Freezing and Thawing Properties of Concrete Using Recycled Coarse Aggregate

재생굵은골재를 사용한 콘크리트의 동결융해 특성

This study was performed to examine the freezing and thawing properties of the high strength concrete using recycled coarse aggregate. The recycled coarse aggregate was replaced by 0%, 25%, 50%, 75% and 100% of natural crushed aggregate. The compressive strength of the concrete used recycled coarse aggregate was shown in more than $400kgf/cm^2$ at the curing age 28 days. The weight loss ratio by freezing and thawing was shown in less than 1% at all mix type. The pulse velocity and relative dynamic modulus were decreased with increasing the freezing and thawing cycles. Also, durability factor for the freezing and thawing were decreased with increasing the content of recycled coarse aggregate. But, recycled concrete replaced with recycled coarse aggregate 100% was shown in more than 60 by durability factor in freezing and thawing of 300cycles Accordingly, these recycled coarse aggregate can be used for high strength concrete.

이 연구는 플라이 애시를 결합재 중량의 20%, 재생굵은골재를 천연쇄석굵은골재의 0%, 25%, 50%, 75%, 100%를 치환하여 압축강도와 동결융해 특성을 구명하였으며, 이 연구를 통해 얻어진 결과를 요약하면 다음과 같다. 1. 재령 28일의 압축강도는 모든 배합비와 W/B 35%에서 $400kgf/cm^2$이상으로 나타나 고강도콘크리트에 이용될 수 있을 것으로 생각된다. 2. 중량감소율은 동결융해 300사이클에서 1%미만으로 나타났고, 표면박리와 같은 현상은 나타나지 않았으며, 재생골재의 대체율이 증가할수록 감소율은 증가하였다. 3. 초음파진동속도는 동결융해 300사이클에서 19~24%정도의 감소율을 나타내었으며, 재생골재의 대체율이 증가할수록 감소율은 증가하는 경향을 나타내었다. 4. 상대동탄성계수는 재생골재의 대체율에 따라 60~72%의 범위로 나타내었으며, 재생골재 대체율이 증가할수록 감소하는 경향을 나타내었다. 5. 내구성지수는 모든 배합에서 60이상을 나타내었으나, 재생골재 대체율이 100%일때는 급격히 떨어지는 경향을 나타내었다. 6. 재생굵은골재를 사용한 콘크리트의 압축강도, 중량감소율, 초음파진동속도, 상대동탄성계수, 내구성지수 시험결과를 볼 때, 시험에 사용한 재생굵은골재는 고강도콘크리트에 사용이 가능할 것으로 판단된다.