A Comparison of shear Bonding Strength with Polyacrylic acid and Phosphoric acid Enamel Surface Conditioning

폴리아크릴산과 인산으로 법랑질표면 처리후 전단결합강도의 비교

The purpose of this study was to compare in vitro shear bonding strength with three different enamel surface preparations (1) 30% sulfated polyacrylic acid with 0.3M lithium sulfate (2) 40% sulfated polyacrylic acid with 0.3M lithium sulfate (3) 37% phosphoric acid. 105 extracted human premolar teeth were divided into each three groups of 35. Metal brackets were bonded to teeth in the three groups. The same self curing resin was used for all groups. A shearing force was applied to the teeth. After debonding, bases of bracket and enamel surfaces were examined under steroscopic microscope to determine the failure modes. Statistical analysis of the data was carried out with one way ANOVA and Student t- test. The results were as follows. 1. Shear bond strength values for the 30% polyacrylic acid and 40% polyacrylic acid group were approximately two thirds of the phosphoric acid group. It maintains clinically acceptable but not enough bond strength. 2. There was no statistically significant difference in shear bond strengths between 30% and 40% polyacrylic acid group. 3. The failure modes of brackets had some differences. In polyacrylic acid groups, the percentage of adhesive/enamel failure was higher than that of adhesive/ bracket interface failure. On the contrary in phosphoric acid groups, the results were reversed. Further study of bond strength could be required. If polyacrylic acid enamel conditioning is used clinically.

이번 연구의 목적은 3가지의 서로 다른 법랑질 표면처리용액을 사용하였을 때 각각의 경우 전단결합강도를 실험실에서 측정하고 비교해보는 것이다. (1)30% sulfated polyacrylic acid with 0.3M lithium sulfate (2)40% sulfated polyacrylic acid with 0.3M lithium sulfate (3)37% phosphoric acid. 105개의 사람의 소구치를 35개씩 3개의 군으로 분류하였다. 3가지의 준비된 용액을 분류된 각 군에 적용하고 동일한 자가 중합 레진을 사용하여 금속 브라켓을 부착하였다. 각각의 치아마다 전단결합강도를 측정하였다. 브라켓을 제거한후 법랑질표면과 브라켓 베이스의 파절양상을 입체현미경으로 관찰하여 다음과 같은 결과를 얻었다. 1. 30%와 40% 폴리 아크릴산을 사용한 군에서 측정된 전단결합강도는 37% 인산을 사용한 그룹의 2/3수준으로 임상적응용이 가능한 수준이었으나 충분하지는 않았다. 2. 폴리아크릴산 그룹간의 전단결합강도에서는 통계학적으로 유의성이 없었다. 3. 브라켓의 탈락양상을 관찰한 결과 폴리아크릴산을 사용한 군에서는 브라켓과 접착제간의 파절보다 접착제와 법랑질간의 파절빈도가 높았다. 인산을 사용한 군에서는 폴리아크릴산의 군과 반대로 관찰되었다. 이상의 결과로 볼 때 폴리아크릴산을 임상에 사용하려면 전단결합강도를 높일 수 있는 연구가 선행되어야 할것으로 사료된다.