초록
In order to examine the effect of humidity on hydrogen embrittlement of STS 444 weld zone for boiler with dry and wet welding conditions, this paper was carried out the accelerated hydrogen osmosis test and the electrochemical Tafel polarization test. In 0.5M $H_2SO_4$ + 0.01M $As_20_3$ solution, this test is added to load of $1400kg/cm^2$ together with hydrogen osmosis by current of $50 {mA/cm^2}$ for 60 min.. The electrochemical Tafel polarization test was carried out in 0.5M $H_2SO_4$ + 0.01M $As_20_3$ solution. Therefore, the effect of humidity on hydrogen embrittlement of STS 444 was considered. The main results are as following: On the basis of hydrogen embrittlement mechanism, that is, integrated electrochemical polarization characteristics with the established mechanism of hydrogen embrittlement, the reduction rate of corrosion current density of weld zone in the wet weld condition is larger than in the dry condition. We can nondestructively predict the degree of hydrogen embrittlement of STS 444 weld zone for boiler through the reduction rate of electrochemical corrosion current density.