Evaluation of Weathering Durability of Waterborne Preservative Treated Wood by Accelerated Weathering

수용성 방부처리재의 기상열화 저항성 평가

  • Received : 2002.09.12
  • Accepted : 2002.11.05
  • Published : 2003.08.26

Abstract

This study was carried out to evaluate the weathering durability of waterborne preservative (AAC, ACQ, CCA, CuAz) treated Japanese red pine (Pinus densiflora S. et Z.) sapwood samples by accelerated weathering, and to find out the factor of stability. When considered the color changes, weight losses, surface degradation, and microstructure changes due to weathering, ACQ-, CCA-, and CuAz-treated samples were durable against weathering; the weathering durability of AAC-treated samples was poor and similar to untreated controls. The lignin content in aqueous extracts collected from ACQ-, CCA-, and CuAz-treated samples during weathering was lower than that from untreated and AAC-treated ones. From these findings, we might concluded that weathering durability of ACQ-, CCA-, and CuAz-treated samples was enhanced by the fixation of preservative component(s) onto the lignin structure, which is very susceptible to weathering.

수용성 방부처리(AAC, CCA-3, ACQ, CuAz) 소나무 시편의 기상열화에 대한 저항성을 평가하기 위하여 인공촉진열화 방법을 사용하였다. 기상열화에 의한 재색 및 중량변화, 물리적 표면열화, 목재조직의 변화를 종합적으로 고려할 때, AAC 처리시편을 제외한 ACQ, CCA, CuAz 처리시편은 기상열화에 대한 저항성이 있음을 알 수 있었다. 이러한 몇몇 방부처리재가 기상열화에 대하여 저항성을 나타내는 요인탐색을 위해 기상열화 산물을 분석하였는데, 그 결과, ACQ, CCA, CuAz 처리시편에서는 낮은 리그닌 함량이 측정되어 기상열화 저항성을 가지는 처리시편은 리그닌 열화가 적게 일어남을 나타냈다. 이는 방부제 유효성분이 목재 주성분 중 기상열화에 민감한 리그닌 구조에 정착함으로써 리그닌 열화에 대한 저항성이 발현되었기 때문으로 판단된다.

Keywords