Preparation and Characterization of La0.8Ca0.2MnO3

La0.8Ca0.2MnO3의 합성 및 특성연구

  • Published : 2003.05.01
Download PDF
⟨ Previous Next ⟩

Abstract

The powders of L $a_{0.8}$C $a_{0.2}$Mn $O_3$ Colossal Magnetoresistance (CMR) materials were synthesized by sol-gel process. Lanthanum(H), Calcium(II) and Manganese(III) 2,4-Pentanedionate were dissolved in a mixed binary solution consisted of propionic acid and methanol with PEG (15 wt%) aqueous solution. The progress of reactions was monitored by FT-IR spectroscopy. The Lao scao.2Mn03 gel powders were annealed at various temperatures. The structural changes were investigated by FT-IR, CP/MAS $^{ 13}$C solid state NMR spectroscopy and XRD. The thermochemical property, particle characterization, microstructure of sintered sample, and cation composition of gel powder were studied by TG/DTA, FE-SEM and ICP-AES. The magnetic characterizations were identified through measurement of magnetic moment by VSM.

초거대 자기 저항 물질인 페로브스카이트 L $a_{0.8}$C $a_{0.2}$Mn $O_3$의 분말을 졸-겔방법으로 제조하였다. Lanthanum(III), Calcium(II) 그리고 Manganese(III) 2,4-Pentanedionate를 Propionic acid와 methane떠 혼합용매를 사용하고 PEG (l5 wt%) 용액을 첨가 하여 안정한 졸용액을 합성하였고 FT-IR spectroscopy로 반응의 진행 정도를 관찰하였다. L $a_{0.8}$C $a_{0.2}$Mn $O_3$ 겔 분말에 대해 온도를 변화시키면서 열처리하여 FT-IR, CP/MAS $^{13}$C solid state NMR spectroscopy와 XRD등을 이용해 구조변화를 관찰하였다. 열분석은 TG/DTA로 측정하였으며, FE-SEM을 통해 입자크기와 균일도를 관찰하였고, 양이온 조성 비율을 알아보기 위해 ICP-AES를 측정하였다. 자성 특성을 규명하기 위해 VSM을 이용하여 자기 모멘트를 측정하였으며, 상자기성 에서 강자기성으로 전이되는 큐리온도( $T_{c}$)를 관찰하였다.

Keywords

References

  1. J. Solid State Chem. v.146 Oxygen Content and Structures of $La_{1-x} Ca_{x} MnO_{3+d}$ as a Function of Synthesis Conditions B.Dabrowski;R.Dybzinski;Z.Bukowski;O.Chmaissem;J.D.Jorgensen https://doi.org/10.1006/jssc.1999.8389
  2. J. Am. Ceram. Soc. v.80 no.10 Sol-gel Synthesis of Perovskite Type Lanthanum Manganite Thin Films and Fine Powders using Metal Acetylacetonate and Poly(vinyl alcohol) Y.Shimizu;T.Murata https://doi.org/10.1111/j.1151-2916.1997.tb03178.x
  3. J. of Nuclear Mater. v.257 Preparation of Lithium Aluminate via Polymeric Precursor Routes S.W.Kwon;S.B.Park;S.T.Hwang https://doi.org/10.1016/S0022-3115(98)00442-5
  4. J. Non-Cryst. Solids v.208 Raman Spectra of Oilgomeric Species obtained by Tetraethoxysilane Hydrolysis-polycondensation Process J.Gando;P.Dhamelincourt;C.Pelegris;M.Jraisnel;A. Le Maguer Mayot https://doi.org/10.1016/S0022-3093(96)00526-1
  5. Mat. Sci. and Eng. B v.18 Synthesis of Nanocrystalline Composite Oxides $La_{1-x} Sr_{x} Fe_{1-y} Co_{y} O_{3}$ with the Perovskite Structure using Poly(ethylene glycol) Gel Method X.Li;H.Zhang;F.Chi;S.Li;B.Xu;M.Zhao https://doi.org/10.1016/0921-5107(93)90133-8
  6. J. Kor. Chem. Soc. v.38 no.11 Preparation of LaMO₃(M: Cr, Mn, Co) Fine Powders using PEG H.B.Park;H.J.Kweon;S.J.Kim;K.Kim
  7. J. Am. Ceram. Soc. v.75 no.4 Sol-gel Synthesis of Strontium-doped Lanthanum Manganite S.Bilger;E.Syskakis;A.Naoumidis;H.Nickel https://doi.org/10.1111/j.1151-2916.1992.tb04167.x
  8. J. Kor. Ceram. Soc. Preparation and Characterization of BaTiO₃Powder and Thin Film using Chelating Ligand M.W.Jung;H.J.Son;J.Y.Lee
  9. Elements of X-ray Diffraction B.D.Cullity
  10. Solid State Ionics v.68 Materials for Electrodes based on Rare Earth Manganites P.Shuk;L.Tichonova;U.Guth https://doi.org/10.1016/0167-2738(94)90175-9
  11. Phys. Rev. B v.53 no.6 Structure, Electron-transport Properties, and Giant Mag-netoresistance of Hole-doped LaMnO₃Systems R.Mahendiran;S.K.Tiwary;A.K.Raychaudhuri;T.V.Ramakrishnan;R.Mahesh;N.Rangavittal;N.R.Rao https://doi.org/10.1103/PhysRevB.53.3348
  12. Phys. Rev. B v.55 no.5 Charge, Orbital, and Magnetic Ordering in $La_{0.5} Ca_{0.5} MnO_{3}$ P.G.Radaelli;D.E.Cox;M.Marezio;S.W.Cheong https://doi.org/10.1103/PhysRevB.55.3015
  13. J. Magn. Magn. Mater. v.189 Influence of the Grain-size and Oxygen Stoichiometry on Magnetic and Transport Properties of Polycrystalline $La_{0.67} Ca_{0.33} MnO_{3}$ Perovskites L.E.Hueso;F.Rivadulla;R.D.Sanchez;D.Caeiro;C.Jardon;C.Vazquez;J.Rivas;M. A. Lopez-Quintela https://doi.org/10.1016/S0304-8853(98)00257-1