Effect of Accelerated Weathering on the Leaching of Copper from Preservative Treated Wood

기상열화가 방부처리재의 구리성분 용탈에 미치는 영향

This is the second in a series of reports on the evaluation of weathering durability of waterborne preservative treated wood by accelerated weathering. The leaching of copper from ACQ-, CCA-, and CuAz-treated samples during weathering was increased by UV irradiation, when compared between full weathering and water-only weathering. The FTIR spectra of the weathered ACQ-, CCA, CuAz-treated samples at 1731 cm^-1, 1625 cm^-1, 1510 cm^-1, which are related to the fixation of copper, were different from those of unweathered controls. This result means that UV irradiation can weaken the chemical bond between lignin and copper and/or extraction of lignin-copper complex can be occured when lignin erode away by weathering.

본 연구는 앞서 발표한 「수용성 방부처리재의 촉진 기상열화 저항성 평가」의 부속실험으로서 기상열화가 방부처리재의 유효성분 중 구리의 용탈에 미치는 영향을 평가하기 위하여 수행되었다. ACQ, CCA, CuAz 처리시편을 대상으로 실시한 자외선 조사 유무에 따른 기상열화 조건에서 공통된 유효성분인 구리의 용탈량은 방부제의 종류에 관계없이 인공강우만 실시했을 때보다 자외선 조사를 함께 겸했던 시편에서 높게 나타났다. 방부처리 전후와 방부처리재의 촉진열화 전후의 목재표면을 FTIR을 이용하여 분석하였는데, 그 결과 구리가 정착되는 것으로 판단되는 1731 cm^-1, 1625 cm^-1, 1510 cm^-1 흡수대가 촉진열화에 의해 큰 변화를 나타냈다. 이는 리그닌과 결합되었던 구리가 리그닌의 자외선 열화시 리그닌과 함께 용출 되었음을 시사한다.