372
  18. J. Power Sources v.44 Rechargeable Lithium Battery with Spinel-related λ-MnO₂for Battery Applications V. Manev;A. Momchilov;A. Nassalevka;A. Kozawa https://doi.org/10.1016/0378-7753(93)80202-Z

피인용 문헌

  1. Cycling performance of LiNi y Mn2 − y O4 prepared by the solid-state reaction vol.47, pp.12, 2011, https://doi.org/10.1134/S1023193511120111